钻头用15CrNiMn钢奥氏体的连续冷却转变
Continuous Cooling Transformation of Austenite in 15CrNiMn Steel for Drilling Bit
摘 要
采用DIL805L型膨胀仪测得了钻头用15CrNiMn钢的奥氏体连续冷却转变（CCT）曲线，研究了试验钢在不同冷却速率下的相变过程、显微组织和硬度。结果表明：试验钢在很宽的冷速范围内均出现贝氏体组织，铁素体、珠光体转变区和贝氏体转变区完全分离；随着冷却速率增加，试验钢的室温组织逐渐细化，硬度明显增大。
相变
CCT曲线
显微组织
硬度
15CrNiMn steel for drilling bit
phase transformation
CCT curve
microstructure
hardness
Abstract
The austenite continuous cooling transformation (CCT) curves of 15CrNiMn steel for drilling bit were determined by DIL805L dilatometer. The phase transformation, microstructure and hardness of the tested steel at different cooling rates were studied. The results show that the bainite structure was obtained in the tested steel over a large range of cooling rates, and the transformation zones of ferrite or pearlite and bainite were separated completely. With the cooling rate increasing, the microstructure of the tested steel became finer and the hardness increased obviously.
中图分类号 TG142.4 DOI 10.11973/jxgccl201802009
所属栏目 试验研究
基金项目 河北省科技计划项目（14211014D）
收稿日期 2017/1/24
修改稿日期 2018/1/3
网络出版日期
作者单位点击查看
备注侯环宇(1981-),女,山西忻州人,工程师,硕士
引用该论文: HOU Huanyu,LIANG Aiguo,AN Zhiguo,CHEN Hongwei,SHI Yuan. Continuous Cooling Transformation of Austenite in 15CrNiMn Steel for Drilling Bit[J]. Materials for mechancial engineering, 2018, 42(2): 40～42
侯环宇,梁爱国,安治国,陈红卫,史远. 钻头用15CrNiMn钢奥氏体的连续冷却转变[J]. 机械工程材料, 2018, 42(2): 40～42
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李美宁.牙轮钻头用钢及热处理[C]//第八届中国钢铁年会论文集.北京:中国金属学会,2011:4603-4605.
【2】何畏,郝广辉,李波,等.18CrNiMo7-6钢牙轮钻头轴承渗碳工艺的优化[J].热加工工艺,2015,44(22):115-121.
【3】杨眉,刘清才,高英,等.牙轮钻头强化用YQ4堆焊层组织性能研究[J].西南石油大学学报(自然科学版),2010,32(2):169-172.
【4】徐亮,章小浒,黄金国,等.700 MPa级低碳微合金钢的连续冷却相变组织及强韧性[J].机械工程材料,2015,39(6):29-35.
【5】TRZASKA J, DOBRZANSKI L A. Modelling of CCT diagrams for engineering and constructional steel[J]. Journal of Materials Processing Technology, 2007, 192/193:504-510.
【6】陈连生,米振鹏,田亚强,等.含铜低碳硅锰钢的连续冷却转变曲线及显微组织[J].机械工程材料,2015,39(12):98-101.
【7】PODDER A S, BHADESHIA H K D H. Thermal stability of austenite retained in bainitic steels[J]. Materials Science and Engineering A,2010,527(7/8):2121-2128.
【8】林惠国,傅代直.钢的奥氏体转变曲线:原理、测试与应用[M].北京:冶金工业出版杜,1998.
【9】金光灿,李锦,罗一平.部分奥氏体化和完全奥氏体化铁素体/马氏体双相钢的CCT曲线[J].机械工程材料,2015,39(5):27-32.
【10】安治国,黄艳新,侯环宇,等.汽车前轴用贝氏体型非调质钢连续冷却转变[J].钢铁,2016,51(12):70-73.
【11】侯环宇,黄艳新,田志强,等.弹簧钢52CrMoV4连续冷却相变的组织变化[J].材料热处理学报,2016,37(9):129-132.
【2】何畏,郝广辉,李波,等.18CrNiMo7-6钢牙轮钻头轴承渗碳工艺的优化[J].热加工工艺,2015,44(22):115-121.
【3】杨眉,刘清才,高英,等.牙轮钻头强化用YQ4堆焊层组织性能研究[J].西南石油大学学报(自然科学版),2010,32(2):169-172.
【4】徐亮,章小浒,黄金国,等.700 MPa级低碳微合金钢的连续冷却相变组织及强韧性[J].机械工程材料,2015,39(6):29-35.
【5】TRZASKA J, DOBRZANSKI L A. Modelling of CCT diagrams for engineering and constructional steel[J]. Journal of Materials Processing Technology, 2007, 192/193:504-510.
【6】陈连生,米振鹏,田亚强,等.含铜低碳硅锰钢的连续冷却转变曲线及显微组织[J].机械工程材料,2015,39(12):98-101.
【7】PODDER A S, BHADESHIA H K D H. Thermal stability of austenite retained in bainitic steels[J]. Materials Science and Engineering A,2010,527(7/8):2121-2128.
【8】林惠国,傅代直.钢的奥氏体转变曲线:原理、测试与应用[M].北京:冶金工业出版杜,1998.
【9】金光灿,李锦,罗一平.部分奥氏体化和完全奥氏体化铁素体/马氏体双相钢的CCT曲线[J].机械工程材料,2015,39(5):27-32.
【10】安治国,黄艳新,侯环宇,等.汽车前轴用贝氏体型非调质钢连续冷却转变[J].钢铁,2016,51(12):70-73.
【11】侯环宇,黄艳新,田志强,等.弹簧钢52CrMoV4连续冷却相变的组织变化[J].材料热处理学报,2016,37(9):129-132.
相关信息