有机涂层防护性能与失效评价研究进展
Research Advances of Protective Performance and Failure Evaluation for Organic Coatings
摘 要
简要综述了近年来评价有机涂层防护与失效的宏观与微观电化学方法。介绍了直流电化学极化、电化学阻抗谱（EIS）、电化学噪声（ENM）等宏观电化学测试方法，此类方法主要反映涂装材料的整体防护特性和老化失效规律；而微区电化学测量方法，如局部电化学阻抗（LEIS）、扫描开尔文探针（SKP）、扫描振动电极（SVET）、扫描电化学显微镜（SECM）和原子力显微镜（AFM）等，主要用于涂层局部或微缺陷的检测，以及界面层物理化学变化规律的研究。简述了应用这些方法所取得的成果，对进一步研究涂层失效具有一定指导意义。
腐蚀失效
电化学测试
防护性能
organic coating
corrosion failure
electrochemical measurement
protective performance
Abstract
The main electrochemical measurement techniques for evaluating the protection and failure of organic coatings in recent years are described. The macroscopic electrochemical measurement techniques including DC electrochemical polarization, electrochemical impedance spectroscopy (EIS), electrochemical noise method (ENM) are introduced which mainly reflect the overall protective performance and aging rule of coatings. And some kinds of localized electrochemical measurement techniques, for instance, local electrochemical impedance spectroscopy (LEIS), scanning Kelvin probe (SKP), scanning vibrating electrode technique (SVET), scanning electrochemical microscopy (SECM) and atomic force microscopy (AFM) are also discussed, these methods are mainly used in detecting coating's local or microscopic defects and researching the rules of the physical and chemical change of interface layer.The research achievements of evaluating organic coating performance by applying these techniques are reviewed, which provide guidance for further study of coating failure.
中图分类号 TG174.4 DOI 10.11973/fsyfh-201709001
所属栏目 专论
基金项目 国家自然科学基金（51371087）
收稿日期 2016/2/29
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: CAI Guangyi,ZHANG Deping,ZHAO Weihang,DONG Zehua. Research Advances of Protective Performance and Failure Evaluation for Organic Coatings[J]. Corrosion & Protection, 2017, 38(9): 657
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】徐永祥,严川伟,高延敏,等. 大气环境中涂层下金属的腐蚀和涂层的失效[J]. 中国腐蚀与防护学报,2002,22(4):58-65.
【2】熊金平,左禹. 有机涂层的电化学检测技术研究进展[J]. 涂料技术与文摘,2007(8):11-13.
【3】陈丽姣,李宁,胡会利,等. 检测涂层防护性能的电化学方法[J]. 涂料工业,2008,38(5):53-57.
【4】郭清泉,陈焕钦. 金属腐蚀与涂层防护[J]. 合成材料老化与应用,2003,32(4):36-39.
【5】孙志华,蔡建平,刘明,等. 金属/有机涂层体系环境失效的电化学研究方法[J]. 装备环境工程,2007,4(4):1-5.
【6】张玉玺. EIS法评价有机涂层耐蚀性能的应用研究进展[J]. 当代化工,2007,36(5):516-534.
【7】张鉴清,曹楚南. 用不可逆电极过程阻抗数学模型处理电化学阻抗谱[J]. 中国腐蚀与防护学报,1993,13(1):27-34.
【8】张鉴清,孙国庆,曹楚南. 评价有机涂层防护性能的EIS数据处理[J]. 腐蚀科学与防护技术,1994,6(4):318-325.
【9】ZHANG J T,HU J M,ZHANG J Q,et al. Studies of impedance models and water transport behaviors of polypropylene coated metals in NaCl solution[J]. Progress in Organic Coatings,2004,49(4):293-301.
【10】张鉴清,曹楚南. Kramers-Kronig转换在阻抗数据分析中的应用——Ⅰ. Kramers-Kronig转换与稳定性分析的关系[J]. 中国腐蚀与防护学报,1991,11(2):105-110.
【11】张鉴清,曹楚南. Kramers-Kronig转换在阻抗数据分析中的应用——Ⅱ. 阻抗数据的可靠性分析[J]. 中国腐蚀与防护学报,1991,11(2):111-118.
【12】BI H,SYKES J. An investigation of cathodic oxygen reduction beneath an intact organic coating on mild steel and its relevance to cathodic disbonding[J]. Progress in Organic Coatings,2015,87:83-87.
