Preparation and Property of Graphene/Polylactic Acid Composite
摘 要
分别以两种粒径(20,125μm)的聚乳酸为基体材料,石墨烯为增强材料,利用球磨法制备了石墨烯/聚乳酸复合粉,再在150℃下压制成两种石墨烯/聚乳酸复合材料,研究了其弯曲性能和导电性能。结果表明:在机械咬合与静电吸附共同作用下,石墨烯包覆在聚乳酸微粒表面形成复合微粒;随石墨烯含量的增加,两种聚乳酸复合材料的抗弯强度均先增大后降低,电导率则先快速增大后趋于平缓,且聚乳酸粒径较小时的复合材料性能更佳,但过多石墨烯又会使复合材料表面出现裂纹、破碎等缺陷;随着成型压力的增大,复合材料的电导率小幅度增加,但抗弯强度变化不明显。
Abstract
Using polylactic acid with two particle size (20, 125 μm) as substrate material, respectively, and graphene as reinforcing material, the graphene/polylactic acid composite powders were prepared by ball milling, then pressed to two graphene/polylactic acid composites at 150 ℃. The bending performance and conductivity of the composites were studied. The results show that the graphene was coated on the surface of polylactic acid particles to form composite particles under the combining effects of mechanical interlocking and electrostatic adsorption. With the increase of graphene content, the bending strength of the two composites first increased then decreased, and the conductivity increased first rapidly then gently, and achieved relatively good values using polylactic acid with relatively small particle size. But too much graphene resulted in the defects on the surface of composites, such as cracks and broken. With the increase of molding pressure, the conductivity of the composite increased slightly, but the bending strength changed not obviously.
中图分类号 TB332 DOI 10.11973/jxgccl201704011
所属栏目 新材料 新工艺
基金项目 国家自然科学基金资助项目(51575313);湖北省自然科学基金资助项目(2014CFB678);华中科技大学材料成型与模具技术国家重点实验室开放基金资助项目(P2015-11)
收稿日期 2016/8/23
修改稿日期 2017/2/24
网络出版日期
作者单位点击查看
备注吴海华(1970-),男,湖北黄冈人,教授,博士.
引用该论文: WU Hai-hua,WU Zhao,LÜ,Jia-wei,WANG Dao,LIU Ning. Preparation and Property of Graphene/Polylactic Acid Composite[J]. Materials for mechancial engineering, 2017, 41(4): 49~53
吴海华,吴朝,吕佳炜,王道,柳宁. 石墨烯/聚乳酸复合材料的制备及性能[J]. 机械工程材料, 2017, 41(4): 49~53
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】杜雪娟. 有限的可选材料阻碍3D打印发展[J]. 现代塑料加工应用, 2015, 27(5):24-24.
【2】王欢欢. 聚乳酸/功能化石墨烯纳米复合薄膜的制备及其结构与性能的研究[D]. 郑州:郑州大学, 2014.
【3】史成波. 石墨烯/聚乳酸纳米复合材料的制备与性能研究[D]. 天津:天津工业大学, 2013.
【4】王成成, 李梦倩, 雷文,等. 3D打印用聚乳酸及其复合材料的研究进展[J]. 塑料科技, 2016,44(6):89-91.
【5】GÓMEZ-NAVARRO C, BURGHARD M, KERN K. Elastic properties of chemically derived single graphene sheets[J].Nano Letters, 2008, 8(7):2045-2049.
【6】谢续明, 杨睿. 若干高性能高分子材料研究进展[J]. 机械工程材料, 2015, 39(7):1-10.
【7】任俊, 卢寿慈. 超细粉体在液相中的分散[J]. 中国粉体工业, 2006(5):13-17.
【8】贾晓林, 谭伟. 纳米粉体分散技术发展概况[J]. 非金属矿, 2003, 26(4):1-3.
【9】KIM I H, JEONG Y G. Polylactide/exfoliated graphite nanocomposites with enhanced thermal stability, mechanical modulus, and electrical conductivity[J]. Journal of Polymer Science Part B: Polymer Physics, 2010, 48(8): 850-858.
【10】SABZI M, JIANG L, LIU F, et al. Graphene nanoplatelets as poly(lactic acid) modifier: linear rheological behavior and electrical conductivity[J]. Journal of Materials Chemistry A, 2013, 1(28): 8253-8261.
【11】LI W, XU Z, CHEN L, et al. A facile method to produce graphene oxide-g-poly(L-lactic acid) as an promising reinforcement for PLLA nanocomposites[J]. Chemical Engineering Journal, 2014, 237(1):291-299.
【12】吴海华, 李厅, 黄川,等. 细鳞片石墨复合密封板材的制备及性能[J]. 机械工程材料, 2015, 39(6):36-39.
【13】张兵兵, 洪若瑜. 石墨烯的制备及其在环氧树脂中的应用[J]. 中国粉体技术, 2015,21(6):40-42.
【14】NORIOKI M. 塑料的抗静电处理[J]. 国外塑料, 1986(4):35-42.
【15】丁芳. 塑料薄膜抗静电性能的研究和测试[J]. 中国化工贸易, 2012(11):86-87.
【2】王欢欢. 聚乳酸/功能化石墨烯纳米复合薄膜的制备及其结构与性能的研究[D]. 郑州:郑州大学, 2014.
【3】史成波. 石墨烯/聚乳酸纳米复合材料的制备与性能研究[D]. 天津:天津工业大学, 2013.
【4】王成成, 李梦倩, 雷文,等. 3D打印用聚乳酸及其复合材料的研究进展[J]. 塑料科技, 2016,44(6):89-91.
【5】GÓMEZ-NAVARRO C, BURGHARD M, KERN K. Elastic properties of chemically derived single graphene sheets[J].Nano Letters, 2008, 8(7):2045-2049.
【6】谢续明, 杨睿. 若干高性能高分子材料研究进展[J]. 机械工程材料, 2015, 39(7):1-10.
【7】任俊, 卢寿慈. 超细粉体在液相中的分散[J]. 中国粉体工业, 2006(5):13-17.
【8】贾晓林, 谭伟. 纳米粉体分散技术发展概况[J]. 非金属矿, 2003, 26(4):1-3.
【9】KIM I H, JEONG Y G. Polylactide/exfoliated graphite nanocomposites with enhanced thermal stability, mechanical modulus, and electrical conductivity[J]. Journal of Polymer Science Part B: Polymer Physics, 2010, 48(8): 850-858.
【10】SABZI M, JIANG L, LIU F, et al. Graphene nanoplatelets as poly(lactic acid) modifier: linear rheological behavior and electrical conductivity[J]. Journal of Materials Chemistry A, 2013, 1(28): 8253-8261.
【11】LI W, XU Z, CHEN L, et al. A facile method to produce graphene oxide-g-poly(L-lactic acid) as an promising reinforcement for PLLA nanocomposites[J]. Chemical Engineering Journal, 2014, 237(1):291-299.
【12】吴海华, 李厅, 黄川,等. 细鳞片石墨复合密封板材的制备及性能[J]. 机械工程材料, 2015, 39(6):36-39.
【13】张兵兵, 洪若瑜. 石墨烯的制备及其在环氧树脂中的应用[J]. 中国粉体技术, 2015,21(6):40-42.
【14】NORIOKI M. 塑料的抗静电处理[J]. 国外塑料, 1986(4):35-42.
【15】丁芳. 塑料薄膜抗静电性能的研究和测试[J]. 中国化工贸易, 2012(11):86-87.
相关信息