钢板近表面缺陷的交流电磁场检测
Alternating Current Field Measurement of the Near-Surface Cracks in Steel Plate
摘 要
将金属薄片覆盖在含有人工裂纹的钢板上来模拟近表面缺陷，通过搭建交流电磁场检测的试验平台来提取近表面缺陷的磁场信号。试验得出了近表面裂纹交流电磁场检测的最佳激励频率、最大埋深厚度及影响近表面裂纹检测的因素，以为近表面裂纹的实际检测提供参考。
近表面裂纹
激励频率
alternating current field measurement
near-surface crack
excitation frequency
Abstract
In view of the near surface defects detection, steel plates containing artificial cracks were covered with the sheet metal to simulate the near-surface defects, and the experiment platform of ACFM was built to extract magnetic field signal of the near-surface defects. Experimental data were analyzed, and the optimal excitation frequency, the maximum burial depth and related influencing factors of ACFM on near-surface cracks were obtained, which could provide a reference for the practical detection on the near-surface cracks.
中图分类号 TG806 TG115.28 DOI 10.11973/wsjc201709003
所属栏目 试验研究
基金项目 国家自然科学基金资助项目（51065024）。
收稿日期 2016/12/16
修改稿日期
网络出版日期
作者单位点击查看
备注胡江(1993-),男,硕士研究生,主要研究方向为电磁无损检测技术
引用该论文: HU Jiang,REN Shangkun,ZU Ruili. Alternating Current Field Measurement of the Near-Surface Cracks in Steel Plate[J]. Nondestructive Testing, 2017, 39(9): 11～14
胡江,任尚坤,祖瑞丽. 钢板近表面缺陷的交流电磁场检测[J]. 无损检测, 2017, 39(9): 11～14
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李健.主动式电磁扫描检测技术及其信号处理方法研究[D].南昌:华东交通大学, 2012.
【2】曹雄恒.矩形线圈激励无损检测技术研究[D].长沙:国防科学技术大学,2002.
【3】魏朋,任尚坤,叶顺科.扰动磁场检测笔试探头的研制及试验分析[J].仪表技术与传感器,2016(7):32-35.
【4】李伟,张传荣,陈国明,等.U型ACFM探头精确建模和实验测试[J].电子测量与仪器学报, 2013,27(7):658-662.
【5】张玉华.金属平板表面缺陷扰动的磁场量分布研究[D].长沙:国防科学技术大学,2003.
【6】李兵,于亮.交流电磁场检测技术在压力容器焊缝检测中的应用[J].检测技术,2016,32(4):47-50.
【2】曹雄恒.矩形线圈激励无损检测技术研究[D].长沙:国防科学技术大学,2002.
【3】魏朋,任尚坤,叶顺科.扰动磁场检测笔试探头的研制及试验分析[J].仪表技术与传感器,2016(7):32-35.
【4】李伟,张传荣,陈国明,等.U型ACFM探头精确建模和实验测试[J].电子测量与仪器学报, 2013,27(7):658-662.
【5】张玉华.金属平板表面缺陷扰动的磁场量分布研究[D].长沙:国防科学技术大学,2003.
【6】李兵,于亮.交流电磁场检测技术在压力容器焊缝检测中的应用[J].检测技术,2016,32(4):47-50.
相关信息