局部热处理对TA1钛合金-SPCC钢压印接头失效行为的影响
Influence of Local Heat Treatment on Failure Behavior of TA1 Titanium Alloy-SPCC Steel Clinched Joint
摘 要
在自行搭建的局部热处理试验平台上将TA1钛合金-SPCC钢压印接头连接部位加热至900 ℃水淬, 研究了局部热处理对此压印接头失效载荷和失效模式的影响。结果表明: 局部热处理后该压印接头的失效载荷为5 371.9 N, 比未经热处理的(4 252.4 N)提高了26.34%; 未经热处理压印接头的失效模式为上下板拉脱失效, 断裂方式为韧性断裂, 局部热处理后该压印接头的失效模式为拉脱+颈部断裂混合失效, 断裂方式为准解理断裂。
压印接头
失效载荷
失效模式
断口形貌
local heat treatment
clinched joint
failure load
failure mode
fracture morphology
Abstract
The connection part of TA1 titanium alloy-SPCC steel clinched joint was heated to 900 ℃ then water quenched on the self-designed experimental platform. The influences of the local heat treatment on the failure load and failure mode of the clinched joint were investigated. The results show that the failure load of the clinched joint after local heat treatment was 5 371.9 N, which was improved by 26.34% comparing to 4 252.4 N before local heat treatment. The failure mode of the clinched joint before local heat treatment was a pull-off failure between upper and lower plate and the fracture mode was ductile fracture. After local heat treatment, the failure mode of the clinched joint was a mixture failure of pull-off and neck breaking and the fracture mode was quasi-cleavage fracture.
中图分类号 TG3 DOI 10.11973/jxgccl201608020
所属栏目
基金项目 国家自然科学基金资助项目(50965009); 昆明理工大学分析测试基金资助项目(20140974)
收稿日期 2015/1/16
修改稿日期 2016/6/19
网络出版日期
作者单位点击查看
备注王医锋(1989-),男,湖北崇阳人,硕士研究生。
引用该论文: WANG Yi-feng,HE Xiao-cong,ZENG Kai,LU Yi,WANG Yu-qi. Influence of Local Heat Treatment on Failure Behavior of TA1 Titanium Alloy-SPCC Steel Clinched Joint[J]. Materials for mechancial engineering, 2016, 40(8): 86～89
王医锋,何晓聪,曾 凯,卢 毅,王玉奇. 局部热处理对TA1钛合金-SPCC钢压印接头失效行为的影响[J]. 机械工程材料, 2016, 40(8): 86～89
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】高建红, 李文辉, 刘伦伦, 等.钛合金和镍合金加工用新型刀具材料的研究进展［J］.机械工程材料, 2014,38(12): 1-5.
【2】董鑫,李培源,王旭,等.腐蚀对TC17钛合金超高周疲劳性能的影响［J］.机械工程材料, 2014, 38(11): 76-79.
【3】杨慧艳, 何晓聪, 周森, 等.压印接头拉剪强度的有限元模拟［J］.机械工程材料, 2013,37(9): 74-78.
【4】HE X C. Recent development in finite element analysis of clinched joints ［J］. The International Journal of Advanced Manufacturing Technology, 2010, 48: 607-612.
【5】刘婉颖,朱毅科,林元华,等.热处理对TC4钛合金显微组织和力学性能的影响［J］.材料导报,2013,27(18): 108-111.
【6】娄宇航,蔺广学,刘俞平,等.TC4真空电子束焊后热处理对接头组织性能的影响［J］.热加工工艺,2013,42(19): 179-182.
【7】邢保英,何晓聪,冯模盛,等.粘接剂对压印连接强度的影响及数理统计分析［J］.材料导报,2012,26(2): 56-59.
【8】LEE C J, KIM J Y, LEE S K,et al. Design of mechanical clinching tools for joining of aluminium alloy sheets［J］. Materials and Design,2010,31: 1854-1861.
【9】刘福龙, 何晓聪, 曾凯, 等. 局部热处理对不同模具压印接头静力性能影响分析［J］. 材料导报, 2014, 28(6): 91-94.
【10】杨慧艳,何晓聪,丁燕芳,等.铝合金压印接头的强度研究［J］.应用力学学报, 2014,31(2): 299-304.
【11】上海交通大学《金属断口分析》编写组. 金属断口分析［M］. 北京: 国防工业出版社, 1979.
【12】杨川,高国庆,崔国栋,等.金属零部件失效分析基础［M］. 北京: 国防工业出版社, 2014.
【2】董鑫,李培源,王旭,等.腐蚀对TC17钛合金超高周疲劳性能的影响［J］.机械工程材料, 2014, 38(11): 76-79.
【3】杨慧艳, 何晓聪, 周森, 等.压印接头拉剪强度的有限元模拟［J］.机械工程材料, 2013,37(9): 74-78.
【4】HE X C. Recent development in finite element analysis of clinched joints ［J］. The International Journal of Advanced Manufacturing Technology, 2010, 48: 607-612.
【5】刘婉颖,朱毅科,林元华,等.热处理对TC4钛合金显微组织和力学性能的影响［J］.材料导报,2013,27(18): 108-111.
【6】娄宇航,蔺广学,刘俞平,等.TC4真空电子束焊后热处理对接头组织性能的影响［J］.热加工工艺,2013,42(19): 179-182.
【7】邢保英,何晓聪,冯模盛,等.粘接剂对压印连接强度的影响及数理统计分析［J］.材料导报,2012,26(2): 56-59.
【8】LEE C J, KIM J Y, LEE S K,et al. Design of mechanical clinching tools for joining of aluminium alloy sheets［J］. Materials and Design,2010,31: 1854-1861.
【9】刘福龙, 何晓聪, 曾凯, 等. 局部热处理对不同模具压印接头静力性能影响分析［J］. 材料导报, 2014, 28(6): 91-94.
【10】杨慧艳,何晓聪,丁燕芳,等.铝合金压印接头的强度研究［J］.应用力学学报, 2014,31(2): 299-304.
【11】上海交通大学《金属断口分析》编写组. 金属断口分析［M］. 北京: 国防工业出版社, 1979.
【12】杨川,高国庆,崔国栋,等.金属零部件失效分析基础［M］. 北京: 国防工业出版社, 2014.
相关信息