Effects of Stirring Speed on Corrosion Resistance and Wearing Resistance for Silver-graphite Composite Coating
摘 要
采用电沉积法在纯铜基体上制备了银-石墨复合镀层,研究了镀液搅拌速率对银-石墨复合镀层耐蚀性和耐磨性的影响。结果表明:随着搅拌速率的增大,复合镀层中石墨的含量先增大后减小,自腐蚀电流密度和自腐蚀电位呈现先增大后减小的趋势,但整体变化幅度不大;搅拌速率为320~920 r/min时,随着搅拌速率的增大,复合镀层摩擦因数增大,磨损率增大。考虑到工业生产要求,最佳搅拌速率为420 r/min,此时制备的复合镀层的磨损率可低至8.13×10-14 m3/(N·m)。
Abstract
A silver-graphite composite coating was prepared by electro-deposition method. The influence of stirring speed on the corrosion resistance and wear resistance of the silver-graphite composite coating was particularly investigated. It is indicated that the area fraction of the graphite in the composite coating first increased and then decreased with the rise of stirring speed. The corrosion current dentisy and corrosion potential showed a trend of first increase and then decrease, but the overall rate of change was not obvious. In the range of 320 r/min to 920 r/min, both the friction coefficient and the wear rate of the silver-graphite composite coating increased with the rise of stirring speed. Considering the industrial production requirements be taken into consideration, the best stirring speed is suggested to be 420 r/min, at this stirring speed, the wear rate of the preparation of composite coating can be as low as 8.13×10-14 m3/(N·m).
中图分类号 TG174.4 DOI 10.11973/fsyfh-201611002
所属栏目 试验研究
基金项目 国网浙江省电力公司科技/信息化项目(B355DW140005); 江西省自然科学基金(20151BAB206017); 航空基金(2013ZF56022)
收稿日期 2015/6/27
修改稿日期
网络出版日期
作者单位点击查看
备注叶志国(1979-),副教授,博士,从事材料电化学相关研究,
引用该论文: CHEN Chuan,CHEN Yi-bin,WANG Bao-feng,LANG Yun,YE Zhi-guo,MA Guang. Effects of Stirring Speed on Corrosion Resistance and Wearing Resistance for Silver-graphite Composite Coating[J]. Corrosion & Protection, 2016, 37(11): 869
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】林岩. 户外高压隔离开关常见缺陷分析及对策[J]. 硅谷,2010(3):16-17.
【2】王俊勃,李英民,王亚平,等. 纳米复合银基电触头材料的研究[J]. 稀有金属材料与工程,2004,33(11):1213-1217.
【3】吴振. 户外高压隔离开关过热的原因及对策[J]. 机电信息,2010(24):89-90.
【4】WANG J,FENG Y,LI Y,et al. Influence of graphite content on sliding wear characteristics of CNTs-Ag-G electrical contact materials[J]. Transactions of Nonferrous Metals Society of China,2009,19(1):113-118.
【5】LIU N L,QI S H,LI S S,et al. Preparation and characterization of phenol formaldehyde/Ag/graphite nanosheet composites[J]. Polymer Testing,2011,30(4):390-396.
【6】MARX D E,BARILLO D J. Silver in medicine:the basic science[J]. Burns,2014,40:S9-S18.
【7】冯秋元,李廷举,金俊泽. 影响微粒复合沉积的诸因素[J]. 材料保护,2006,39(5):35-39.
【8】陈哲. 银-石墨自润滑电接触复合镀层的制备研究[D]. 上海:上海交通大学,2008.
【9】郝丽丽. 铝合金表面Ni-P-β-SiC化学复合镀层制备与应用[D]. 西安:西安科技大学,2006.
【10】谭澄宇. Ni、Cu基复合镀层制备及其电化学基础研究[D]. 长沙:中南大学,2008.
【2】王俊勃,李英民,王亚平,等. 纳米复合银基电触头材料的研究[J]. 稀有金属材料与工程,2004,33(11):1213-1217.
【3】吴振. 户外高压隔离开关过热的原因及对策[J]. 机电信息,2010(24):89-90.
【4】WANG J,FENG Y,LI Y,et al. Influence of graphite content on sliding wear characteristics of CNTs-Ag-G electrical contact materials[J]. Transactions of Nonferrous Metals Society of China,2009,19(1):113-118.
【5】LIU N L,QI S H,LI S S,et al. Preparation and characterization of phenol formaldehyde/Ag/graphite nanosheet composites[J]. Polymer Testing,2011,30(4):390-396.
【6】MARX D E,BARILLO D J. Silver in medicine:the basic science[J]. Burns,2014,40:S9-S18.
【7】冯秋元,李廷举,金俊泽. 影响微粒复合沉积的诸因素[J]. 材料保护,2006,39(5):35-39.
【8】陈哲. 银-石墨自润滑电接触复合镀层的制备研究[D]. 上海:上海交通大学,2008.
【9】郝丽丽. 铝合金表面Ni-P-β-SiC化学复合镀层制备与应用[D]. 西安:西安科技大学,2006.
【10】谭澄宇. Ni、Cu基复合镀层制备及其电化学基础研究[D]. 长沙:中南大学,2008.
相关信息