压片机模具失效原因分析
Analysis on Failure Reasons of Tablet Press Dies
摘 要
压片机模具在使用过程中发生卷边和崩裂失效。通过化学成分分析、硬度测试、金相检验及断口形貌分析的方法, 对压片机模具的失效原因进行了分析。结果表明: 压片机模具失效是由于模具原材料中的夹杂物等缺陷较多所致; 建议选用合格的原材料, 并对所用原材料进行质量检查。
失效
夹杂物
缺陷
tablet press die
failure
inclusion
defect
Abstract
Curling and breaking failure occurred to the tablet press dies during the process of using. The failure reasons of the tablet press dies were analyzed by means of chemical composition analysis, hardness testing, metallographic examination and fracture morphology analysis. The results show that the failure of the tablet press dies was caused by amounts of inclusions and other defects in the raw material of dies. Improvement measures were suggested that qualified raw materials should be selected and quality inspection should be done to the raw materials.
中图分类号 TG76 TG115.2 DOI 10.11973/lhjy-wl201609015
所属栏目 质量控制与失效分析
基金项目 辽宁省自然基金资助项目(2014028016)
收稿日期 2015/11/10
修改稿日期
网络出版日期
作者单位点击查看
备注孙 晶(1962-), 女, 副教授, 博士, 主要从事高强度镁合金、材料强化及失效分析方面的研究。
引用该论文: SUN Jing,GUO Quan-ying,ZHANG Guo-yu. Analysis on Failure Reasons of Tablet Press Dies[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2016, 52(9): 655～658
孙 晶,郭全英,张国玉. 压片机模具失效原因分析[J]. 理化检验－物理分册, 2016, 52(9): 655～658
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】马飞.压片机现状及发展方向浅析［J］.机电信息, 2009(23):18-21.
【2】陈再良,付海峰,吕东显,等.模具主要失效形式与可靠性技术［J］.失效分析与预防,2011,6(4):261-266.
【3】刘瑞堂.机械零件失效分析［M］.哈尔滨:哈尔滨工业大学出版社,2005.
【4】陈再良,吕东显,付海峰.模具失效分析中的几个问题［J］.理化检验-物理分册,2009,45(增刊):17-18.
【5】黄沙.GCr15轧辊热处理爆裂失效分析［J］.理化检验-物理分册,2013,49(7):402-406.
【6】汤海芳,江东才,朱启茂,等.Q345R钢板探伤不合格原因分析［J］.理化检验-物理分册,2013,49(7):463-466.
【2】陈再良,付海峰,吕东显,等.模具主要失效形式与可靠性技术［J］.失效分析与预防,2011,6(4):261-266.
【3】刘瑞堂.机械零件失效分析［M］.哈尔滨:哈尔滨工业大学出版社,2005.
【4】陈再良,吕东显,付海峰.模具失效分析中的几个问题［J］.理化检验-物理分册,2009,45(增刊):17-18.
【5】黄沙.GCr15轧辊热处理爆裂失效分析［J］.理化检验-物理分册,2013,49(7):402-406.
【6】汤海芳,江东才,朱启茂,等.Q345R钢板探伤不合格原因分析［J］.理化检验-物理分册,2013,49(7):463-466.
相关信息