Analysis on Fracture Reasons of Rectangular Hanging Plates of Hanging Fittings in the 220 kV Electric Transmission Line
摘 要
某220 kV输电线路悬垂金具直角挂板发生断裂事故。通过对该事故背景进行分析,结合宏观检测、载荷分析、断口扫描电镜及能谱分析的方法,从金具的连接方式、运行环境、材质状况等方面分析了该220 kV输电线路悬垂金具直角挂板的断裂原因。结果表明:该直角挂板在制造时已经存在裂纹,在腐蚀介质和大风的共同作用下裂纹不断扩展,最终直角挂板发生腐蚀疲劳断裂。最后针对断裂原因提出了预防措施。
Abstract
A fracture accident of the rectangular hanging plates of hanging fittings occurred in a 220 kV electric transmission line. Based on the analysis of the accident background, through the macroscopic inspection, load analysis, scanning electron microscope and spectrum analysis of the fracture, the fracture reasons were analyzed from the aspects of the connection type, operation environment, material quality condition, and so on. The results show that:there were some cracks in the rectangular hanging plates during manufacturing process; under the combined action of corrosive medium and high wind, cracks propagated constantly, and eventually led to the corrosion fatigue fracture of the rectangular hanging plates. Finally, some preventive measures were proposed according to the fracture reasons.
中图分类号 TM75 TG115 DOI 10.11973/lhjy-wl201705013
所属栏目 质量控制与失效分析
基金项目
收稿日期 2016/7/28
修改稿日期
网络出版日期
作者单位点击查看
备注洪毅成(1981-),男,工程师,主要从事电网金属材料失效分析研究,hongych99@126.com
引用该论文: HONG Yicheng,CAI Jianbin. Analysis on Fracture Reasons of Rectangular Hanging Plates of Hanging Fittings in the 220 kV Electric Transmission Line[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2017, 53(5): 361~364
洪毅成,蔡建宾. 220kV输电线路悬垂金具直角挂板断裂原因分析[J]. 理化检验-物理分册, 2017, 53(5): 361~364
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】邓大勇, 闫斌,何喜梅,等.110 kV线路"Z"型挂板断裂分析[J].青海电力,2011,30(4):51-53.
【2】柴志华,张树林,蔚泽廷.220 kV忻义线116号金具断裂分析[J].山西电力,2013(2):67-69.
【3】武家升,刘亮,李朋.35 kV套管线夹断裂原因分析[J].理化检验-物理分册,2015,51(7):517-519.
【4】王荣辉.500 kV输电线路金具断裂原因分析及处理措施[J].科技致富向导,2014(3):94-95.
【5】毕虎才,董勇军,冀晋川.电网线路金具断裂及预防[J].山西电力,2014(1):22-24.
【6】钟群鹏,赵子华.断口学[M].北京:高等教育出版社,2015:242-258.
【2】柴志华,张树林,蔚泽廷.220 kV忻义线116号金具断裂分析[J].山西电力,2013(2):67-69.
【3】武家升,刘亮,李朋.35 kV套管线夹断裂原因分析[J].理化检验-物理分册,2015,51(7):517-519.
【4】王荣辉.500 kV输电线路金具断裂原因分析及处理措施[J].科技致富向导,2014(3):94-95.
【5】毕虎才,董勇军,冀晋川.电网线路金具断裂及预防[J].山西电力,2014(1):22-24.
【6】钟群鹏,赵子华.断口学[M].北京:高等教育出版社,2015:242-258.
相关信息