X70钢在不同含水量砂土中的腐蚀电化学行为
Electrochemical Behavior of X70 Steel Corrosion in Sand with Different Water Content
摘 要
通过砂土通电加速腐蚀试验, 采用电化学阻抗谱(EIS)和极化曲线、扫描电镜(SEM)等测试技术研究了X70钢在不同含水量砂土中的腐蚀电化学行为。试验结果表明, X70钢在低含水量砂土中(小于等于9%)通电腐蚀24 h后的电化学阻抗谱(EIS)Nyquist图具有两个时间常数, 高频区呈现砂土介质特征容抗弧, 中低频段为腐蚀活化反应过程对应的容抗弧; 在较高含水量砂土中(大于9%)的Nyquist图较前者多出一小段高频感抗弧。砂土颗粒间孔隙较大, 通气透水性能较好, X70钢的腐蚀反应以活化控制为主, 腐蚀速率随含水量的升高而增大, 在18%含水量时接近峰值。
砂土
含水量
电化学阻抗谱(EIS)
腐蚀
X70 steel
sand
water content
electrochemical impedance spectroscopy(EIS)
corrosion
Abstract
Electrochemical behavior of X70 pipeline steel corrosion in sand with different water content was studied by means of electrochemical impedance spectroscopy (EIS) and polarization technique. It was found that EIS of X70 pipeline steel in sand with low water content (not more than 9%) after 24 h contains a capacitive arc at high frequency which represents the soil characteristic and one at lower frequency exhibiting processes of corrosion activation reaction; In sand with higher water content (more than 9%), EIS contains another high-frequency inductive loop. Corrosion rate of X70 steel in sand raised with the increase of water content and then reached the peak with 18% water content.
中图分类号 TG172
所属栏目 试验研究
基金项目 国家自然科学基金(51178287; 51208333); 山西省自然科学基金(2014011036-1; 2014131019); 太原理工大学优秀青年基金(TYUT2014YQ017)
收稿日期
修改稿日期
网络出版日期
作者单位点击查看
备注申博著(1991-), 男, 1991年生, 硕士研究生
引用该论文: SHEN Bo-zhu,HAN Peng-ju,ZHANG Wen-bo. Electrochemical Behavior of X70 Steel Corrosion in Sand with Different Water Content[J]. Corrosion & Protection, 2015, 36(S1): 157
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李谋成, 林海潮, 曹楚南. 湿度对钢铁材料在中性土壤中腐蚀行为的影响[J]. 腐蚀科学与防护技术, 2000, 12(4): 218-221.
【2】李晓刚, 杜翠薇, 董超芳, 等. X70钢的腐蚀行为与试验研究[M]. 北京: 科学出版社, 2006.
【3】李谋成, 林海潮, 曹楚南. 碳钢在土壤腐蚀中的电化学阻抗谱特征[J]. 中国腐蚀与防护学报, 2000, 20(2): 111-117.
【4】胥聪敏, 国荣, 胡海军, 等. X80管线钢在海滨盐碱土壤模拟溶液中的耐腐蚀性能研究[J]. 钢铁研究学报, 2010, 22(3): 42-46.
【5】么惠平, 闫茂成, 杨旭, 等. X80管线钢红壤腐蚀初期电化学行为[J]. 中国腐蚀与防护学报, 2014, 34(5): 473-476.
【6】曹楚南, 张鉴清. 电化学阻抗谱导论[M]. 北京: 科学出版社, 2002.
【7】曹楚南. 腐蚀电化学原理[M]. 北京: 化学工业出版社, 2008.
【8】BARBALAT M,LANARDE L,CARON D,et al. Electrochemical study of the corrosion rate of carbon steel in soil: Evolution with time and determination of residual corrosion rates under cathodic protection[J]. Corrosion Science, 2012, 55: 246-253.
【9】鲁新如, 杜翠薇, 李晓刚, 等. X70钢在大庆两种土壤中的腐蚀行为[J]. 腐蚀与防护, 2008, 29(9): 503-506.
【10】ISMAIL A I M,EI-SHAMY A M. Engineering behaviour of soil materials on the corrosion of mild steel[J]. Applied Clay Science,2009, 42(3/4): 356-362.
【11】COLE I S,MARNEY D. The science of pipe corrosion: A review of the literature on the corrosion of ferrous metals in soils[J]. Corrosion Science, 2012, 56: 55-56.
【12】陈旭, 杜翠薇, 李晓刚, 等. 含水量对X70钢在大港滨海盐渍土壤中腐蚀行为的影响[J]. 北京科技大学学报, 2008, 30(7): 730-734.
【13】梁平, 李晓刚, 杜翠薇, 等. 影响埋地X70管线钢腐蚀性的土壤因素评价[J]. 腐蚀与防护, 2009, 23(8): 526-530.
【14】CARLOS ALBERTO,FERREIRA M,JOSE A C P,et al. Evaluation of the corrosivity of the soil through its chemical composition[J]. Science of the Total Environment, 2007, 388(1/3): 250-255.
【2】李晓刚, 杜翠薇, 董超芳, 等. X70钢的腐蚀行为与试验研究[M]. 北京: 科学出版社, 2006.
【3】李谋成, 林海潮, 曹楚南. 碳钢在土壤腐蚀中的电化学阻抗谱特征[J]. 中国腐蚀与防护学报, 2000, 20(2): 111-117.
【4】胥聪敏, 国荣, 胡海军, 等. X80管线钢在海滨盐碱土壤模拟溶液中的耐腐蚀性能研究[J]. 钢铁研究学报, 2010, 22(3): 42-46.
【5】么惠平, 闫茂成, 杨旭, 等. X80管线钢红壤腐蚀初期电化学行为[J]. 中国腐蚀与防护学报, 2014, 34(5): 473-476.
【6】曹楚南, 张鉴清. 电化学阻抗谱导论[M]. 北京: 科学出版社, 2002.
【7】曹楚南. 腐蚀电化学原理[M]. 北京: 化学工业出版社, 2008.
【8】BARBALAT M,LANARDE L,CARON D,et al. Electrochemical study of the corrosion rate of carbon steel in soil: Evolution with time and determination of residual corrosion rates under cathodic protection[J]. Corrosion Science, 2012, 55: 246-253.
【9】鲁新如, 杜翠薇, 李晓刚, 等. X70钢在大庆两种土壤中的腐蚀行为[J]. 腐蚀与防护, 2008, 29(9): 503-506.
【10】ISMAIL A I M,EI-SHAMY A M. Engineering behaviour of soil materials on the corrosion of mild steel[J]. Applied Clay Science,2009, 42(3/4): 356-362.
【11】COLE I S,MARNEY D. The science of pipe corrosion: A review of the literature on the corrosion of ferrous metals in soils[J]. Corrosion Science, 2012, 56: 55-56.
【12】陈旭, 杜翠薇, 李晓刚, 等. 含水量对X70钢在大港滨海盐渍土壤中腐蚀行为的影响[J]. 北京科技大学学报, 2008, 30(7): 730-734.
【13】梁平, 李晓刚, 杜翠薇, 等. 影响埋地X70管线钢腐蚀性的土壤因素评价[J]. 腐蚀与防护, 2009, 23(8): 526-530.
【14】CARLOS ALBERTO,FERREIRA M,JOSE A C P,et al. Evaluation of the corrosivity of the soil through its chemical composition[J]. Science of the Total Environment, 2007, 388(1/3): 250-255.
相关信息