Corrosion Behavior of Oil Casing Materials Used Commonly in Thermal Production Well in Acid Medium
摘 要
通过模拟工况下的腐蚀试验,对不同油套管材料的腐蚀行为进行分析和研究,同时结合腐蚀预测软件进行数据分析。结果表明:在50 ℃及150 ℃下,N80、BG80-3Cr、P110、BG90H四种材料的均匀腐蚀速率大于0.2 mm/a,腐蚀较严重;BG90H-9Cr和BG90H-13Cr在试验温度范围内具有良好的抗CO2+H2S+O2均匀及局部腐蚀能力;温度对油套管用钢的腐蚀影响较为复杂,随温度升高,腐蚀速率上升,但温度较高时,当金属表面生成致密的腐蚀产物膜后,腐蚀速率随温度升高而降低。
Abstract
The corrosion behaviors of different oil casing materials were studied in corrosion test under simulated working conditions, at the same time the data analysis was conducted with corrosion prediction software. The results show that uniform corrosion rates of N80, BG80-3Cr, P110 and BG90H at 50 ℃ and 150 ℃ were higher than 0.2 mm/a, the four materials corroded seriously. In the experimental temperature range, BG90H-9Cr and BG90H-13Cr had good resistance to uniform and localized corrosion in CO2+H2S+O2 media. The effect of temperature on corrosion of oil casing steel was more complicated. With the increase of temperature, the corrosion rate rose first, and then declined at relatively high temperatures because corrosion product films generated on the surface of metal materials.
中图分类号 TG172.8 DOI 10.11973/fsyfh-201608006
所属栏目 试验研究
基金项目 国家重大科技专项(2011ZX05012-002)
收稿日期 2015/11/9
修改稿日期
网络出版日期
作者单位点击查看
备注计 玲(1984-),硕士,从事采油工程等方面的科研工作
引用该论文: JI Ling. Corrosion Behavior of Oil Casing Materials Used Commonly in Thermal Production Well in Acid Medium[J]. Corrosion & Protection, 2016, 37(8): 635
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吴新民,邵秀丽,薛晨. pH值对碳钢在高含硫油田水中腐蚀行为的影响[J]. 中国腐蚀与防护学报,2013,33(2):159-163.
【2】范志刚,李翠楠,王燕,等. 流速对天然气输气管道腐蚀的影响规律研究[J]. 钻采工艺,2010,33(2):88-90.
【3】DENPO K,OGAWA H. Fluid flow effects on CO2 corrosion resistance of oil well materials[J]. Corrosion,1993,49(6):442-449.
【4】龙凤乐,郑文军,陈长风,等. 温度、CO2分压、流速、pH值对X65管线钢CO2均匀腐蚀速率的影响规律[J]. 腐蚀与防护,2005,26(7):290-286.
【2】范志刚,李翠楠,王燕,等. 流速对天然气输气管道腐蚀的影响规律研究[J]. 钻采工艺,2010,33(2):88-90.
【3】DENPO K,OGAWA H. Fluid flow effects on CO2 corrosion resistance of oil well materials[J]. Corrosion,1993,49(6):442-449.
【4】龙凤乐,郑文军,陈长风,等. 温度、CO2分压、流速、pH值对X65管线钢CO2均匀腐蚀速率的影响规律[J]. 腐蚀与防护,2005,26(7):290-286.
相关信息