Q195钢盘条折弯开裂原因分析
Analysis on Cracking Reasons during Bending of Q195 Steel Wire Rods
摘 要
规格为φ6.5 mm的Q195钢热轧盘条，拉拔至φ5.0 mm弯折后出现开裂。通过宏观观察、化学成分分析、金相检验、扫描电镜及能谱分析的方法，对盘条折弯开裂的原因进行了分析。结果表明：严重的混晶组织在折弯力的作用下产生裂纹，裂纹沿夹杂物扩展，最终造成盘条的折弯开裂。
盘条
折弯开裂
混晶
夹杂物
Q195 steel
steel wire rod
cracking during bending
mixed crystal
inclusion
Abstract
Q195 steel hot-rolled wire rods cracked during bending after drawing from φ6.5 mm to φ5.0 mm. The reasons of cracking during bending of steel wire rods were analyzed by means of macroscopic observation, chemical composition analysis, metallographic examination, scanning electron microscope and energy spectrum analysis. The results show that: severe mixed crystal structure led to the formation of cracks under the action of bending force; cracks extended along the inclusions, and finally caused the cracking during bending of the steel wire rods.
中图分类号 TG335.6+3 TG115.2 DOI 10.11973/lhjy-wl201703015
所属栏目 质量控制与失效分析
基金项目
收稿日期 2016/6/10
修改稿日期
网络出版日期
作者单位点击查看
备注林柱(1987-),男,工程师,学士,主要从事钢铁材料理化检测工作,xiaoaoabc@163.com。
引用该论文: LIN Zhu,NI Wen-xiao,WANG Li-tao,XUE Jun-feng,WANG Gang. Analysis on Cracking Reasons during Bending of Q195 Steel Wire Rods[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2017, 53(3): 212～213
林柱,倪文啸,王立涛,薛俊峰,王刚. Q195钢盘条折弯开裂原因分析[J]. 理化检验－物理分册, 2017, 53(3): 212～213
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】朱伯平,牛海云.提高Q195L盘条拉拔性能的工艺研究[J].南方金属,2008,6(3):21-25.
【2】张亚军,吴艳杰,高寒蕾.冷轧Q195L带钢表面翘皮缺陷分析[J].理化检验-物理分册,2009,45(9):579-582.
【3】罗兴壮,苏捷杰.低碳冷镦钢盘条混晶组织分析与改进[J].柳钢科技,2015(6):19-21.
【4】周刚,高长益,蔡晓霞.H08A焊丝钢拉拔断裂分析[J].理化检验-物理分册,2013,49(7):472-475.
【2】张亚军,吴艳杰,高寒蕾.冷轧Q195L带钢表面翘皮缺陷分析[J].理化检验-物理分册,2009,45(9):579-582.
【3】罗兴壮,苏捷杰.低碳冷镦钢盘条混晶组织分析与改进[J].柳钢科技,2015(6):19-21.
【4】周刚,高长益,蔡晓霞.H08A焊丝钢拉拔断裂分析[J].理化检验-物理分册,2013,49(7):472-475.
相关信息