GIS设备导体缺陷X射线数字成像检测及缺陷产生原因分析
Detection of GIS Equipment Conductor Defects by X-ray Digital Imaging and Analysis of Defect Causes
摘 要
采用X射线数字成像系统对气体绝缘金属封闭开关变电站（GIS）设备导体进行检测，发现导体焊接部位存在裂纹、未熔合等缺陷。经解体检查，X射线数字成像结果与实物缺陷一致。同时，理化试验结果表明，焊接工艺不当是导致导体产生缺陷的根本原因，并提出相应的解决措施。
GIS设备
导体
缺陷检测
X-ray digital imaging
GIS equipment
conductor
defect detection
Abstract
By using X-ray digital imaging system, the test on GIS equipment conductor found some defects on welded parts of the conductor, such as cracks and incomplete fusion. After disintegrating, the X-ray digital imaging result is consistent with the physical defects. Meanwhile, the results of the physical and chemical test show that the improper welding process is the root cause of defects of the conductor, and following that appropriate solutions are proposed.
中图分类号 TG115.28 DOI 10.11973/wsjc201709019
所属栏目 实践经验
基金项目
收稿日期 2016/12/29
修改稿日期
网络出版日期
作者单位点击查看
备注胡加瑞(1984-),男,工程师,主要从事电力系统金属部件失效分析工作
引用该论文: HU Jiarui,LI Wenbo,LIU Chun,CHEN Hongdong,XIE Yi. Detection of GIS Equipment Conductor Defects by X-ray Digital Imaging and Analysis of Defect Causes[J]. Nondestructive Testing, 2017, 39(9): 76～79
胡加瑞,李文波,刘纯,陈红冬,谢亿. GIS设备导体缺陷X射线数字成像检测及缺陷产生原因分析[J]. 无损检测, 2017, 39(9): 76～79
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李继胜,赵学风,杨景刚,等.GIS典型缺陷局部放电测量与分析[J].高电压技术,2009,35(10): 2440-2445.
【2】罗俊华,赵中原,邱毓昌,等.局部放电信号三维图谱的分形特征研究 [J].高电压技术,2001, 27(6):24-25.
【3】李大勇.GIS设备故障原因分析及对策[J].中国科技信息,2011(6):98-99.
【4】李强,孙朝明.数字射线检测中图像评定尺的设计与应用[J].无损检测,2011,33(4):33-35.
【5】杨再华,李玉和,李庆祥,等.基于边缘特征提取的图像清晰度评价函数[J].计算机工程与应用, 2005,41(10):35-36.
【6】杨卫.宏微观断裂力学[M].北京:国防工业出版社,1995.
【2】罗俊华,赵中原,邱毓昌,等.局部放电信号三维图谱的分形特征研究 [J].高电压技术,2001, 27(6):24-25.
【3】李大勇.GIS设备故障原因分析及对策[J].中国科技信息,2011(6):98-99.
【4】李强,孙朝明.数字射线检测中图像评定尺的设计与应用[J].无损检测,2011,33(4):33-35.
【5】杨再华,李玉和,李庆祥,等.基于边缘特征提取的图像清晰度评价函数[J].计算机工程与应用, 2005,41(10):35-36.
【6】杨卫.宏微观断裂力学[M].北京:国防工业出版社,1995.
相关信息