Effect of Mn Element on Properties of Copper-Based CuZnNi Alloy Brazing Filler
摘 要
通过在CuZnNi合金钎料中添加不同含量的锰元素,研究了锰元素对CuZnNi合金钎料的液相线温度、润湿性能和钎料与接头力学性能的影响。结果表明:随着钎料中锰含量的增加,钎料的液相线温度逐渐降低,当锰的质量分数为4.5%时,钎料的液相线温度下降了54 ℃;钎料的铺展面积随钎料中锰含量的增加而逐渐增大,当锰的质量分数为4.5%时,钎料的铺展面积达到了298 mm2;随着钎料中锰含量的增加,钎料的抗拉强度逐渐增大,而伸长率呈先上升后略下降的趋势;钎焊接头的抗剪强度随钎料中锰含量的增加而显著提高,当锰的质量分数为4.5%时,抗剪强度达到了221 MPa,比基体钎料的提高了16.1%。
Abstract
Different contents of Mn element were added to CuZnNi alloy brazing filler. The effect of Mn element on liquidus temperature, wettability, and mechanical properties of brazing filler and joint was studied. The results show that liquidus temperature of brazing filler decreased gradually with increase of Mn content and liquidus temperature of brazing filler dropped 54℃ when mass fraction of Mn was 4.5%. Spreading area of brazing filler increased gradually with increase of Mn content and reached 298 mm2 when mass fraction of Mn was 4.5%. The tensile strength of CuZnNi increased and elongation increased first and then decreased with increase of Mn content. The shear strength of brazed joints increased gradually with the increase of Mn content and the shear strength was 221.2 MPa while mass fraction of Mn was 4.5% which was increased by 16.1% compared with that of base brazing filler.
中图分类号 TG454 DOI 10.11973/jxgccl201709015
所属栏目 材料性能及应用
基金项目 河南省杰出青年基金资助项目(144100510002)
收稿日期 2016/12/20
修改稿日期 2017/7/7
网络出版日期
作者单位点击查看
备注顾天亮(1992-),男,河南周口人,硕士研究生导师:闫焉服教授
引用该论文: GU Tianliang,YAN Yanfu,ZHANG Shaoqi. Effect of Mn Element on Properties of Copper-Based CuZnNi Alloy Brazing Filler[J]. Materials for mechancial engineering, 2017, 41(9): 81~84
顾天亮,闫焉服,张绍棋. 锰元素对铜基CuZnNi合金钎料性能的影响[J]. 机械工程材料, 2017, 41(9): 81~84
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陈龙,严莹,何云.硬质合金涂层刀片铣削AISI410不锈钢刀具寿命研究[J].硬质合金,2013, 30(1):29-33.
【2】薛维华,齐晓旭,李智超.热处理工艺对BCu58ZnMn钎料钎焊接头组织与性能的影响[J].机械工程材料,2015,39(6):20-24.
【3】ROBERTS P M. Improved brazing methods for tungsten carbide tools bits[J]. Welding Journal, 1997, 50(7):267-274.
【4】阙仲萍,王海龙.YG8硬质合金与42CrMo钢的真空钎焊连接[J].机械工程材料,2009,33(2):35-38.
【5】瞿智明,张福勤,夏莉.Cu基钎料钎焊紫铜的接头力学性能和微观组织[J].粉末冶金材料科学与工程,2015(1):133-138.
【6】钟文晨.低银铜基钎料化学成分的设计[J].广东有色金属学报,2005, 15(4):16-19.
【7】马向阳,俞伟元,路文江,等.高强度低熔点铜基钎料的研制[J].热加工工艺,2012, 41(11):133-135.
【8】黄俊兰,龙伟民,张冠星.Sn元素对铜磷钎料性能和组织的影响[J].焊接,2012(3):57-60.
【9】李小强,敖敬培,李子阳,等.CuMnNiCo钎料钎焊MGH956合金接头组织及力学性能研究[J].材料工程,2015,43(5):21-26.
【10】王大勇,冯吉才.杨氏方程的能量求解法及润湿角计算模型[J].焊接学报,2002,23(6):59-61.
【2】薛维华,齐晓旭,李智超.热处理工艺对BCu58ZnMn钎料钎焊接头组织与性能的影响[J].机械工程材料,2015,39(6):20-24.
【3】ROBERTS P M. Improved brazing methods for tungsten carbide tools bits[J]. Welding Journal, 1997, 50(7):267-274.
【4】阙仲萍,王海龙.YG8硬质合金与42CrMo钢的真空钎焊连接[J].机械工程材料,2009,33(2):35-38.
【5】瞿智明,张福勤,夏莉.Cu基钎料钎焊紫铜的接头力学性能和微观组织[J].粉末冶金材料科学与工程,2015(1):133-138.
【6】钟文晨.低银铜基钎料化学成分的设计[J].广东有色金属学报,2005, 15(4):16-19.
【7】马向阳,俞伟元,路文江,等.高强度低熔点铜基钎料的研制[J].热加工工艺,2012, 41(11):133-135.
【8】黄俊兰,龙伟民,张冠星.Sn元素对铜磷钎料性能和组织的影响[J].焊接,2012(3):57-60.
【9】李小强,敖敬培,李子阳,等.CuMnNiCo钎料钎焊MGH956合金接头组织及力学性能研究[J].材料工程,2015,43(5):21-26.
【10】王大勇,冯吉才.杨氏方程的能量求解法及润湿角计算模型[J].焊接学报,2002,23(6):59-61.
相关信息