Application of Phosphating Process to Anti-corrosion Coating of Submarine Pipeline
摘 要
介绍了磷化工艺原理、工艺流程及其工艺控制,通过在工业管道上进行3LPE涂敷试验,研究了磷化处理对涂层性能的影响。结果表明:磷化处理提高了钢管的表面质量,涂层附着力得到改善。
Abstract
The principle, treating steps and parameter control of phosphating process are introduced. By applying 3LPE coating onto industry pipes for comparing tests, the effects of phosphating process on the performance of coating were studied. The results showed that the surface quality of the steel pipeline was improved, and coating adhesion property was enhanced after phosphating process.
中图分类号 TG174.4 DOI 10.11973/fsyfh-201611015
所属栏目 应用技术
基金项目
收稿日期 2015/6/29
修改稿日期
网络出版日期
作者单位点击查看
备注李长春(1984-),工程师,研究生,从事海洋油气管道防腐、保温及配重工艺及技术研究工作,
引用该论文: LI Chang-chun,XIANG Zheng-le,WANG Ming-hao,ZHAO Li,JIA Zhen,LV Xi-jun. Application of Phosphating Process to Anti-corrosion Coating of Submarine Pipeline[J]. Corrosion & Protection, 2016, 37(11): 925
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】唐春华. 金属表面磷化技术[M]. 北京:化学工业出版社,2009:1-3.
【2】李汝江,韩秀林,王友生,等. 钢管3PE外防腐工艺的探讨[J]. 焊管,2008,31(6):75-77.
【3】相政乐,王铭浩,贾振,等. 国外管道防腐涂敷中的化学预处理工艺[J]. 石油工程建设,2013,39(1):6-8.
【4】徐学武. 海底油气管道内腐蚀分析与防护[J]. 腐蚀与防护,2014,35(5):500-504.
【5】孙挺,何翊,刘仰硕. JP级钢管磷化的研究[J]. 腐蚀与防护,2004,25(7):301-303.
【6】ALAN K J. Fusion-bonded epoxy a foundation for pipeline corrosion protection[M]. Houston:NACE Press,2003:285-286.
【2】李汝江,韩秀林,王友生,等. 钢管3PE外防腐工艺的探讨[J]. 焊管,2008,31(6):75-77.
【3】相政乐,王铭浩,贾振,等. 国外管道防腐涂敷中的化学预处理工艺[J]. 石油工程建设,2013,39(1):6-8.
【4】徐学武. 海底油气管道内腐蚀分析与防护[J]. 腐蚀与防护,2014,35(5):500-504.
【5】孙挺,何翊,刘仰硕. JP级钢管磷化的研究[J]. 腐蚀与防护,2004,25(7):301-303.
【6】ALAN K J. Fusion-bonded epoxy a foundation for pipeline corrosion protection[M]. Houston:NACE Press,2003:285-286.
相关信息