Safety Analysis of Single Defect Corroded Submarine Pipe under Combining Load
摘 要
采用许用应力法对腐蚀海底管道的安全性进行评估,并通过有限元模拟对组合载荷(内压与轴向压应力叠加作用)下单缺陷腐蚀海底管道进行应力分析,探讨了影响管道峰值应力的缺陷几何参数的敏感性。结果表明:轴向压应力一定时,随内压不断增加,管道有效应力呈先下降后上升的变化趋势,进入屈服稳定阶段后,有效应力继续增大,直至管道破坏。
Abstract
The safety of corroded submarine pipe was assessed according to allowable stress approach. The stress in single defect corroded pipe under combining load (internal pressure and compressive load along longitudinal axis) was analyzed through finite element simulation. The sensibility of geometry parameters that affected the maximum pressure of pipe was studied. The results show that effective stress of pipe displayed a tendency of increase first and then decrease with the increase of internal pressure, as the value of compressive longitudinal stress of corroded pipe kept stable. Then the pipe reached stable yielding stage until failure.
中图分类号 P751 DOI 10.11973/fsyfh-201704014
所属栏目 应用技术
基金项目
收稿日期 2016/11/21
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: HUANG Yu-li,YANG Dong-quan,LU Ping,LI Xue-xun. Safety Analysis of Single Defect Corroded Submarine Pipe under Combining Load[J]. Corrosion & Protection, 2017, 38(4): 311
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】DNV-RP-F101 Corroded pipelines[S].
【2】韩文海,周晶. 腐蚀海底管道可靠性分析[J]. 石油学报,2015,36(4):516-520.
【3】YAN S T,SHEN X L,JIN Z J,et al. On elastic-plastic collapse of subsea pipelines under external hydrostatic pressure and denting force[J]. Applied Ocean Research,2016,58:305-321.
【4】AKBARI ALASHTI R,JAFARI S,HOSSEINIPOUR S J. Experimental and numerical investigation of ductile damage effect on load bearing capacity of a dented API XB pipe subjected to internal pressure[J]. Engineering Failure Analysis,2014,47:208-228.
【5】NETTO T A. On the effect of narrow and long corrosion defects on the collapse pressure of pipelines[J]. Applied Ocean Research,2009,31:75-81.
【6】谭开忍,肖熙. 含有腐蚀缺陷海底管道极限载荷分析[J]. 海洋工程,2006,24(3):63-67.
【7】API 579-1/ASME FFS-1 Fitness-for-service standard second edition[S].
【8】中国船级社. 海底管道结构分析指南[M]. 北京:人民交通出版社,2007.
【9】GONG S F,YUAN L,JIN W L. Buckling response of offshore pipelines under combined tension,bending,and external pressure[J]. Journal of Zhejiang University—SCIENCE A,2011,12(8):627-636.
【10】CHIODO M S G,RUGGIERI C. Failure assessments of corroded pipelines with axial defects using stress-based criteria:Numerical studies and verification analyses[J]. International Journal of Pressure Vessels and Piping,2009,86:164-176.
【11】赵冬岩,余建星,岳志勇,等. 含缺陷海底管道屈曲稳定性的数值模拟[J]. 天津大学学报,2009,42(12):1067-1071.
【12】NETTO T A. A simple procedure for the perdiction of the collapse pressure of pipelines with narrow and long corrosion defects-correlation with new experimental data[J]. Applied Ocean Research,2010,32:132-134.
【2】韩文海,周晶. 腐蚀海底管道可靠性分析[J]. 石油学报,2015,36(4):516-520.
【3】YAN S T,SHEN X L,JIN Z J,et al. On elastic-plastic collapse of subsea pipelines under external hydrostatic pressure and denting force[J]. Applied Ocean Research,2016,58:305-321.
【4】AKBARI ALASHTI R,JAFARI S,HOSSEINIPOUR S J. Experimental and numerical investigation of ductile damage effect on load bearing capacity of a dented API XB pipe subjected to internal pressure[J]. Engineering Failure Analysis,2014,47:208-228.
【5】NETTO T A. On the effect of narrow and long corrosion defects on the collapse pressure of pipelines[J]. Applied Ocean Research,2009,31:75-81.
【6】谭开忍,肖熙. 含有腐蚀缺陷海底管道极限载荷分析[J]. 海洋工程,2006,24(3):63-67.
【7】API 579-1/ASME FFS-1 Fitness-for-service standard second edition[S].
【8】中国船级社. 海底管道结构分析指南[M]. 北京:人民交通出版社,2007.
【9】GONG S F,YUAN L,JIN W L. Buckling response of offshore pipelines under combined tension,bending,and external pressure[J]. Journal of Zhejiang University—SCIENCE A,2011,12(8):627-636.
【10】CHIODO M S G,RUGGIERI C. Failure assessments of corroded pipelines with axial defects using stress-based criteria:Numerical studies and verification analyses[J]. International Journal of Pressure Vessels and Piping,2009,86:164-176.
【11】赵冬岩,余建星,岳志勇,等. 含缺陷海底管道屈曲稳定性的数值模拟[J]. 天津大学学报,2009,42(12):1067-1071.
【12】NETTO T A. A simple procedure for the perdiction of the collapse pressure of pipelines with narrow and long corrosion defects-correlation with new experimental data[J]. Applied Ocean Research,2010,32:132-134.
相关信息