低碳钢淬火发蓝工艺及膜层性能
The Process and Property of Low-Carbon Steel Treated by Quench-Bluing
摘 要
采用淬火发蓝工艺在低碳钢表面制备了一层发蓝膜过程。通过扫描电子显微镜、XRD电子衍射、点滴试验、擦拭试验、电化学测试和盐雾试验对蓝色氧化膜的厚度、晶体结构、连续性、耐磨性、耐腐蚀性进行评价。结果表明，淬火发蓝工艺简单、操作方便并且膜层厚度较薄，色泽美观，连续性、耐磨性和耐蚀性优异。
低碳钢
膜层
性能
quench-bluing
low-carbon steel
film
performance
Abstract
The process of quench-bluing treatment on low-carbon steel was introduced. The thickness, crystal structure, continuity, wear resistance and corrosion resistance of the blue oxide film were evaluated by scanning electron microscopy, X-ray diffraction, drip experiment, wipe test, electrochemical test and salt spray test. The results show that quench-bluing process is easy to operate, the thin film has beautiful color and the performances of film are excellent.
中图分类号 TG174 DOI 10.11973/fsyfh-201801010
所属栏目 应用技术
基金项目 南通市产学研协同创新计划项目（BC2014010）；上海市钢铁冶金新技术开发应用重点实验室开放课题基金资助（SELF-2015-01）
收稿日期 2016/4/10
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: LI Hui,SUN Jinhu,ZHONG Qingdong,HUANG Zherui,LI Yulin. The Process and Property of Low-Carbon Steel Treated by Quench-Bluing[J]. Corrosion & Protection, 2018, 39(1): 49
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】黄艳松,马俊文,汪彬. 钢铁零件常温氧化新工艺[J]. 腐蚀与防护,2009,30(10):753.
【2】张俊喜,钱瑜明,张铃松,等. 新型不锈钢低温发黑工艺[J]. 腐蚀与防护,2008,29(5):272-274.
【3】葛瑞荣,周尚荣,刘诚,等. 45钢蒸汽发蓝工艺及膜层性能研究[J]. 热加工工艺,2010,39(10):194-197.
【4】ZHU H,CAO F,ZUO D,et al. A new hydrothermal blackening technology for Fe3O4 coatings of carbon steel[J]. Applied Surface Science,2008,254(18):5905-5909.
【5】黄菲,张万灵,涂元强. 钢铁发蓝工艺研究[J]. 武汉工程职业技术学院学报,2010,22(2):14-17.
【6】姚远,卢建树,吴敏. 氮气保护低碳钢水蒸气发黑方法及膜层性能[J]. 腐蚀与防护,2008,29(9):544-546.
【7】张瀚福. 介绍发蓝淬火的经验[J]. 机械工人,1958(1):21.
【8】张发余,张以峰,张书弟. 钢铁常温发黑工艺[J]. Plating and Finishing,2004,26(3):20-23.
【9】王树成,王英兰. 我国钢铁发黑技术的应用和发展[J]. 表面技术,2012,41(3):112-114.
【10】CHEN J,HUANG K,LIU S. Hydrothermal preparation of a protective Fe3O4 film on Fe foil[J]. Corrosion Science,2008,50(7):1982-1986.
【11】KUZNETSOV Y I,VERSHOK D B,TIMASHEV S F,et al. Features of formation of magnetite coatings on low-carbon steel in hot nitrate solutions[J]. Russian Journal of Electrochemistry,2010,46(10):1155-1166.
【12】FRANGER S,BERTHET P,BERTHON J. Electrochemical synthesis of Fe3O4 nanoparticles in alkaline aqueous solutions containing complexing agents[J]. Journal of Solid State Electrochemistry,2004,8(4):218-223.
【13】文斯雄. 提高钢铁件发蓝膜层耐蚀性的措施[J]. 材料保护,2000,33(9):10-11.
【14】张玉峰,周厚强. 弹簧件常温复合发蓝工艺研究[J]. 电镀与涂饰,2002,21(4):20-22.
【2】张俊喜,钱瑜明,张铃松,等. 新型不锈钢低温发黑工艺[J]. 腐蚀与防护,2008,29(5):272-274.
【3】葛瑞荣,周尚荣,刘诚,等. 45钢蒸汽发蓝工艺及膜层性能研究[J]. 热加工工艺,2010,39(10):194-197.
【4】ZHU H,CAO F,ZUO D,et al. A new hydrothermal blackening technology for Fe3O4 coatings of carbon steel[J]. Applied Surface Science,2008,254(18):5905-5909.
【5】黄菲,张万灵,涂元强. 钢铁发蓝工艺研究[J]. 武汉工程职业技术学院学报,2010,22(2):14-17.
【6】姚远,卢建树,吴敏. 氮气保护低碳钢水蒸气发黑方法及膜层性能[J]. 腐蚀与防护,2008,29(9):544-546.
【7】张瀚福. 介绍发蓝淬火的经验[J]. 机械工人,1958(1):21.
【8】张发余,张以峰,张书弟. 钢铁常温发黑工艺[J]. Plating and Finishing,2004,26(3):20-23.
【9】王树成,王英兰. 我国钢铁发黑技术的应用和发展[J]. 表面技术,2012,41(3):112-114.
【10】CHEN J,HUANG K,LIU S. Hydrothermal preparation of a protective Fe3O4 film on Fe foil[J]. Corrosion Science,2008,50(7):1982-1986.
【11】KUZNETSOV Y I,VERSHOK D B,TIMASHEV S F,et al. Features of formation of magnetite coatings on low-carbon steel in hot nitrate solutions[J]. Russian Journal of Electrochemistry,2010,46(10):1155-1166.
【12】FRANGER S,BERTHET P,BERTHON J. Electrochemical synthesis of Fe3O4 nanoparticles in alkaline aqueous solutions containing complexing agents[J]. Journal of Solid State Electrochemistry,2004,8(4):218-223.
【13】文斯雄. 提高钢铁件发蓝膜层耐蚀性的措施[J]. 材料保护,2000,33(9):10-11.
【14】张玉峰,周厚强. 弹簧件常温复合发蓝工艺研究[J]. 电镀与涂饰,2002,21(4):20-22.
相关信息