海上油田生产系统的腐蚀
Corrosion of Production Systems for Offshore Oilfield
摘 要
对南海某油田生产系统的采出水水质和腐蚀区域产物进行了分析。结果表明：该油田生产系统的腐蚀主要是高温CO2引起的点蚀；同时，采出水明显的CaCO3结垢倾向、高矿化度、高Cl-含量会提高点蚀发生的概率。向油井中连续投加高温缓蚀剂，可使油田的腐蚀得到很好的控制。
CO2腐蚀
缓蚀剂
oilfiled
CO2 corrosion
corrosion inhibitor
Abstract
Produced water quality and corrosion products of the production system of an offshore oilfield in the South China Sea were analyzed.The results show that the main cause of the production system corrosion was pitting corrosion resulting from CO2 at high temperature.And obvious scaling tendency of CaCO3,high TDS (total dissolved solid) and high content of Cl- for produced water promoted the probability of pitting.The corrosion was controlled well by continuous adding high temperature corrosion inhibitor.
中图分类号 TG174 DOI 10.11973/fsyfh-201708013
所属栏目 失效分析
基金项目
收稿日期 2015/12/22
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: XUE Rui,YIN Shuo,HAO Lansuo. Corrosion of Production Systems for Offshore Oilfield[J]. Corrosion & Protection, 2017, 38(8): 637
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陈宏程,吴涛,郝兰锁. 西江油田115邮轮腐蚀探析[J]. 广州化工,2015,43(4):166-167,226.
【2】刘长坤,李春福,赵海杰,等. 高矿化度油气田盐卤水对碳钢的腐蚀行为研究[J]. 西南石油大学学报(自然科学版),2010,32(2):154-158.
【3】郝兰锁,明云峰,徐应波,等. 海上油田腐蚀探析及防护[J]. 工业水处理,2012,32(6):74-76.
【4】林冠发,白真权,赵新伟,等. 温度对二氧化碳腐蚀产物膜形貌特征的影响[J]. 石油学报,2004,25(3):101-109.
【5】张绍广. 海上油田原油处理系统腐蚀结垢的预测与评价[J]. 腐蚀与防护,2009,30(11):818-821.
【6】徐应波,吴涛,刘殿宇,等. 海上油田生产水系统结垢研究与控制[J]. 工业水处理,2013,33(6):82-84.
【7】叶帆. 凝析气田集输管道腐蚀原因分析[J]. 天然气与石油,2010,28(1):10-13.
【2】刘长坤,李春福,赵海杰,等. 高矿化度油气田盐卤水对碳钢的腐蚀行为研究[J]. 西南石油大学学报(自然科学版),2010,32(2):154-158.
【3】郝兰锁,明云峰,徐应波,等. 海上油田腐蚀探析及防护[J]. 工业水处理,2012,32(6):74-76.
【4】林冠发,白真权,赵新伟,等. 温度对二氧化碳腐蚀产物膜形貌特征的影响[J]. 石油学报,2004,25(3):101-109.
【5】张绍广. 海上油田原油处理系统腐蚀结垢的预测与评价[J]. 腐蚀与防护,2009,30(11):818-821.
【6】徐应波,吴涛,刘殿宇,等. 海上油田生产水系统结垢研究与控制[J]. 工业水处理,2013,33(6):82-84.
【7】叶帆. 凝析气田集输管道腐蚀原因分析[J]. 天然气与石油,2010,28(1):10-13.
相关信息