【13】ZUO Y,PANG R,LI W,et al. The evaluation of coating performance by the variations of phase angles in middle and high frequency domains of EIS[J]. Corrosion Science,2008,50(12):3322-3328.
【14】HUTTUNEN-SAARIVIRTA E,YUDIN V E,MYAGKOVA L A,et al. Corrosion protection of galvanized steel by polyimide coatings:EIS and SEM investigations[J]. Progress in Organic Coatings,2011,72(3):269-278.
【15】MAHDAVI F,TAN M Y J,FORSYTH M. Electrochemical impedance spectroscopy as a tool to measure cathodic disbondment on coated steel surfaces:capabilities and limitations[J]. Progress in Organic Coatings,2015,88:23-31.
【16】董泽华,郭兴蓬,郑家燊. 电化学噪声的分析方法[J]. 材料保护,2001,34(7):20-23.
【17】张鉴清,张昭,王建明,等. 电化学噪声的分析与应用——Ⅰ. 电化学噪声的分析原理[J]. 中国腐蚀与防护学报,2001,21(5):55-65.
【18】张鉴清,张昭,王建明,等. 电化学噪声的分析与应用——Ⅱ. 电化学噪声的应用[J]. 中国腐蚀与防护学报,2002,22(4):50-57.
【19】罗振华,姚琲,蔡健平,等. 有机涂层性能评价技术研究进展[J]. 腐蚀科学与防护技术,2004,16(5):313-317.
【20】张涛,杨延格,邵亚薇,等. 电化学噪声分析方法的研究进展[J]. 中国腐蚀与防护学报,2014,34(1):1-18.
【21】胡会利,李宁,程瑾宁. 电化学噪声在腐蚀领域中的研究进展[J]. 腐蚀科学与防护技术,2007,27(2):114-118.
【22】MILLS D,PICTON P,MULARCZYK L. Developments in the electrochemical noise method (ENM) to make it more practical for assessment of anti-corrosive coatings[J]. Electrochimica Acta,2014,124:199-205.
【23】ARMAN S Y,RAMEZANZADEH B,FARGHADANI S,et al. Application of the electrochemical noise to investigate the corrosion resistance of an epoxy zinc-rich coating loaded with lamellar aluminum and micaceous iron oxide particles[J]. Corrosion Science,2013,77:118-127.
【24】JAMALI S S,MILLS D J,SYKES J M. Measuring electrochemical noise of a single working electrode for assessing corrosion resistance of polymer coated metals[J]. Progress in Organic Coatings,2014,77(3):733-741.
【25】TAN Y. Sensing localised corrosion by means of electrochemical noise detection and analysis[J]. Sensors and Actuators B:Chemical,2009,139(2):688-698.
【26】龙凤仪,杨燕,王树立,等. 微区电化学测量技术及其在腐蚀中的应用[J]. 腐蚀科学与防护技术,2015,27(2):194-198.
【27】王力伟,李晓刚,杜翠薇,等. 微区电化学测量技术进展及在腐蚀领域的应用[J]. 中国腐蚀与防护学报,2010,30(6):498-503.
【28】卢琳,李晓刚,高瑾. 有机涂层/金属界面腐蚀的微区电化学[J]. 化学进展,2011(8):1618-1626.
【29】王力伟,王新华,卢琳,等. 有机涂层剥离的微区电化学研究进展[J]. 腐蚀与防护,2014(2):158-162.
【30】骆鸿,肖葵,董超芳,等. 金属腐蚀微区电化学研究进展(2)局部电化学阻抗谱[J]. 腐蚀与防护,2009,50(8):511-514.
【31】续冉,王佳. 局部电化学阻抗方法在腐蚀研究中的应用[J]. 中国腐蚀与防护学报,2015,35(4):287-296.
【32】章妮,孙志华,张琦,等. 局部阻抗测试技术在评定有机涂层环境失效中的应用[J]. 装备环境工程,2007,4(1):75-78.
【33】HUANG V M,WU S,ORAZEM M E,et al. Local electrochemical impedance spectroscopy:a review and some recent developments[J]. Electrochimica Acta,2011,56:8048-8057.
