某汽油加氢脱硫装置引风机系统腐蚀原因及处置措施
Corrosion Reasons and Corresponding Protective Measures of Suction Fan System in a Gasoline Hydrodesulfurization Unit
摘 要
通过对汽油加氢脱硫装置加热炉引风机系统腐蚀产物的现场目测、操作条件和介质组成的考察,探讨了该系统的腐蚀原因。结果表明: 汽油加氢脱硫装置加热炉引风机系统腐蚀的原因是烟气中的硫化物在低温条件下形成的露点腐蚀，并对此具体问题提出了相应的防护措施。
引风机
低温露点腐蚀
防护措施
gasoline hydrodesulfurization
induced draft fan
low temperature dew point corrosion
protective measures
Abstract
The corrosion reasons for the induced draft fan system of heating furnace in a gasoline hydro-desulfurization unit were studied through on-site observation of the corrosion products and investigation of operating conditions and medium composition. The results show that dew point corrosion of sulfur compounds in flue gas at low temperature was the main reason for system corrosion. And some corresponding protective measures were propounded to solve this problem.
中图分类号 TG172 DOI 10.11973/fsyfh-201612016
所属栏目 失效分析
基金项目
收稿日期 2015/7/1
修改稿日期
网络出版日期
作者单位点击查看
备注陶武军(1982-),工程师, 学士,从事炼化设备日常维护技术管理、炼油设备腐蚀防护技术管理的相关研究工作
引用该论文: TAO Wu-jun,QI Yao-guang,ZOU An. Corrosion Reasons and Corresponding Protective Measures of Suction Fan System in a Gasoline Hydrodesulfurization Unit[J]. Corrosion & Protection, 2016, 37(12): 1023
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张德印，张扬. 石化企业火焰加热炉腐蚀及防护措施[J]. 石油化工腐蚀与防护，2005，22（3）: 25-29.
【2】姚庆. 工艺加热炉腐蚀原因分析与对策[J]. 腐蚀与防护，2006，27（2）: 77-79.
【3】李德付. 关于燃气加热炉低温腐蚀的原因与对策[J]. 现代化工，2006，26（1）: 59-61.
【2】姚庆. 工艺加热炉腐蚀原因分析与对策[J]. 腐蚀与防护，2006，27（2）: 77-79.
【3】李德付. 关于燃气加热炉低温腐蚀的原因与对策[J]. 现代化工，2006，26（1）: 59-61.
相关信息