涂层厚度对涡流检测的影响
The Influence of Coating Thickness on the Eddy Current Testing
摘 要
采用放置式探头对带有不同厚度涂层的含有表面缺陷的钢板进行涡流检测，研究涡流检测表面缺陷的能力与涂层厚度之间的关系。结果表明：在表面涂层厚度不大于2 500 μm时，使用放置式探头的涡流检测方法检测钢板上的不同类型缺陷和不同深度缺陷的效果更好。
涂层
涡流检测
不同类型
不同深度
placed type probe
coating
eddy current testing
different category
different depth
Abstract
The relationship between the effectiveness of detecting surface defects and the coating thickness was researched with the method of eddy current testing, and the placed type probe was used to inspect a defective steel plate with different coating thicknesses. Results have shown that better testing effect for surface defects on a steel plate with different categories and different depths can be realized by the eddy current test using a placed type probe if the surface coating thickness is not greater than 2 500 μm.
中图分类号 TB553 TG115.28 DOI 10.11973/wsjc201801008
所属栏目 试验研究
基金项目
收稿日期 2017/7/25
修改稿日期
网络出版日期
作者单位点击查看
备注岳庚新(1988-),男,硕士研究生,主要从事无损检测技术研究工作
引用该论文: YUE Gengxin. The Influence of Coating Thickness on the Eddy Current Testing[J]. Nondestructive Testing, 2018, 40(1): 34～36
岳庚新. 涂层厚度对涡流检测的影响[J]. 无损检测, 2018, 40(1): 34～36
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】徐可北,周俊华. 涡流检测[M]. 北京:机械工业出版社, 2004.
【2】刘振作. 涡流涂镀层测厚仪开发与应用现状[J]. 工程与试验, 2003, 43(2):4-7.
【3】张会云. 金属薄镀层涡流测厚技术研究[D]. 北京:北京机械科学研究院, 2003:2-3.
【4】吕香慧, 张宇, 楼淼, 等. 带涂层焊缝的电磁涡流检测[J]. 无损检测, 2010,32(6):441-443.
【5】陈朝晖. 基于涡流探伤原理的焊缝疲劳裂纹监测系统设计[D]. 南昌:华东交通大学, 2013.
【6】彭国平, 杜南胜, 李洪刚. 不锈钢储液罐的涡流检测[J]. 无损检测, 2012, 34(10):35-36.
【7】林俊明, 张开良, 林发炳, 等. 焊缝表面裂纹涡流检测技术[J].中国锅炉压力容器安全,2004,20(6):33-36.
【2】刘振作. 涡流涂镀层测厚仪开发与应用现状[J]. 工程与试验, 2003, 43(2):4-7.
【3】张会云. 金属薄镀层涡流测厚技术研究[D]. 北京:北京机械科学研究院, 2003:2-3.
【4】吕香慧, 张宇, 楼淼, 等. 带涂层焊缝的电磁涡流检测[J]. 无损检测, 2010,32(6):441-443.
【5】陈朝晖. 基于涡流探伤原理的焊缝疲劳裂纹监测系统设计[D]. 南昌:华东交通大学, 2013.
【6】彭国平, 杜南胜, 李洪刚. 不锈钢储液罐的涡流检测[J]. 无损检测, 2012, 34(10):35-36.
【7】林俊明, 张开良, 林发炳, 等. 焊缝表面裂纹涡流检测技术[J].中国锅炉压力容器安全,2004,20(6):33-36.
相关信息