Causes Analysis on Fracture of the Conductive Screw of a Gas Turbine Generator
摘 要
某燃气轮发电机使用的导电螺钉(T2铜)在使用过程中发生断裂,引起发电机跳闸。为找出导电螺钉断裂的原因,对导电螺钉进行了宏观检查、结构分析、化学成分分析、断口分析、金相检验和力学性能测试。结果表明:该导电螺钉发生断裂失效是由结构应力和高温下螺钉强度降低导致的,最后给出了相应的改进建议。
Abstract
The conductive screw (T2 copper) of a gas turbine generator fractured during use, resulting in the tripping of the generator. To find out the fracture causes, the conductive screw was analyzed from the aspects of macroscopic examination, structure analysis, chemical composition analysis, fracture analysis, metallographic examination and mechanical property test. The results show that the fracture failure of the conductive screw was due to the structural stress and the decreased strength at the high temperature. Finally, the corresponding improvement suggestions were given.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl201607009
所属栏目 质量控制与失效分析
基金项目
收稿日期 2015/8/4
修改稿日期
网络出版日期
作者单位点击查看
联系人作者陈强(272211089@qq.com)
备注陈 强(1985-),男,助理工程师,主要从事发电厂金属检测方面的工作
引用该论文: CHEN Qiang,ZHOU Gong-wen,ZHENG Wen-xiang,LIU Jun-jian. Causes Analysis on Fracture of the Conductive Screw of a Gas Turbine Generator[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2016, 52(7): 476~478
陈 强,周公文,郑文祥,刘俊建. 燃气轮发电机导电螺钉的断裂原因分析[J]. 理化检验-物理分册, 2016, 52(7): 476~478
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张亦良,黄惠茹,李想.车削加工残余应力分布规律的实验研究[J].北京工业大学学报,2006,32(7): 582-586.
【2】周荣莲,凌洁,杨静,等.磨削残余应力的产生与X射线衍射分析方法[J].理化检验-物理分册,2014,50(6): 424-428.
【3】刘筱薇,金应荣.铜导线的短路熔痕与过热熔断熔痕分析[J].热加工工艺,2011,40(14): 194-197.
【4】张立军,赵升吨,唐勇.热应力对金属棒料内部损伤的机理研究[J].西安交通大学学报,2009,43(1): 99-103.
【5】程柄午,郑程,许鹤君.测量铜合金电导率的方法比较[J].理化检验-物理分册,2015,51(9): 628-631
【2】周荣莲,凌洁,杨静,等.磨削残余应力的产生与X射线衍射分析方法[J].理化检验-物理分册,2014,50(6): 424-428.
【3】刘筱薇,金应荣.铜导线的短路熔痕与过热熔断熔痕分析[J].热加工工艺,2011,40(14): 194-197.
【4】张立军,赵升吨,唐勇.热应力对金属棒料内部损伤的机理研究[J].西安交通大学学报,2009,43(1): 99-103.
【5】程柄午,郑程,许鹤君.测量铜合金电导率的方法比较[J].理化检验-物理分册,2015,51(9): 628-631
相关信息