Effect of Heat Treatment Process on Microstructure and Mechanical Properties of 1.2367 Steel
摘 要
对1.2367钢进行了不同加热温度和冷却方式的淬火以及不同温度回火的热处理等试验,通过硬度检验、显微组织观察、冲击功测试等对比分析方法确定了最佳热处理工艺,分析了相应的组织、性能。结果表明:其最佳的热处理工艺为1 010~1 040℃加热油淬,550~600℃回火;相应的硬度50~45 HRC,横向冲击功300 J以上,可以满足热作模具高温硬度和抗冲击性能的要求。
Abstract
By testing of different heating temperature and cooling quenching and tempering at different temperatures of heat treatment of 1.2367 steel, through hardness test, microstructure observation, impact test comparative analysis method, the optimum heat treatment process was determined and the corresponding microstructure, performance were analysised. The results show that the optimum heat treatment process is 1 010 to 1 040℃ heating oil quenching, tempering 550 to 600℃; the hardness of 45-50 HRC, transverse impact energy more than 300 J, can meet the hot die hardness and impact toughness of high temperature performance requirements.
中图分类号 TG142.45
所属栏目
基金项目
收稿日期
修改稿日期
网络出版日期
作者单位点击查看
备注孙秀华(1968-),女,高级工程师,主要从事工模具钢新产品工艺研究及开发
引用该论文: SUN Xiuhua,LIU Baoshiand,WEI Wentao. Effect of Heat Treatment Process on Microstructure and Mechanical Properties of 1.2367 Steel[J]. Materials for mechancial engineering, 2017, 41(Z2): 81~84
孙秀华,刘宝石,魏文韬. 热处理工艺对1.2367钢组织及力学性能的影响[J]. 机械工程材料, 2017, 41(Z2): 81~84
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
相关信息