耐蚀钢筋研究现状及腐蚀评价方法分析
Recent Status of Research on Corrosion Resistant Steel Bars and Analysis on Existing Corrosion Evaluation Methods
摘 要
在海洋环境中，钢筋锈蚀是导致混凝土失效的主要原因，提高钢筋耐蚀性是提高海洋环境中混凝土耐久性的根本。总结了近年来国内外耐蚀钢筋的种类及耐蚀钢筋的研究现状，并对混凝土中钢筋常用的物理检测方法和电化学检测方法进行了总结。评价了目前国内外常见的用于评价钢筋耐蚀性的方法的特点。
耐蚀钢筋
电化学方法
物理检测
加速腐蚀方法
reinforced concrete
corrosion resistant steel bar
electrochemical method
physical testing
accelerated corrosion test
Abstract
Steel bar corrosion is the main cause of the failure of concrete in marine environment, and the improvement of corrosion resistance of steel bars is the best method to inprove the durability of concrete in marine environment. The recent status and existing problems of research on the corrosion resistant steel bars are reviewed in this paper. The physical testing methods and electrochemical testing methods of steel bars in concrete are summarized. The characteristics of rapid corrosion evaluation methods of reinforced steel bars existing at home and abroad are analyzed.
中图分类号 TG172 DOI 10.11973/fsyfh-201709002
所属栏目 专论
基金项目 国家重点基础研究发展计划（2014CB643300）
收稿日期 2016/1/5
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHOU Hehe,ZHAO Jinbin,CAI Jiaxing,LIU Ming,CHENG Xuequn. Recent Status of Research on Corrosion Resistant Steel Bars and Analysis on Existing Corrosion Evaluation Methods[J]. Corrosion & Protection, 2017, 38(9): 665
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】MAHDI V,MOHAMMAD S,POURIA G. Comparative studies of experimental and numerical techniques in measurement of corrosion rate and time-to-corrosion-initiation of rebar in concrete in marine environments[J]. Cement and Concrete Composites,2014,48:98-107.
【2】任晓云,李建三,管松,等. 桥梁的腐蚀与防护[J]. 合肥工业大学学报(自然科学版),2002,25(z1):957-961.
【3】葛燕,朱锡昶,李岩. 桥梁钢筋混凝土结构防腐蚀[M]. 北京:化学工业出版社,2011.
【4】洪乃丰. 防冰盐腐蚀与钢筋混凝土的耐久性[J]. 建筑技术,2000,31(2):102-104.
【5】左国望. 氯离子侵蚀环境下混凝土裂缝与钢筋锈蚀关系研究[D]. 武汉:湖北工业大学,2015.
【6】程学群,刘明,金柱,等. 严酷海洋环境耐蚀钢筋的腐蚀规律及混凝土耐久性预测[C]//2014海洋材料腐蚀与防护大会.[出版地不详]:[出版者不详],2014.
【7】MOETAZ M E,ALI A J. Durability assessment of epoxy modified concrete[J]. Construction and Building Materials,2010,24(8):1523-1528.
【8】张国学,吴苗苗. 不锈钢钢筋混凝土的应用及发展[J]. 佛山科学技术学院学报(自然科学版),2006,24(2):10-13.
【9】许贤敏. 国外不锈钢筋的研究动态[J]. 山东建材,2000(5):29-32.
【10】RICARDO R,DE R. New developments in steel protection from corrosion[J]. Massachusetts institute of technology,2001.
【11】AKHOONDAN M,SAGVÉS A A. Cathodic behavior of 9% Cr steel reinforcement in concrete[J]. Corrosion,2011:11010-1.
【12】张彦文. 合金化镀锌板镀层抗粉化性能及相关工艺研究[D]. 武汉:武汉理工大学,2012.
【13】陈贞萍. 钢筋表面锌铝镀层及其与环氧树脂粘附性研究[D]. 广州:华南理工大学,2014.
【14】顾宝珊,汪兵,纪晓春,等. JT245经济型耐候钢锈层的电化学研究[J]. 钢铁研究学报,2005,17(5):62-65.
【15】张学元,杜元龙,史志明. 钢筋混凝土腐蚀与防护的技术发展动态[J]. 腐蚀与护,1999,20(1):9-12.
【16】王钧. 耐腐蚀钢筋的成分优化及耐蚀机理的研究[D]. 济南:山东大学,2004.
【17】郭湛,完卫国,孙维,等. 含稀土高强度耐腐蚀钢筋的研究[J]. 钢铁,2010,45(12):53-58.
【18】LIU M,CHENG X,LI X,et al. Corrosion behavior of Cr modified HRB400 steel rebar in simulated concrete pore solution[J]. Construction & Building Materials,2015,93:884-890.
【19】ASTM C876-91(Reproved 1999). Standard test method for half-cell potentials of uncoated reinforcing steel in concrete[S].
【20】GLASS G K,PAGE C L,SHORT N R. Factors affecting the corrosion rate of steel in carbonated mortars[J]. Corrosion Science,1991,32(12):1283-1294.
【21】许晨,李志远,金伟良. 混凝土中钢筋锈蚀的电化学阻抗谱特征研究[J]. 腐蚀科学与防护技术,2011,23(5):393-398.
【22】ROB B P. Test methods for on site measurement of resistivity of concrete-a RILEM TC-154 technical recommendation[J]. Construction and Building Materials,200(15):125-131.
