工件表面油漆层厚度对焊缝磁粉检测的影响
Influence of Workpiece Surface Paint Layer Thickness on the Weld Magnetic Particle Testing
摘 要
通过对一定状态下（母材为低碳钢Q345D，焊材为灰铸铁焊丝HS401，焊完急速水冷却）带油漆层的焊缝工件进行磁粉检测，分析了油漆层厚度对磁粉检测灵敏度的影响，所得结果可供同行参考。
磁粉检测
试板
裂纹
paintlayer
magnetic particle testing
test plate
crack
Abstract
Magnetic particle testing was carried out for workpieces with various paint layers under some special conditions (low carbon steel Q345D for parent metal, the gray cast iron wire HS401 for weld material, and a rapid water cooling after finishing welding), in order to study the influence of paint layer thickness on magnetic particle detection sensitivity, which might provide useful reference for the others.
中图分类号 TG115.28 DOI 10.11973/wsjc201707013
所属栏目 试验研究
基金项目
收稿日期 2016/4/9
修改稿日期
网络出版日期
作者单位点击查看
备注苏鹏涛(1984-),男,工程师,主要从事钢结构无损检测技术研究工作
引用该论文: SU Pengtao. Influence of Workpiece Surface Paint Layer Thickness on the Weld Magnetic Particle Testing[J]. Nondestructive Testing, 2017, 39(7): 58～60
苏鹏涛. 工件表面油漆层厚度对焊缝磁粉检测的影响[J]. 无损检测, 2017, 39(7): 58～60
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王珍.带涂层工件磁粉检测的实验分析[J]. 黑龙江电力, 2011,33(6):470-471.
【2】李亚江. 焊接缺陷分析与对策[M]. 北京:化学工业出版社,2011.
【3】宋志哲. 磁粉检测 [M]. 北京:中国劳动社会保障出版社,2007.
【4】张世远,路权,薛荣华,等.磁性材料基础[M]. 北京:科学出版社,1988.
【2】李亚江. 焊接缺陷分析与对策[M]. 北京:化学工业出版社,2011.
【3】宋志哲. 磁粉检测 [M]. 北京:中国劳动社会保障出版社,2007.
【4】张世远,路权,薛荣华,等.磁性材料基础[M]. 北京:科学出版社,1988.
相关信息