【34】LILLARD R S,MORAN P J,ISAACS H S. A novel method for generating quantitative local electrochemical impedance spectroscopy[J]. Electrochemical Society,1992,139(4):1007-1012.
【35】SNIHIROVA D,LIPHARDT L,GRUNDMEIER G,et al. Electrochemical study of the corrosion inhibition ability of "smart" coatings applied on AA2024[J]. Journal of Solid State Electrochemistry,2013,17(8):2183-2192.
【36】ZHANG Y,SHAO Y,MENG G,et al. Evaluation of the corrosion protection of defective polyaniline/epoxy coating by localized electrochemical impedance spectroscopy[J]. Journal of Coatings Technology and Research,2015,12(4):777-785.
【37】高瑾,钱海燕,孙晓华,等. 海水压力对深海用环氧涂层防护性能的影响[J]. 化工学报,2015,66(11):4572-4577.
【38】ZHONG C,TANG X,CHENG Y F. Corrosion of steel under the defected coating studied by localized electrochemical impedance spectroscopy[J]. Electrochimica Acta,2008,53(14):4740-4747.
【39】STRATMANN M,STRECKEL H,KIM K T,et al. The measurement of polarisation curves on metal surfaces which are covered by thin electrolyte layers[J]. Corrosion Science,1990,30(6):715-734.
【40】STRATMANN M. The investigation of the corrosion properties of metals,covered with adsorbed electrolyte layers——a new experimental technique[J]. Corrosion Science,1987,27(8):869-872.
【41】安英辉,董超芳,肖葵,等. Kelvin探针测量技术在电化学研究中的应用进展[J]. 腐蚀科学与防护技术,2008,20(6):440-444.
【42】DE LA FUENTE D,ROHWERDER M. Fundamental investigation on the stability of the steel/coating interfaces contaminated by submicroscopic salt particles[J]. Progress in Organic Coatings,2008,61(2):233-239.
【43】REDDY B,SYKES J M. Degradation of organic coatings in a corrosive environment:a study by scanning Kelvin probe and scanning acoustic microscope[J]. Progress in Organic Coatings,2005,52(4):280-287.
【44】张伟,王佳,赵增元,等. 有机涂层失效过程的电化学阻抗和电位分布响应特征[J]. 高等学校化学学报,2009,30(4):762-766.
【45】李迎超,高瑾,李晓刚,等. 扫描Kelvin探针研究缺陷涂层的膜下腐蚀电化学行为[J]. 北京科技大学学报,2010,32(9):1169-1174.
【46】赵增元,吕伟艳,马永青,等. 扫描Kelvin探针表面电位特征参数在有机涂层劣化研究中的应用[J]. 腐蚀与防护,2014,35(10):1033-1036.
【47】ISAACS H S. The measurement of the galvanic corrosion of soldered copper using the scanning vibrating electrode technique[J]. Corrosion Science,1988,28(6):547-558.
【48】骆鸿,董超芳,肖葵,等. 金属腐蚀微区电化学研究进展(3)扫描振动电极技术[J]. 腐蚀与防护,2009,30(9):631-635.
【49】续冉,王佳,王燕华. 扫描振动电极技术在腐蚀研究中的应用[J]. 腐蚀科学与防护技术,2015,27(4):375-381.
【50】KAMARAJ K,DEVARAPALLI R,SIVA T,et al. Self-healing electrosynthesied polyaniline film as primer coat for AA 2024-T3[J]. Materials Chemistry and Physics,2015,153:256-265.
【51】TIAN Z,SHI H,LIU F,et al. Inhibiting effect of 8-hydroxyquinoline on the corrosion of silane-based sol-gel coatings on AA 2024-T3[J]. Progress in Organic Coatings,2015,82:81-90.
【52】MONTEMOR M F,SNIHIROVA D V,TARYBA M G,et al. Evaluation of self-healing ability in protective coatings modified with combinations of layered double hydroxides and cerium molibdate nanocontainers filled with corrosion inhibitors[J]. Electrochimica Acta,2012,60:31-40.
【53】GNEDENKOV A S,SINEBRYUKHOV S L,MASHTALYAR D V,et al. Localized corrosion of the Mg alloys with inhibitor-containing coatings:SVET and SIET studies[J]. Corrosion Science,2016,102:269-278.
