Corrosion Behavior of A286 Flap Lock in Accelerated Corrosive Environment in Laboratory
摘 要
对安装与未安装两种形式口盖锁进行了实验室加速腐蚀试验,通过蚀坑深度和力矩差(松脱力矩与拧紧力矩的差值)研究了A286口盖锁的腐蚀行为,分析了装配过程及装配应力对口盖锁腐蚀行为的影响。结果表明:安装口盖锁的腐蚀程度明显高于未安装口盖锁的;未安装口盖锁的主要腐蚀形式是接触腐蚀,而安装类口盖锁的主要腐蚀形式是接触腐蚀和应力腐蚀;应力腐蚀对口盖锁腐蚀的影响比接触腐蚀的更大。
Abstract
To study the corrosion behavior of A286 flap lock, accelerated environment corrosion tests for installed flap lock and uninstalled flap lock were carried out in laboratory. Corrosion behavior of A286 flap lock was analyzed through pit depth and torque difference between loosening and tightening. And the influences of assembly process and assembly stress on the corrosion behavior of flap lock were studied. The results show that the corrosion of installed flap lock was more serious than that of the uninstalled flap lock. The main corrosion form of uninstalled flap lock was contact corrosion, while the main corrosion forms of installed flap lock were contact corrosion and stress corrosion. Stress corrosion had greater influence on corrosion behavior of flap lock than contact corrosion.
中图分类号 TG172 DOI 10.11973/fsyfh-201712008
所属栏目 试验研究
基金项目
收稿日期 2016/4/17
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHAO Lianhong,LIU Yuanhai,WANG Haowei. Corrosion Behavior of A286 Flap Lock in Accelerated Corrosive Environment in Laboratory[J]. Corrosion & Protection, 2017, 38(12): 938
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】杨文芳. 浅谈飞机口盖锁的选用[J]. 航空标准化与质量,2011,12(3):45-50.
【2】郁春娟. 常用金属紧固件在水环境中的腐蚀行为[J]. 装备环境工程,2010,7(5):4-12.
【3】刘成臣,王浩伟,杨晓华. 不同材料在海洋大气环境下的加速环境谱研究[J]. 装备环境工程,2013,7(2):18-24.
【4】刘成臣,王浩伟,鲁国富. 2A12铝合金当量加速腐蚀试验[J]. 腐蚀与防护,2014,35(5):458-461.
【5】张有宏,铝国志,任克亮,等. 不同环境下LY12-CZ铝合金表面腐蚀损伤演化规律研究[J]. 航空学报,2007,28(1):142-145.
【6】HARLOW D J,WEI R P. A probability model for the growth of corrosion pits in aluminum alloys induced by constituent particles[J]. Engineering Fracture Mechanic,1988,59(3):305-325.
【2】郁春娟. 常用金属紧固件在水环境中的腐蚀行为[J]. 装备环境工程,2010,7(5):4-12.
【3】刘成臣,王浩伟,杨晓华. 不同材料在海洋大气环境下的加速环境谱研究[J]. 装备环境工程,2013,7(2):18-24.
【4】刘成臣,王浩伟,鲁国富. 2A12铝合金当量加速腐蚀试验[J]. 腐蚀与防护,2014,35(5):458-461.
【5】张有宏,铝国志,任克亮,等. 不同环境下LY12-CZ铝合金表面腐蚀损伤演化规律研究[J]. 航空学报,2007,28(1):142-145.
【6】HARLOW D J,WEI R P. A probability model for the growth of corrosion pits in aluminum alloys induced by constituent particles[J]. Engineering Fracture Mechanic,1988,59(3):305-325.
相关信息