Cracking Reason and Solution for Head Plate Made of Explosive Welding Stainless Complex Steel Plate
摘 要
对16台大型爆炸焊不锈钢复合钢板制压力容器进行检验,发现14台容器封头内部存在大量裂纹,通过宏观检查、硬度测试、金相检测、磁记忆检测、介质组分分析等方法,确定封头内壁裂纹属应力腐蚀裂纹。磁记忆检测出裂纹发生的部位均为高应力区,与介质中含有的敏感性F-、Cl-共同作用导致应力腐蚀开裂的发生。对封头产生的高应力进行了分析,对大型复合钢板封头的选取及裂纹的处理提出了建议。
Abstract
By the inspection of 16 large pressure vessels of explosive welding stainless complex steel plates, amounts of crack were found in 14 vessel heads, the cracking in heads was determined as stress corrosion cracking by macrography, hardness test, optical microscopy, magnetic memory testing, medium component analysis etc. High stress area was in the location where cracking occurred. Under the combined action of the stress and corrosive medium of F- and Cl-, stress corrosion cracking in heads occured. High stress in head was analyzed, and large complex steel plate head type choice and crack treatment were proposed.
中图分类号 TG172 DOI 10.11973/fsyfh-201707013
所属栏目 应用技术
基金项目
收稿日期 2015/12/24
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHU Yanxuan,BAI Mingqing,WANG Likun,GUO Jinding,LIU Jiafei. Cracking Reason and Solution for Head Plate Made of Explosive Welding Stainless Complex Steel Plate[J]. Corrosion & Protection, 2017, 38(7): 543
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】中国石化设备管理协会. 石油化工装置设备腐蚀与防护手册[M]. 北京:中国石化出版社,2001:411-412.
【2】谢铁军,刘东学,陈钢,等. 压力容器应力分布图谱[M]. 北京:北京科学技术出版社,1994.
【3】陈可华,金元文. 椭圆形封头的受力分析[J]. 机械设计与制造,2007(3):37-39,55.
【4】付磊,罗云蓉,付伶. 球形封头的应力分布研究[J]. 机械设计与制造,2013(10):209-212.
【5】任晶波,王殿祥,王晓旭,等. 不锈钢等复合钢板热处理状态对各项性能的影响[J]. 石油和化工设备,2012(6):16-19.
【6】孙望秋. 材质及高,中温消应处理对不锈复合钢板耐蚀性的影响[J]. 南化科技,1993,14(4):30-32.
【2】谢铁军,刘东学,陈钢,等. 压力容器应力分布图谱[M]. 北京:北京科学技术出版社,1994.
【3】陈可华,金元文. 椭圆形封头的受力分析[J]. 机械设计与制造,2007(3):37-39,55.
【4】付磊,罗云蓉,付伶. 球形封头的应力分布研究[J]. 机械设计与制造,2013(10):209-212.
【5】任晶波,王殿祥,王晓旭,等. 不锈钢等复合钢板热处理状态对各项性能的影响[J]. 石油和化工设备,2012(6):16-19.
【6】孙望秋. 材质及高,中温消应处理对不锈复合钢板耐蚀性的影响[J]. 南化科技,1993,14(4):30-32.
相关信息