【54】BORISOVA D,MÖHWALD H,SHCHUKIN D G. Influence of embedded nanocontainers on the efficiency of active anticorrosive coatings for aluminum alloys part I:influence of nanocontainer concentration[J]. ACS Applied Materials & Interfaces,2012,4(6):2931-2939.
【55】BORISOVA D,MOHWALD H,SHCHUKIN D G. Mesoporous silica nanoparticles for active corrosion protection[J]. ACS Nano,2011,5(3):1939-1946.
【56】BARD A J,FAN F R F,KWAK J,et al. Scanning electrochemical microscopy. Introduction and principles[J]. Analytical Chemistry,1989,61(2):132-138.
【57】BARD A J,FAN F R,PIERCE D T,et al. Chemical imaging of surfaces with the scanning electrochemical microscope[J]. Science,1991,254(5028):68-74.
【58】曹发和,夏妍,刘文娟,等. SECM基本原理及其在金属腐蚀中的应用[J]. 电化学,2013,19(5):393-401.
【59】尹其和. 扫描电化学显微镜的基本原理与应用[J]. 中山大学研究生学刊(自然科学·医学版),2011,32(2):46-60.
【60】GONZALEZ-GARCIA Y,SANTANA J J,GONZALEZ-GUZMAN J,et al. Scanning electrochemical microscopy for the investigation of localized degradation processes in coated metals[J]. Progress in Organic Coatings,2010,69(2):110-117.
【61】SOUTO R M,GONZALEZ-GARCIA Y,GONZALEZ S. Characterization of coating systems by scanning electrochemical microscopy:surface topology and blistering[J]. Progress in Organic Coatings,2009,65(4):435-439.
【62】SOUTO R M,GONZALEZ-GARCL A Y,GONZALEZ S,et al. Damage to paint coatings caused by electrolyte immersion as observed in situ by scanning electrochemical microscopy[J]. Corrosion Science,2004,46(11):2621-2628.
【63】BASTOS A C,SIMOES A M,GONZALEZ S,et al. Application of the scanning electrochemical microscope to the examination of organic coatings on metallic substrates[J]. Progress in Organic Coatings,2005,53(3):177-182.
【64】GONZ LEZ S,SANTANA J J,GONZ LEZ-GARC A Y,et al. Scanning electrochemical microscopy for the investigation of localized degradation processes in coated metals:effect of oxygen[J]. Corrosion Science,2011,53(5):1910-1915.
【65】SANTANA J J,PAHLER M,SOUTO R M,et al. Direct evidence of early blister formation in polymer-coated metals from exposure to chloride-containing electrolytes by alternating-current scanning electrochemical microscopy[J]. Electrochimica Acta,2012,77:60-64.
【66】姜洪霞,高瑾,钱海燕,等. 纳米TiO2对丙烯酸酯聚氨酯涂层/碳钢界面的初期失效行为的影响[J]. 工程科学学报,2015,37(8):1029-1035.
【67】LI J,ECCO L,FEDAL M,et al. In-situ AFM and EIS study of a solventborne alkyd coating with nanoclay for corrosion protection of carbon steel[J]. Progress in Organic Coatings,2015,87:179-188.
【68】GOLRU S S,ATTAR M M,RAMEZANZADEH B. Effects of surface treatment of aluminium alloy 1050 on the adhesion and anticorrosion properties of the epoxy coating[J]. Applied Surface Science,2015,345:360-368.
【2】熊金平,左禹. 有机涂层的电化学检测技术研究进展[J]. 涂料技术与文摘,2007(8):11-13.
【3】陈丽姣,李宁,胡会利,等. 检测涂层防护性能的电化学方法[J]. 涂料工业,2008,38(5):53-57.
【4】郭清泉,陈焕钦. 金属腐蚀与涂层防护[J]. 合成材料老化与应用,2003,32(4):36-39.
【5】孙志华,蔡建平,刘明,等. 金属/有机涂层体系环境失效的电化学研究方法[J]. 装备环境工程,2007,4(4):1-5.
【6】张玉玺. EIS法评价有机涂层耐蚀性能的应用研究进展[J]. 当代化工,2007,36(5):516-534.
【7】张鉴清,曹楚南. 用不可逆电极过程阻抗数学模型处理电化学阻抗谱[J]. 中国腐蚀与防护学报,1993,13(1):27-34.
