闪光对焊焊接380CL钢轮辋焊缝开裂原因分析
Weld Cracking Analysis of 380CL Steel Rim Welded by Flash Butt Welding
摘 要
利用光学显微镜、扫描电子显微镜等分析了闪光对焊焊接380CL钢轮辋焊缝开裂的原因。结果表明: 该轮辋焊缝的开裂为脆性开裂, 焊缝区晶粒异常长大及焊后冷速较快而产生的粗大魏氏组织是其失效的根本原因; 通过优化闪光对焊工艺, 降低焊接时焊缝中心高温停留时间以有效控制焊缝奥氏体晶粒尺寸, 可以保证焊缝良好的强韧性、避免焊缝开裂。
380CL钢
闪光对焊
焊缝开裂
rim
380CL steel
flash butt welding
weld cracking
Abstract
The weld cracking reason of 380CL steel rim welded by flash butt welding was analyzed by using optical microscope, scanning electron microscope and so on. The results show that the weld cracking of the rim was brittle cracking. The coarse widmansttten structure, which was produced due to the abnormal growth of grains in weld seam and the rapid cooling rate after welding, was the main reason for the cracking failure. By optimizing the flash butt welding process, shortening high-temperature residence time in the weld center to effectively control the weld austenite grain size and ensuring a good strength and toughness property of the weld would prevent the weld cracking.
中图分类号 TG453.9 DOI 10.11973/jxgccl201610022
所属栏目 失效分析
基金项目
收稿日期 2015/6/24
修改稿日期 2016/8/24
网络出版日期
作者单位点击查看
备注惠亚军(1988-), 男, 安徽宿州人, 工程师, 硕士。
引用该论文: HUI Ya-jun,LI Wen-yuan,PAN Hui,LIU Kun,CHEN Bin,CUI Yang,WU Ke-min. Weld Cracking Analysis of 380CL Steel Rim Welded by Flash Butt Welding[J]. Materials for mechancial engineering, 2016, 40(10): 100～103
惠亚军,李文远,潘 辉,刘 锟,陈 斌,崔 阳,吴科敏. 闪光对焊焊接380CL钢轮辋焊缝开裂原因分析[J]. 机械工程材料, 2016, 40(10): 100～103
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘克文,于大明.汽车钢圈闪光对焊接头的组织性能研究［J］.现代焊接,2013(11): 23-25.
【2】赵红利,李发云,罗成,等.汽车滚型轮毂闪光对焊开裂分析［J］.焊接技术, 2009,38(3): 56-58.
【3】熊春英,张亚舫,罗学泉,等. 国产化材料车轮钢圈焊接工艺的确定［J］.机械工程材料, 2014, 38(12): 50-53.
【4】李宝华,柯黎明,邢丽,等.搅拌摩擦焊工艺参数对LY12铝合金焊缝金属流动形态的影响［J］.机械工程材料,2008, 32(6): 22-24.
【5】张桂芹, 董建君, 王燕. 380CL车轮钢闪光对接焊组织与性能［J］.热加工工艺,2012,41(15): 141-144.
【6】黄华刚,王克争,何方殿,等. 闪光对焊接头金相组织、性能和工艺关系的研究［J］.焊接,2001(11): 11-14.
【7】张根元,陈洪莲,徐迈里,等. 45钢交流闪光对焊焊接热影响区晶粒长大的数值模拟［J］.机械工程材料,2008, 32(7): 75-86.
【8】李敏,宋振官. 380CL 钢制轮辋焊缝开裂分析［J］. 宽厚板,2013,19(4): 28-30.
【9】崔忠析. 金属学与热处理［M］.北京: 机械工业出版社, 1994: 54-55.
【10】吴丰顺,张贵锋,王士元,等.直流电阻对焊过程的有限元分析［J］.机械工程学报,1998,34(6): 90-95.
【11】张德芬,李曾珍,罗红松,等.不预热焊接工艺焊接X70管线钢接头的组织与性能［J］.机械工程材料,2014,38(12): 37-41.
【12】李继红,杨亮,张兴璇,等.超低碳微合金管线钢焊接接头的组织与冲击性能［J］.机械工程材料,2014,38(6): 75-78.
【13】王维斌,史耀武,雷永平. 400 MPa超细晶粒钢直流电阻闪光对焊接头组织的数值模拟［J］.机械工程学报,2015,41(1): 77-80.
【14】赵雷,乔汉文,梁军,等. 焊接参数对T92/S30432异种钢焊接接头室温力学性能的影响［J］.机械工程材料,2015,39(1): 33-35.
【15】王勇,叶其斌,陈军平,等.微观组织对C-Mn 钢低温脆性的影响［J］.钢铁研究学报, 2011,23(1): 166-168.
【2】赵红利,李发云,罗成,等.汽车滚型轮毂闪光对焊开裂分析［J］.焊接技术, 2009,38(3): 56-58.
【3】熊春英,张亚舫,罗学泉,等. 国产化材料车轮钢圈焊接工艺的确定［J］.机械工程材料, 2014, 38(12): 50-53.
【4】李宝华,柯黎明,邢丽,等.搅拌摩擦焊工艺参数对LY12铝合金焊缝金属流动形态的影响［J］.机械工程材料,2008, 32(6): 22-24.
【5】张桂芹, 董建君, 王燕. 380CL车轮钢闪光对接焊组织与性能［J］.热加工工艺,2012,41(15): 141-144.
【6】黄华刚,王克争,何方殿,等. 闪光对焊接头金相组织、性能和工艺关系的研究［J］.焊接,2001(11): 11-14.
【7】张根元,陈洪莲,徐迈里,等. 45钢交流闪光对焊焊接热影响区晶粒长大的数值模拟［J］.机械工程材料,2008, 32(7): 75-86.
【8】李敏,宋振官. 380CL 钢制轮辋焊缝开裂分析［J］. 宽厚板,2013,19(4): 28-30.
【9】崔忠析. 金属学与热处理［M］.北京: 机械工业出版社, 1994: 54-55.
【10】吴丰顺,张贵锋,王士元,等.直流电阻对焊过程的有限元分析［J］.机械工程学报,1998,34(6): 90-95.
【11】张德芬,李曾珍,罗红松,等.不预热焊接工艺焊接X70管线钢接头的组织与性能［J］.机械工程材料,2014,38(12): 37-41.
【12】李继红,杨亮,张兴璇,等.超低碳微合金管线钢焊接接头的组织与冲击性能［J］.机械工程材料,2014,38(6): 75-78.
【13】王维斌,史耀武,雷永平. 400 MPa超细晶粒钢直流电阻闪光对焊接头组织的数值模拟［J］.机械工程学报,2015,41(1): 77-80.
【14】赵雷,乔汉文,梁军,等. 焊接参数对T92/S30432异种钢焊接接头室温力学性能的影响［J］.机械工程材料,2015,39(1): 33-35.
【15】王勇,叶其斌,陈军平,等.微观组织对C-Mn 钢低温脆性的影响［J］.钢铁研究学报, 2011,23(1): 166-168.
相关信息