一种新型中央空调绿色水处理剂的性能
Performance of a Newly Green Water Treatment Agent for Central Air Conditioner
摘 要
采用静态阻垢法和旋转挂片法通过筛选得到了一种适宜中央空调循环冷却水处理的绿色复合型水处理剂。利用扫描电镜对形成的垢样进行形貌观察，采用电化学方法分析了复合药剂的缓蚀机理。结果表明：当PESA、PAAS、BTA、SDBS的复配质量比为8：2：5：25时，复合药剂的阻垢缓蚀效果最佳，最佳加药量为80 mg/L，此时，复合药剂的阻垢率大于90%，对A3碳钢和T2紫铜的缓蚀率分别达到91.13%、88.61%。
复合型水处理剂
阻垢
缓蚀
绿色环保
central air conditioner
compound water treatment agent
scale inhibition
corrosion inhibition
environmentally friendly
Abstract
Static scale inhibition method and rotary coupon tests were used to obtain a kind of green agent, which is suitable for central air conditioner circulating cooling water treatment. Scanning electron microscopy (SEM) was used to observe the morphology of the scale samples, and electrochemical method was used to analyze the corrosion inhibition mechanism of the compound agent. Results show that the best ratio of the compound (PESA, PAAS, BTA, SDBS) was 8:2:5:25, and the optimal dosage was 80 mg/L. At this proportion, the scale inhibition rate was more than 90%, while the corrosion inhibition rate of A3 carbon steel and T2 red copper reached 91.13% and 88.61%, respectively.
中图分类号 TQ085+.412 DOI 10.11973/fsyfh-201709013
所属栏目 应用技术
基金项目
收稿日期 2016/2/25
修改稿日期
网络出版日期
作者单位点击查看
联系人作者朱志平(zzp8389@163.com)
引用该论文: LI Maodong,DAI Chenlin,QIAO Yue,YANG Bo,ZHU Zhiping. Performance of a Newly Green Water Treatment Agent for Central Air Conditioner[J]. Corrosion & Protection, 2017, 38(9): 721
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】文强,王延生. 中央空调系统水处理技术浅论[J]. 清洗世界,2005,21(5):26-30.
【2】闫美芳,刘振法,董倩倩,等. 多功能环保型缓蚀阻垢剂的研制及性能研究[J]. 工业水处理,2011,31(7):64-66,70.
【3】BARAKA-LOKMANES,SORBIE K,POISSON N,et al. Can green scale inhibitors replace phosphonate scale inhibitors:carbonate coreflooding experi-ments[J]. Petroleum Science and Technology,2009,27(4):427-441.
【4】SRISUWAN N,OCHOA N,PÉBRE N,et al. Variation of carbon steel corrosion rate with flow conditions in the presence of an inhibitive formulation[J]. Corrosion Science,2008,50(5):1245-1250.
【5】樊荣,黄南哲. 中央空调冷却水系统铜材设备的腐蚀控制[J]. 工业水处理,2005,25(10):67-70.
【6】宁守庆,张洪涛. 中央空调循环冷却水处理的研究[J]. 中国科技信息,2012(1):105-106.
【7】王俊锋,董继先,郭睿. 一种复合型水处理阻垢缓蚀剂[J]. 腐蚀与防护,2010,31(2):164-166.
【8】GB 16632-2008水处理剂阻垢性能的测定碳酸钙沉积法[S].
【9】GB 18175-2000水处理剂缓蚀性能的测定旋转挂片法[S].
【10】TOUIR R,CENOUI M,EL BAKRI M,et al. Sodium gluconate as corrosion and scale inhibitor of ordinary steel in simulated cooling water[J]. Corrosion Science,2008,50(6):1530-1537.
【11】ÁLVAREZ-BUSTAMANTE R,NEGRÓN-SILVA G,ABREU-QUIJANO M,et al. Electrochemical study of 2-mercaptoimidazole as a novel corrosion inhibitor for steels[J]. Electrochimica Acta,2009,54(23):5393-5399.
【12】张慧鑫,包伯荣,葛红花,等. 一种低磷阻垢缓蚀剂的缓蚀性能[J]. 腐蚀与防护,2006,27(12):611-613,619.
【13】雷武,王风云,夏明珠,等. 绿色阻垢剂聚环氧琥珀酸的合成与阻垢机理初探[J]. 化工学报,2006,57(9):2207-2213.
【14】胡丹. 环保型无磷缓蚀阻垢剂的研制及缓蚀阻垢机理研究[D]. 武汉:武汉理工大学,2012.
【15】夏笑虹. 聚丙烯酸钠的阻垢、缓蚀机理研究[D]. 长沙:湖南大学,2001.
