Liquidity and Stability on Magnesia Stabilized Zirconia Slurry
摘 要
为了获得流动性和稳定性较好的氧化镁稳定氧化锆浆料,通过黏度测试和沉降试验,并结合Zeta电位和粒径测试,分析了固含量、分散剂加入量、浆料pH和球磨时间对浆料流动性和稳定性的影响。结果表明:随着固含量增大,浆料的黏度增大,流动性变差,稳定性增加;随着分散剂加入量和浆料pH增加以及球磨时间延长,浆料的流动性先增强后变差,稳定性先增强后趋于稳定;浆料呈碱性时,Zeta电位的绝对值较大,浆料的稳定性好;随分散剂加入量增加,Zeta电位的绝对值先增大后减小;当固含量为45%、加入稳定剂的体积分数为2%、浆料pH为9、球磨时间为48 h时,可获得流动性和稳定性均较好的陶瓷浆料。
Abstract
In order to obtain magnesia stabilized zirconia slurry with good liquidity and stability, the effects of solid content, dispersant addition, slurry pH and milling time on the liquidity and stability of slurry were analyzed by viscosity test, sedimentation test and Zeta potential and particle size test. The results show that with the increase of solid content, viscosity and stability of slurry increase and liquidity decreases. Liquidity of slurry increases and then decreases, and the stability increases and then changes little as the increase of dispersant addition, slurry pH and milling time. Absolute value of Zeta potential of the alkaline slurry is larger and its stability is the best. Zeta potential increases and then decreases with the increase of dispersant addition.When the solid content was 45%, volume fraction of dispersant was 2%, slurry pH was 9 and milling time was 48 h, the ceramic slurry can obtain better liquidity and stability.
中图分类号 TQ174 DOI 10.11973/jxgccl201702010
所属栏目 试验研究
基金项目
收稿日期 2015/12/1
修改稿日期 2016/12/8
网络出版日期
作者单位点击查看
备注杜亚男(1988-),女,山东临沂人,工程师,硕士。
引用该论文: DU Ya-nan,XIE Jian-lin. Liquidity and Stability on Magnesia Stabilized Zirconia Slurry[J]. Materials for mechancial engineering, 2017, 41(2): 51~54
杜亚男,谢建林. 氧化镁稳定氧化锆浆料的流动性和稳定性[J]. 机械工程材料, 2017, 41(2): 51~54
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】孙静,黄传真,刘含莲,等.稳定氧化锆陶瓷的研究现状[J]. 机械工程材料,2005,29(8):1-3.
【2】ZHANG H, LU H, ZHU Y W,et al. Preparations and characterizations of new mesoporous ZrO2 and Y2O3-stabilized ZrO2 spherical powders[J]. Powder Technology, 2012, 22(7):9-16.
【3】马亚鲁,马卫兵,郑俊萍,等.少量掺杂Al2O3,SiO2的Mg-PSZ陶瓷材料的液相烧结[J].硅酸盐通报,2000(5):32-35.
【4】OHTSUKA H, MIZUTANI H, LIO S,et al. Effects of sintering additives on dispersion properties of Al2O3 slurry containing polyacrylic acid dispersant[J]. Journal of the European Ceramic Society, 2011, 31(4):517-522.
【5】CHIN C H, MUCHTAR A, AZHARI C H, et al. Optimization of pH and dispersant amount of Y-TZP suspension for colloidal stability[J]. Ceramics International, 2015, 41(8):9939-9946.
【6】BRISEOE B J, BIUNDO G L, OZKAN N. Drying kineties of water-based ceramic suspensions for tape casting[J]. Ceram Int, 1998, 24:347-357.
【7】ZVRCHER S, GRAULE T. Influence of dispersant structure on the rheological properties of highly-concentrated zirconia dispersions[J]. Euro Ceram Soc, 2005, 25(6):863-873.
【8】刘阳桥,高濂,孙静,等.丙烯酸类共聚物对纳米Y-TZP水悬浮液性质的影响[J]. 高等学校化学学报,2001,22(10):1738-1740.
【9】李明利,梁辉,徐明霞,等.分散剂用量对钛酸锶钡水基浆料稳定性的影响[J]. 硅酸盐学报,2007,35(11):1453-1456.
【10】周邵萍,葛晓陵.TiO2悬浮液颗粒团聚机理及团聚体分形特征研究[J]. 硅酸盐通报,2013,32(8):1680-1683.
【11】周芳,刘冠芳,刘斌,等.钛酸钡陶瓷浆料流变性研究[J]. 绝缘材料,2009,42(2):48-51.
【12】LIU T C, CHIU S J. Effect of metal loading sequence on the activity of Sn-Ni/C for methanol carbonylation[J]. Appl Catal, 1994, 117(1):17-27.
【2】ZHANG H, LU H, ZHU Y W,et al. Preparations and characterizations of new mesoporous ZrO2 and Y2O3-stabilized ZrO2 spherical powders[J]. Powder Technology, 2012, 22(7):9-16.
【3】马亚鲁,马卫兵,郑俊萍,等.少量掺杂Al2O3,SiO2的Mg-PSZ陶瓷材料的液相烧结[J].硅酸盐通报,2000(5):32-35.
【4】OHTSUKA H, MIZUTANI H, LIO S,et al. Effects of sintering additives on dispersion properties of Al2O3 slurry containing polyacrylic acid dispersant[J]. Journal of the European Ceramic Society, 2011, 31(4):517-522.
【5】CHIN C H, MUCHTAR A, AZHARI C H, et al. Optimization of pH and dispersant amount of Y-TZP suspension for colloidal stability[J]. Ceramics International, 2015, 41(8):9939-9946.
【6】BRISEOE B J, BIUNDO G L, OZKAN N. Drying kineties of water-based ceramic suspensions for tape casting[J]. Ceram Int, 1998, 24:347-357.
【7】ZVRCHER S, GRAULE T. Influence of dispersant structure on the rheological properties of highly-concentrated zirconia dispersions[J]. Euro Ceram Soc, 2005, 25(6):863-873.
【8】刘阳桥,高濂,孙静,等.丙烯酸类共聚物对纳米Y-TZP水悬浮液性质的影响[J]. 高等学校化学学报,2001,22(10):1738-1740.
【9】李明利,梁辉,徐明霞,等.分散剂用量对钛酸锶钡水基浆料稳定性的影响[J]. 硅酸盐学报,2007,35(11):1453-1456.
【10】周邵萍,葛晓陵.TiO2悬浮液颗粒团聚机理及团聚体分形特征研究[J]. 硅酸盐通报,2013,32(8):1680-1683.
【11】周芳,刘冠芳,刘斌,等.钛酸钡陶瓷浆料流变性研究[J]. 绝缘材料,2009,42(2):48-51.
【12】LIU T C, CHIU S J. Effect of metal loading sequence on the activity of Sn-Ni/C for methanol carbonylation[J]. Appl Catal, 1994, 117(1):17-27.
相关信息