【8】张鉴清,孙国庆,曹楚南. 评价有机涂层防护性能的EIS数据处理[J]. 腐蚀科学与防护技术,1994,6(4):318-325.
【9】ZHANG J T,HU J M,ZHANG J Q,et al. Studies of impedance models and water transport behaviors of polypropylene coated metals in NaCl solution[J]. Progress in Organic Coatings,2004,49(4):293-301.
【10】张鉴清,曹楚南. Kramers-Kronig转换在阻抗数据分析中的应用——Ⅰ. Kramers-Kronig转换与稳定性分析的关系[J]. 中国腐蚀与防护学报,1991,11(2):105-110.
【11】张鉴清,曹楚南. Kramers-Kronig转换在阻抗数据分析中的应用——Ⅱ. 阻抗数据的可靠性分析[J]. 中国腐蚀与防护学报,1991,11(2):111-118.
【12】BI H,SYKES J. An investigation of cathodic oxygen reduction beneath an intact organic coating on mild steel and its relevance to cathodic disbonding[J]. Progress in Organic Coatings,2015,87:83-87.
【13】ZUO Y,PANG R,LI W,et al. The evaluation of coating performance by the variations of phase angles in middle and high frequency domains of EIS[J]. Corrosion Science,2008,50(12):3322-3328.
【14】HUTTUNEN-SAARIVIRTA E,YUDIN V E,MYAGKOVA L A,et al. Corrosion protection of galvanized steel by polyimide coatings:EIS and SEM investigations[J]. Progress in Organic Coatings,2011,72(3):269-278.
【15】MAHDAVI F,TAN M Y J,FORSYTH M. Electrochemical impedance spectroscopy as a tool to measure cathodic disbondment on coated steel surfaces:capabilities and limitations[J]. Progress in Organic Coatings,2015,88:23-31.
【16】董泽华,郭兴蓬,郑家燊. 电化学噪声的分析方法[J]. 材料保护,2001,34(7):20-23.
【17】张鉴清,张昭,王建明,等. 电化学噪声的分析与应用——Ⅰ. 电化学噪声的分析原理[J]. 中国腐蚀与防护学报,2001,21(5):55-65.
【18】张鉴清,张昭,王建明,等. 电化学噪声的分析与应用——Ⅱ. 电化学噪声的应用[J]. 中国腐蚀与防护学报,2002,22(4):50-57.
【19】罗振华,姚琲,蔡健平,等. 有机涂层性能评价技术研究进展[J]. 腐蚀科学与防护技术,2004,16(5):313-317.
【20】张涛,杨延格,邵亚薇,等. 电化学噪声分析方法的研究进展[J]. 中国腐蚀与防护学报,2014,34(1):1-18.
【21】胡会利,李宁,程瑾宁. 电化学噪声在腐蚀领域中的研究进展[J]. 腐蚀科学与防护技术,2007,27(2):114-118.
【22】MILLS D,PICTON P,MULARCZYK L. Developments in the electrochemical noise method (ENM) to make it more practical for assessment of anti-corrosive coatings[J]. Electrochimica Acta,2014,124:199-205.
【23】ARMAN S Y,RAMEZANZADEH B,FARGHADANI S,et al. Application of the electrochemical noise to investigate the corrosion resistance of an epoxy zinc-rich coating loaded with lamellar aluminum and micaceous iron oxide particles[J]. Corrosion Science,2013,77:118-127.
【24】JAMALI S S,MILLS D J,SYKES J M. Measuring electrochemical noise of a single working electrode for assessing corrosion resistance of polymer coated metals[J]. Progress in Organic Coatings,2014,77(3):733-741.
【25】TAN Y. Sensing localised corrosion by means of electrochemical noise detection and analysis[J]. Sensors and Actuators B:Chemical,2009,139(2):688-698.
【26】龙凤仪,杨燕,王树立,等. 微区电化学测量技术及其在腐蚀中的应用[J]. 腐蚀科学与防护技术,2015,27(2):194-198.
【27】王力伟,李晓刚,杜翠薇,等. 微区电化学测量技术进展及在腐蚀领域的应用[J]. 中国腐蚀与防护学报,2010,30(6):498-503.
【28】卢琳,李晓刚,高瑾. 有机涂层/金属界面腐蚀的微区电化学[J]. 化学进展,2011(8):1618-1626.