【16】郑兴文,曾宪光,龚敏,等. 环保型无磷缓蚀阻垢剂的制备[J]. 腐蚀与防护,2012(5):381-384.
【17】张景玲. 苯并三氮唑复配体系对铜的协同缓蚀性能的研究[D]. 长沙:湖南大学,2011.
【18】尹正子,康永. 苯并三氮唑复配缓蚀剂对铜缓蚀机理[J]. 清洗世界,2013,29(6):24-27.
【19】BELAKHMIMA R A,DKHIRECHE N,TOUIR R,et al. Development of a multi-component SG with CTAB as corrosion,scale,and microorganism inhibitor for cooling water systems[J]. Materials Chemistry and Physics,2015,152:85-94.
【20】张亚利,孙典亭,郭国霖,等. 电化学交流阻抗复数平面图和电容复数平面图上相似图形的等效电路变换规则(Ⅱ)——含有Warburg阻抗的等效电路的变换[J]. 高等学校化学学报,2000,21(7):1086-1092.
【2】闫美芳,刘振法,董倩倩,等. 多功能环保型缓蚀阻垢剂的研制及性能研究[J]. 工业水处理,2011,31(7):64-66,70.
【3】BARAKA-LOKMANES,SORBIE K,POISSON N,et al. Can green scale inhibitors replace phosphonate scale inhibitors:carbonate coreflooding experi-ments[J]. Petroleum Science and Technology,2009,27(4):427-441.
【4】SRISUWAN N,OCHOA N,PÉBRE N,et al. Variation of carbon steel corrosion rate with flow conditions in the presence of an inhibitive formulation[J]. Corrosion Science,2008,50(5):1245-1250.
【5】樊荣,黄南哲. 中央空调冷却水系统铜材设备的腐蚀控制[J]. 工业水处理,2005,25(10):67-70.
【6】宁守庆,张洪涛. 中央空调循环冷却水处理的研究[J]. 中国科技信息,2012(1):105-106.
【7】王俊锋,董继先,郭睿. 一种复合型水处理阻垢缓蚀剂[J]. 腐蚀与防护,2010,31(2):164-166.
【8】GB 16632-2008水处理剂阻垢性能的测定碳酸钙沉积法[S].
【9】GB 18175-2000水处理剂缓蚀性能的测定旋转挂片法[S].
【10】TOUIR R,CENOUI M,EL BAKRI M,et al. Sodium gluconate as corrosion and scale inhibitor of ordinary steel in simulated cooling water[J]. Corrosion Science,2008,50(6):1530-1537.
【11】ÁLVAREZ-BUSTAMANTE R,NEGRÓN-SILVA G,ABREU-QUIJANO M,et al. Electrochemical study of 2-mercaptoimidazole as a novel corrosion inhibitor for steels[J]. Electrochimica Acta,2009,54(23):5393-5399.
【12】张慧鑫,包伯荣,葛红花,等. 一种低磷阻垢缓蚀剂的缓蚀性能[J]. 腐蚀与防护,2006,27(12):611-613,619.
【13】雷武,王风云,夏明珠,等. 绿色阻垢剂聚环氧琥珀酸的合成与阻垢机理初探[J]. 化工学报,2006,57(9):2207-2213.
【14】胡丹. 环保型无磷缓蚀阻垢剂的研制及缓蚀阻垢机理研究[D]. 武汉:武汉理工大学,2012.
【15】夏笑虹. 聚丙烯酸钠的阻垢、缓蚀机理研究[D]. 长沙:湖南大学,2001.
【16】郑兴文,曾宪光,龚敏,等. 环保型无磷缓蚀阻垢剂的制备[J]. 腐蚀与防护,2012(5):381-384.
【17】张景玲. 苯并三氮唑复配体系对铜的协同缓蚀性能的研究[D]. 长沙:湖南大学,2011.
【18】尹正子,康永. 苯并三氮唑复配缓蚀剂对铜缓蚀机理[J]. 清洗世界,2013,29(6):24-27.
【19】BELAKHMIMA R A,DKHIRECHE N,TOUIR R,et al. Development of a multi-component SG with CTAB as corrosion,scale,and microorganism inhibitor for cooling water systems[J]. Materials Chemistry and Physics,2015,152:85-94.
【20】张亚利,孙典亭,郭国霖,等. 电化学交流阻抗复数平面图和电容复数平面图上相似图形的等效电路变换规则(Ⅱ)——含有Warburg阻抗的等效电路的变换[J]. 高等学校化学学报,2000,21(7):1086-1092.
相关信息