Analysis of Aging Failure of 3PE Heat Shrinkable Sleeve and Improvement Measures
摘 要
利用热水浸泡的方法研究了湿热老化对不同类型的补口用3PE热收缩带腐蚀防护性能的影响。结果表明:热熔胶中含有的酸酐基团能加速3PE热收缩带的失效进程;干膜型3PE热收缩带的底漆固化程度优于湿膜型3PE热收缩带的底漆固化程度。
Abstract
The effects of wet and heat aging on corrosion protection of different types of 3PE heat shrinkable sleeve used in joint coating were studied by hot-water soak method. The results reveal that the acid anhydride groups in hot melt adhesive would accelerate the failure of the 3PE heat shrinkable sleeve; and the curing degree of the primer of dry film coating was superior to that of wet film coating.
中图分类号 TG174 DOI 10.11973/fsyfh-201802018
所属栏目 失效分析
基金项目
收稿日期 2016/7/21
修改稿日期
网络出版日期
作者单位点击查看
联系人作者王世银(andnce@163.com)
引用该论文: WANG Shiyin,FAN Xiaoyin,LIU Changhai. Analysis of Aging Failure of 3PE Heat Shrinkable Sleeve and Improvement Measures[J]. Corrosion & Protection, 2018, 39(2): 162
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张清玉. 油气田工程实用防腐蚀技术[M]. 北京:中国石化出版社,2009.
【2】罗锋,王国丽,窦鹏,等. 管道热收缩带补口失效原因分析及相关对策研究[J]. 石油规划设计,2012,23(1):11-15.
【3】李章亚. 油气田腐蚀与防护手册[M]. 北京:石油工业出版社,1999.
【4】D·L·贝特曼. 热熔黏合剂[M]. 北京:轻工业出版社,1989.
【5】汪贤华,周义能,韩丽娜,等. 石油天然气防腐钢管胶粘剂性能及应用[J]. 防腐保温技术,2002,10(3):5-8.
【6】吴迎霞,沈赤霞. 管道防腐用改性EVA热熔胶的研制[J]. 化学与黏合,2006,28(3):166-168.
【7】张志强,杨军伟. 60度防腐热熔胶:200910035813.3[P]. 2009-09-23.
【8】张志强,杨军伟. 80度防腐热熔胶及其制备方法:200910035357.2[P]. 2009-09-25.
【9】张其滨,刘金霞,赫连建峰. 埋地钢质管道聚乙烯防腐层:GB/T 23257-2009[S]. 北京:中国标准出版社,2009.
【2】罗锋,王国丽,窦鹏,等. 管道热收缩带补口失效原因分析及相关对策研究[J]. 石油规划设计,2012,23(1):11-15.
【3】李章亚. 油气田腐蚀与防护手册[M]. 北京:石油工业出版社,1999.
【4】D·L·贝特曼. 热熔黏合剂[M]. 北京:轻工业出版社,1989.
【5】汪贤华,周义能,韩丽娜,等. 石油天然气防腐钢管胶粘剂性能及应用[J]. 防腐保温技术,2002,10(3):5-8.
【6】吴迎霞,沈赤霞. 管道防腐用改性EVA热熔胶的研制[J]. 化学与黏合,2006,28(3):166-168.
【7】张志强,杨军伟. 60度防腐热熔胶:200910035813.3[P]. 2009-09-23.
【8】张志强,杨军伟. 80度防腐热熔胶及其制备方法:200910035357.2[P]. 2009-09-25.
【9】张其滨,刘金霞,赫连建峰. 埋地钢质管道聚乙烯防腐层:GB/T 23257-2009[S]. 北京:中国标准出版社,2009.
相关信息
标题 | 相关频次 | |
氟化铵辅助消解-电感耦合等离子体质谱法测定热熔胶中7种微量元素 | 2 | |
聚丙烯热收缩带补口材料研制 | 2 | |
盐雾环境中螺栓防腐蚀方法优选 | 2 |