【23】文邦伟,张伦武,李继红,等. 装甲钢自然环境试验与人工加速试验的相关性[J]. 装备环境工程,2006,3(3):97-101.
【24】DARWIN D,OREILLY M E,BROWNING J A,et al. Multiple corrosion protection systems for reinforced concrete bridge components:laboratory and field tests[C]//2010 Concrete Bridge Conference:Achieving Safe,Smart & Sustainable Bridges.[S.l.]:[s.n.],2010.
【25】巴恒静,张猛. 混凝土中钢筋锈蚀的氯离子临界浓度的研究[C]//第八届全国混凝土耐久性学术交流会.[出版地不详]:[出版者不详],2012.
【26】翟之阳. 混凝土中临界氯离子浓度的试验研究[D]. 上海:上海交通大学,2008.
【27】侯保荣. 海洋钢筋混凝土腐蚀与修复补强技术[M]. 北京:科学出版社,2012.
【2】任晓云,李建三,管松,等. 桥梁的腐蚀与防护[J]. 合肥工业大学学报(自然科学版),2002,25(z1):957-961.
【3】葛燕,朱锡昶,李岩. 桥梁钢筋混凝土结构防腐蚀[M]. 北京:化学工业出版社,2011.
【4】洪乃丰. 防冰盐腐蚀与钢筋混凝土的耐久性[J]. 建筑技术,2000,31(2):102-104.
【5】左国望. 氯离子侵蚀环境下混凝土裂缝与钢筋锈蚀关系研究[D]. 武汉:湖北工业大学,2015.
【6】程学群,刘明,金柱,等. 严酷海洋环境耐蚀钢筋的腐蚀规律及混凝土耐久性预测[C]//2014海洋材料腐蚀与防护大会.[出版地不详]:[出版者不详],2014.
【7】MOETAZ M E,ALI A J. Durability assessment of epoxy modified concrete[J]. Construction and Building Materials,2010,24(8):1523-1528.
【8】张国学,吴苗苗. 不锈钢钢筋混凝土的应用及发展[J]. 佛山科学技术学院学报(自然科学版),2006,24(2):10-13.
【9】许贤敏. 国外不锈钢筋的研究动态[J]. 山东建材,2000(5):29-32.
【10】RICARDO R,DE R. New developments in steel protection from corrosion[J]. Massachusetts institute of technology,2001.
【11】AKHOONDAN M,SAGVÉS A A. Cathodic behavior of 9% Cr steel reinforcement in concrete[J]. Corrosion,2011:11010-1.
【12】张彦文. 合金化镀锌板镀层抗粉化性能及相关工艺研究[D]. 武汉:武汉理工大学,2012.
【13】陈贞萍. 钢筋表面锌铝镀层及其与环氧树脂粘附性研究[D]. 广州:华南理工大学,2014.
【14】顾宝珊,汪兵,纪晓春,等. JT245经济型耐候钢锈层的电化学研究[J]. 钢铁研究学报,2005,17(5):62-65.
【15】张学元,杜元龙,史志明. 钢筋混凝土腐蚀与防护的技术发展动态[J]. 腐蚀与护,1999,20(1):9-12.
【16】王钧. 耐腐蚀钢筋的成分优化及耐蚀机理的研究[D]. 济南:山东大学,2004.
【17】郭湛,完卫国,孙维,等. 含稀土高强度耐腐蚀钢筋的研究[J]. 钢铁,2010,45(12):53-58.
【18】LIU M,CHENG X,LI X,et al. Corrosion behavior of Cr modified HRB400 steel rebar in simulated concrete pore solution[J]. Construction & Building Materials,2015,93:884-890.
【19】ASTM C876-91(Reproved 1999). Standard test method for half-cell potentials of uncoated reinforcing steel in concrete[S].
【20】GLASS G K,PAGE C L,SHORT N R. Factors affecting the corrosion rate of steel in carbonated mortars[J]. Corrosion Science,1991,32(12):1283-1294.
【21】许晨,李志远,金伟良. 混凝土中钢筋锈蚀的电化学阻抗谱特征研究[J]. 腐蚀科学与防护技术,2011,23(5):393-398.
【22】ROB B P. Test methods for on site measurement of resistivity of concrete-a RILEM TC-154 technical recommendation[J]. Construction and Building Materials,200(15):125-131.
【23】文邦伟,张伦武,李继红,等. 装甲钢自然环境试验与人工加速试验的相关性[J]. 装备环境工程,2006,3(3):97-101.
【24】DARWIN D,OREILLY M E,BROWNING J A,et al. Multiple corrosion protection systems for reinforced concrete bridge components:laboratory and field tests[C]//2010 Concrete Bridge Conference:Achieving Safe,Smart & Sustainable Bridges.[S.l.]:[s.n.],2010.
【25】巴恒静,张猛. 混凝土中钢筋锈蚀的氯离子临界浓度的研究[C]//第八届全国混凝土耐久性学术交流会.[出版地不详]:[出版者不详],2012.
【26】翟之阳. 混凝土中临界氯离子浓度的试验研究[D]. 上海:上海交通大学,2008.
【27】侯保荣. 海洋钢筋混凝土腐蚀与修复补强技术[M]. 北京:科学出版社,2012.
相关信息