摘 要
为了研究3PE防腐蚀层服役过程中的失效问题,采用现场测试、实验室分析和模拟试验等方法对服役中3PE防腐蚀层的剥离问题进行了分析,并对其寿命进行了预测。结果表明:生产过程中表面处理、环氧粉末喷涂等工艺控制不当,服役过程中防腐蚀层破损、阴极保护电位过负等环境因素,均会导致3PE防腐蚀层的剥离;同样的电流密度下,随着时间的延长,阴极剥离距离逐渐增加,且在试验前期增加较快,在试验后期增加变缓;相同时间下,施加的电流密度越高,阴极剥离距离越大,3PE防腐蚀层的特征寿命与电流密度的倒数呈指数关系。
Abstract
To study the failure problems of 3PE anticorrosion layer,testing on the spot,lab analysis and simulated experiments were used to study the disbondment of 3PE anticorrosion layer and predict its life.The results show that the bad processing control in the production such as surface treatment and fusion bonded epoxy (FBE) spray and the environmental factors such as coating damage and too negative cathodic protection potential caused the disbondment of 3PE anticorrosion layer.At the same current density,cathodic disbondment distance increased as the test period increased.The increase rate of cathodic disbondment distance was high at the early stage of test and was low at the late stage of test.In the same testing period,cathodic disbondment distance increased with the increase of current density and the characteristic life of the 3PE anticorrosion layer had exponent relationship with the reciprocal of current density.
中图分类号 TG172.4 DOI 10.11973/fsyfh-201708016
所属栏目 失效分析
基金项目
收稿日期 2016/10/8
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHU Lin,CUI Wei,XING Yunying,ZHONG Ting,DONG Liang,WANG Xiuyun. Failure Analysis and Life Prediction for 3PE Anticorrosion Layer[J]. Corrosion & Protection, 2017, 38(8): 650
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】胡士信,董旭. 我国管道防腐层技术现状[J]. 油气储运,2004,23(7):4-8.
【2】陈群尧,王善学,李建忠,等. 地钢质管道新型三层PE防腐层的结构设计[J]. 油气储运,2001,20(1):17-22.
【3】尹国耀,雷胜利. 3PE管道防腐在国内十年的实践[J]. 焊管,2007,30(1):8-11.
【4】张婷,龚敏,林修洲. 3PE防腐蚀层联合阴极保护对管道的保护效果[J]. 腐蚀与防护,2012,33(9):765-768.
【5】吕德东. 油田埋地管道防腐层破损点检测及影响因素[J]. 管道技术与设备,2007(3):39-40.
【6】孟繁亮. 管道防腐层破损原因及检测技术探讨[J]. 化学工程与设备,2012(5):107-111.
【7】代卿,青树勇. 天然气管道三层PE防腐层的常见失效模[J]. 内蒙古石油化工,2011(6):65-66.
【8】埋地钢质管道聚乙烯防腐层:GB/T 23257-2009[S].
【9】管道聚乙烯防腐层技术标准:SY/T 0413-2002[S].
【10】Petroleum and natural gas industries-external coatings for buried or submerged pipelines used in pipeline transportation systems:ISO 21809.1:2011[S].
【11】External fusion bond epoxy coating for steel pipe/external polyethylene coating for pipe:CSA Z245.20/21-2006[S].
【12】挤压出式外部聚乙烯涂层:NFA-49-710-1988[S].
【13】Polyethylene coatings on steel pipes and fittings-Requirements and testings:DIN 30670-2016[S].
【14】Material and construction standard for three layer polyethylene coating system:IPS-G-TP-335-2007[S].
【2】陈群尧,王善学,李建忠,等. 地钢质管道新型三层PE防腐层的结构设计[J]. 油气储运,2001,20(1):17-22.
【3】尹国耀,雷胜利. 3PE管道防腐在国内十年的实践[J]. 焊管,2007,30(1):8-11.
【4】张婷,龚敏,林修洲. 3PE防腐蚀层联合阴极保护对管道的保护效果[J]. 腐蚀与防护,2012,33(9):765-768.
【5】吕德东. 油田埋地管道防腐层破损点检测及影响因素[J]. 管道技术与设备,2007(3):39-40.
【6】孟繁亮. 管道防腐层破损原因及检测技术探讨[J]. 化学工程与设备,2012(5):107-111.
【7】代卿,青树勇. 天然气管道三层PE防腐层的常见失效模[J]. 内蒙古石油化工,2011(6):65-66.
【8】埋地钢质管道聚乙烯防腐层:GB/T 23257-2009[S].
【9】管道聚乙烯防腐层技术标准:SY/T 0413-2002[S].
【10】Petroleum and natural gas industries-external coatings for buried or submerged pipelines used in pipeline transportation systems:ISO 21809.1:2011[S].
【11】External fusion bond epoxy coating for steel pipe/external polyethylene coating for pipe:CSA Z245.20/21-2006[S].
【12】挤压出式外部聚乙烯涂层:NFA-49-710-1988[S].
【13】Polyethylene coatings on steel pipes and fittings-Requirements and testings:DIN 30670-2016[S].
【14】Material and construction standard for three layer polyethylene coating system:IPS-G-TP-335-2007[S].
相关信息