【29】王力伟,王新华,卢琳,等. 有机涂层剥离的微区电化学研究进展[J]. 腐蚀与防护,2014(2):158-162.
【30】骆鸿,肖葵,董超芳,等. 金属腐蚀微区电化学研究进展(2)局部电化学阻抗谱[J]. 腐蚀与防护,2009,50(8):511-514.
【31】续冉,王佳. 局部电化学阻抗方法在腐蚀研究中的应用[J]. 中国腐蚀与防护学报,2015,35(4):287-296.
【32】章妮,孙志华,张琦,等. 局部阻抗测试技术在评定有机涂层环境失效中的应用[J]. 装备环境工程,2007,4(1):75-78.
【33】HUANG V M,WU S,ORAZEM M E,et al. Local electrochemical impedance spectroscopy:a review and some recent developments[J]. Electrochimica Acta,2011,56:8048-8057.
【34】LILLARD R S,MORAN P J,ISAACS H S. A novel method for generating quantitative local electrochemical impedance spectroscopy[J]. Electrochemical Society,1992,139(4):1007-1012.
【35】SNIHIROVA D,LIPHARDT L,GRUNDMEIER G,et al. Electrochemical study of the corrosion inhibition ability of "smart" coatings applied on AA2024[J]. Journal of Solid State Electrochemistry,2013,17(8):2183-2192.
【36】ZHANG Y,SHAO Y,MENG G,et al. Evaluation of the corrosion protection of defective polyaniline/epoxy coating by localized electrochemical impedance spectroscopy[J]. Journal of Coatings Technology and Research,2015,12(4):777-785.
【37】高瑾,钱海燕,孙晓华,等. 海水压力对深海用环氧涂层防护性能的影响[J]. 化工学报,2015,66(11):4572-4577.
【38】ZHONG C,TANG X,CHENG Y F. Corrosion of steel under the defected coating studied by localized electrochemical impedance spectroscopy[J]. Electrochimica Acta,2008,53(14):4740-4747.
【39】STRATMANN M,STRECKEL H,KIM K T,et al. The measurement of polarisation curves on metal surfaces which are covered by thin electrolyte layers[J]. Corrosion Science,1990,30(6):715-734.
【40】STRATMANN M. The investigation of the corrosion properties of metals,covered with adsorbed electrolyte layers——a new experimental technique[J]. Corrosion Science,1987,27(8):869-872.
【41】安英辉,董超芳,肖葵,等. Kelvin探针测量技术在电化学研究中的应用进展[J]. 腐蚀科学与防护技术,2008,20(6):440-444.
【42】DE LA FUENTE D,ROHWERDER M. Fundamental investigation on the stability of the steel/coating interfaces contaminated by submicroscopic salt particles[J]. Progress in Organic Coatings,2008,61(2):233-239.
【43】REDDY B,SYKES J M. Degradation of organic coatings in a corrosive environment:a study by scanning Kelvin probe and scanning acoustic microscope[J]. Progress in Organic Coatings,2005,52(4):280-287.
【44】张伟,王佳,赵增元,等. 有机涂层失效过程的电化学阻抗和电位分布响应特征[J]. 高等学校化学学报,2009,30(4):762-766.
【45】李迎超,高瑾,李晓刚,等. 扫描Kelvin探针研究缺陷涂层的膜下腐蚀电化学行为[J]. 北京科技大学学报,2010,32(9):1169-1174.
【46】赵增元,吕伟艳,马永青,等. 扫描Kelvin探针表面电位特征参数在有机涂层劣化研究中的应用[J]. 腐蚀与防护,2014,35(10):1033-1036.
【47】ISAACS H S. The measurement of the galvanic corrosion of soldered copper using the scanning vibrating electrode technique[J]. Corrosion Science,1988,28(6):547-558.
【48】骆鸿,董超芳,肖葵,等. 金属腐蚀微区电化学研究进展(3)扫描振动电极技术[J]. 腐蚀与防护,2009,30(9):631-635.
【49】续冉,王佳,王燕华. 扫描振动电极技术在腐蚀研究中的应用[J]. 腐蚀科学与防护技术,2015,27(4):375-381.
【50】KAMARAJ K,DEVARAPALLI R,SIVA T,et al. Self-healing electrosynthesied polyaniline film as primer coat for AA 2024-T3[J]. Materials Chemistry and Physics,2015,153:256-265.
