Corrosion Mechanism for Q235 Steel Tube Wall in Outer Tube Gallery of an Oil Company
摘 要
在石油企业外管廊大气环境中对Q235碳钢进行不同腐蚀时间的静态挂片试验，并对现场Q235碳钢钢管进行取样，采用X射线衍射（XRD、X射线光电子能谱（XPS）、扫描电镜（SEM）等技术对Q235碳钢表面腐蚀产物进行分析。结果表明：经过长期腐蚀之后，腐蚀产物中的铁主要是以含氧化合物γ-FeOOH和α-Fe2O3的形式存在；大气中存在的SO2对腐蚀过程具有催化作用。
Q235碳钢
大气腐蚀
SO2
outer tube gallery
Q235 carbon steel
atmospheric corrosion
SO2
Abstract
Static coupon testing for different times was carried out for Q235 carbon steel in the atmospheric corrosion environment of outer tube gallery of an oil company. Q235 carbon steel tubes on site were sampled. The corrosion products on the surface of Q235 carbon steel were analyzed by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM). The results show that the element Fe existed as γ-FeOOH and α-Fe2O3 in corrosion products after long-time corrosion, SO2 in atmosphere worked as catalyst in corrosion process.
中图分类号 TG172 DOI 10.11973/fsyfh-201702010
所属栏目 试验研究
基金项目
收稿日期 2015/8/28
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: DU Yu,YIN Ming-fu. Corrosion Mechanism for Q235 Steel Tube Wall in Outer Tube Gallery of an Oil Company[J]. Corrosion & Protection, 2017, 38(2): 134
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】ELOLA A S,OTERO T F,PORRO A,et al. Evolution of the the pitting of aluminum exposed to the atmosphere[J]. Corrsion,1992,48(10):854-863.
【2】MA Y,LI Y,WANG F. The effect of β-FeOOH on the corrosion behavior of low carbon steel exposed in tropic marine environment[J]. Mater Chem Phys,2008,112:844-852.
【3】安百刚,张学元,韩恩厚,等. 铝和铝合金的大气腐蚀研究现状[J]. 中国有色金属学报,2001,11(增2):11-15.
【4】MA Y,LI Y,WANG F. Corrosion of low carbon steel in atmospheric environments of different chloride content[J]. Corros Sci,2009,51:997-1006.
【5】叶堤. 庆市大气污染对材料腐蚀的研究[D]. 重庆:重庆大学,2005.
【6】王振尧,于全成,汪川,等. 在含硫污染的海洋大气环境中核电用钢的腐蚀行为[J]. 科学通报,2012,57(31):2991-2998.
【7】冯拉俊,马小菊,雷阿利. 硫离子对碳钢腐蚀性的影响[J]. 腐蚀科学与防护技术,2006,18(3):180-182.
【8】卜全民,温力. 炼制高硫原油对设备的腐蚀与安全对策[J]. 腐蚀科学与防护技术,2002,14(6):362-364.
【9】唐俊文,邵亚薇,陈阵. 碳钢在90℃、H2S-HCl-H2O环境下的腐蚀行为[J]. 中国腐蚀与防护学报,2011,31(2):34-38.
【10】汪川,王振尧,柯伟. Q235碳钢在SO2气体中的初期腐蚀行为[J]. 金属学报,2008,44(6):729-734.
【11】汪川,王振尧,柯伟. Q235碳钢在潮湿SO2环境中的初期腐蚀锈层的表征[J]. 科学通报,2008,53(23):2833-2838.
【2】MA Y,LI Y,WANG F. The effect of β-FeOOH on the corrosion behavior of low carbon steel exposed in tropic marine environment[J]. Mater Chem Phys,2008,112:844-852.
【3】安百刚,张学元,韩恩厚,等. 铝和铝合金的大气腐蚀研究现状[J]. 中国有色金属学报,2001,11(增2):11-15.
【4】MA Y,LI Y,WANG F. Corrosion of low carbon steel in atmospheric environments of different chloride content[J]. Corros Sci,2009,51:997-1006.
【5】叶堤. 庆市大气污染对材料腐蚀的研究[D]. 重庆:重庆大学,2005.
【6】王振尧,于全成,汪川,等. 在含硫污染的海洋大气环境中核电用钢的腐蚀行为[J]. 科学通报,2012,57(31):2991-2998.
【7】冯拉俊,马小菊,雷阿利. 硫离子对碳钢腐蚀性的影响[J]. 腐蚀科学与防护技术,2006,18(3):180-182.
【8】卜全民,温力. 炼制高硫原油对设备的腐蚀与安全对策[J]. 腐蚀科学与防护技术,2002,14(6):362-364.
【9】唐俊文,邵亚薇,陈阵. 碳钢在90℃、H2S-HCl-H2O环境下的腐蚀行为[J]. 中国腐蚀与防护学报,2011,31(2):34-38.
【10】汪川,王振尧,柯伟. Q235碳钢在SO2气体中的初期腐蚀行为[J]. 金属学报,2008,44(6):729-734.
【11】汪川,王振尧,柯伟. Q235碳钢在潮湿SO2环境中的初期腐蚀锈层的表征[J]. 科学通报,2008,53(23):2833-2838.
相关信息