【51】TIAN Z,SHI H,LIU F,et al. Inhibiting effect of 8-hydroxyquinoline on the corrosion of silane-based sol-gel coatings on AA 2024-T3[J]. Progress in Organic Coatings,2015,82:81-90.
【52】MONTEMOR M F,SNIHIROVA D V,TARYBA M G,et al. Evaluation of self-healing ability in protective coatings modified with combinations of layered double hydroxides and cerium molibdate nanocontainers filled with corrosion inhibitors[J]. Electrochimica Acta,2012,60:31-40.
【53】GNEDENKOV A S,SINEBRYUKHOV S L,MASHTALYAR D V,et al. Localized corrosion of the Mg alloys with inhibitor-containing coatings:SVET and SIET studies[J]. Corrosion Science,2016,102:269-278.
【54】BORISOVA D,MÖHWALD H,SHCHUKIN D G. Influence of embedded nanocontainers on the efficiency of active anticorrosive coatings for aluminum alloys part I:influence of nanocontainer concentration[J]. ACS Applied Materials & Interfaces,2012,4(6):2931-2939.
【55】BORISOVA D,MOHWALD H,SHCHUKIN D G. Mesoporous silica nanoparticles for active corrosion protection[J]. ACS Nano,2011,5(3):1939-1946.
【56】BARD A J,FAN F R F,KWAK J,et al. Scanning electrochemical microscopy. Introduction and principles[J]. Analytical Chemistry,1989,61(2):132-138.
【57】BARD A J,FAN F R,PIERCE D T,et al. Chemical imaging of surfaces with the scanning electrochemical microscope[J]. Science,1991,254(5028):68-74.
【58】曹发和,夏妍,刘文娟,等. SECM基本原理及其在金属腐蚀中的应用[J]. 电化学,2013,19(5):393-401.
【59】尹其和. 扫描电化学显微镜的基本原理与应用[J]. 中山大学研究生学刊(自然科学·医学版),2011,32(2):46-60.
【60】GONZALEZ-GARCIA Y,SANTANA J J,GONZALEZ-GUZMAN J,et al. Scanning electrochemical microscopy for the investigation of localized degradation processes in coated metals[J]. Progress in Organic Coatings,2010,69(2):110-117.
【61】SOUTO R M,GONZALEZ-GARCIA Y,GONZALEZ S. Characterization of coating systems by scanning electrochemical microscopy:surface topology and blistering[J]. Progress in Organic Coatings,2009,65(4):435-439.
【62】SOUTO R M,GONZALEZ-GARCL A Y,GONZALEZ S,et al. Damage to paint coatings caused by electrolyte immersion as observed in situ by scanning electrochemical microscopy[J]. Corrosion Science,2004,46(11):2621-2628.
【63】BASTOS A C,SIMOES A M,GONZALEZ S,et al. Application of the scanning electrochemical microscope to the examination of organic coatings on metallic substrates[J]. Progress in Organic Coatings,2005,53(3):177-182.
【64】GONZ LEZ S,SANTANA J J,GONZ LEZ-GARC A Y,et al. Scanning electrochemical microscopy for the investigation of localized degradation processes in coated metals:effect of oxygen[J]. Corrosion Science,2011,53(5):1910-1915.
【65】SANTANA J J,PAHLER M,SOUTO R M,et al. Direct evidence of early blister formation in polymer-coated metals from exposure to chloride-containing electrolytes by alternating-current scanning electrochemical microscopy[J]. Electrochimica Acta,2012,77:60-64.
【66】姜洪霞,高瑾,钱海燕,等. 纳米TiO2对丙烯酸酯聚氨酯涂层/碳钢界面的初期失效行为的影响[J]. 工程科学学报,2015,37(8):1029-1035.
【67】LI J,ECCO L,FEDAL M,et al. In-situ AFM and EIS study of a solventborne alkyd coating with nanoclay for corrosion protection of carbon steel[J]. Progress in Organic Coatings,2015,87:179-188.
【68】GOLRU S S,ATTAR M M,RAMEZANZADEH B. Effects of surface treatment of aluminium alloy 1050 on the adhesion and anticorrosion properties of the epoxy coating[J]. Applied Surface Science,2015,345:360-368.
相关信息