Corrosion Behavior of 2205 Duplex Stainless Steel in Severe Environment of Oilfield
摘 要
模拟了油田酸化完井全过程和产出工况,结合电化学分析研究了2205双相不锈钢在这两种环境中的腐蚀行为。结果表明:试验钢在含CO2气体的地层水中发生轻微的均匀腐蚀,在CO2分压为4.80 MPa、试验温度为220℃下的均匀腐蚀速率仅为0.002 1 mm·a-1;在酸化完井全过程腐蚀时,试验钢发生明显的铁素体相选择性溶解腐蚀,腐蚀速率最小为0.523 6 mm·a-1,远高于其在含CO2气体地层水中的腐蚀速率;在新配制酸溶液中腐蚀时,试验钢处于活化状态,腐蚀速率较大,在含0.1 MPa CO2气体的地层水中,试验钢阳极区出现钝化现象,腐蚀速率显著降低。
Abstract
The corrosion behavior of 2205 duplex stainless steel under the simulated conditions of the whole process of simulated acidification well completion and production was studied by the combination of electrochemical analysis. The results show that the test steel exhibited slightly uniform corrosion in the formation water containing CO2. When the CO2 partial pressure was 4.80 MPa and the experimental temperature was 220℃, the corrosion rate was only 0.002 1 mm·a-1. The test steel had an obvious ferrite phase selective dissolve corrosion during corrosion in the whole process of acidification well completion, with a lowest corrosion rate of 0.523 6 mm·a-1, which was much higher than that in the formation water containing CO2. The test steel was activated in the fresh prepared acid solution, and the corrosion rate was relatively high. In the formation water containing 0.1 MPa CO2, the anodic polarization zone of the test steel showed a passivation phenomenon, and thus the corrosion rate was reduced significantly.
中图分类号 TG172.8 DOI 10.11973/jxgccl201802018
所属栏目 材料性能及应用
基金项目 国家自然科学基金资助项目(51271146);陕西省自然科学基础研究计划项目(2016JM5064)
收稿日期 2017/7/30
修改稿日期 2017/12/26
网络出版日期
作者单位点击查看
备注赵国仙(1968-),女,山西运城人,教授,博士
引用该论文: ZHAO Guoxian,WANG Yaqian,JI Ling,LIANG Jianjun,XIE Junfeng,LÜ,Xianghong. Corrosion Behavior of 2205 Duplex Stainless Steel in Severe Environment of Oilfield[J]. Materials for mechancial engineering, 2018, 42(2): 82~87
赵国仙,王雅倩,计玲,梁建军,谢俊峰,吕祥鸿. 油田苛刻环境中2205双相不锈钢的腐蚀行为[J]. 机械工程材料, 2018, 42(2): 82~87
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】GUNN R. Duplex stainless steels:Microstructure, properties and applications[M].[S.l.]:Woodhead Publishing, 1997:94-102.
【2】ALVAREZ-ARMAS I. Duplex stainless steels:Brief history and some recent alloys[J]. Recent Patents on Mechanical Engineering, 2008, 1(1):51-57.
【3】安杰.深层低渗透油气藏4in套管压裂工艺技术研究[D].北京:中国石油大学,2011.
【4】朱斯明. 油层压裂:攻坚克难促产能[N]. 中国石化报,2010-08-09(7).
【5】王连成,李明朗,程万庆,等.酸化压裂方法在碳酸盐岩热储层中的应用[J].水文地质工程地质,2010, 37(5):128-132.
【6】肖国华.不动管柱分层酸化压裂工艺管柱研究[J].石油机械,2004,32(2):49-55.
【7】张双双.酸化液对13Cr油管柱的腐蚀[D].西安:西安石油大学,2014.
【8】解琼,史培阳,姜茂发. 铁素体不锈钢在盐酸溶液中的腐蚀过程[J]. 东北大学学报(自然科学版),2015,36(1):38-42.
【9】颜润浦,赵吉庆,杨钢,等. 工业纯钛在盐酸中的腐蚀行为[J]. 腐蚀与防护,2015,36(2):182-186.
【10】SCHUTZ R W, THODLA R, BAXTER C F, et al. Preliminary determination of hot sour brine environmental effect on fatigue crack growth rate in grade 29 titanium pipe base and weld metal[C]//Corrosion 2011. Houston, Texas:NACE International, 2011:NACE-11119.
【11】王凤平,康万利,敬和民,等. 腐蚀电化学原理,方法及应用[M].北京:化学工业出版社,2008:39-90.
【12】毕树平,杨立,韩韦英,等.电化学测量铝的方法:7502591303[P].2006-09-27.
【13】曹楚南,吴萌顺. 腐蚀电化学[M]. 北京:化学工业出版社,1994:91-115.
【14】王荣光,闵国全. 双相不锈钢在应力腐蚀开裂过程中的选择性腐蚀[J]. 中国腐蚀与防护学报, 1998, 18(1):47-51.
【15】付燕,林昌健,蔡文达.微电化学技术研究双相不锈钢优选腐蚀行为[J].金属学报, 2005,41(3):302-306.
【16】蔡文达,蔡坤铭, 林昌健, 等. 双相不锈钢的选择性腐蚀研究[J]. 电化学,2003,9(2):170-176.
【2】ALVAREZ-ARMAS I. Duplex stainless steels:Brief history and some recent alloys[J]. Recent Patents on Mechanical Engineering, 2008, 1(1):51-57.
【3】安杰.深层低渗透油气藏4in套管压裂工艺技术研究[D].北京:中国石油大学,2011.
【4】朱斯明. 油层压裂:攻坚克难促产能[N]. 中国石化报,2010-08-09(7).
【5】王连成,李明朗,程万庆,等.酸化压裂方法在碳酸盐岩热储层中的应用[J].水文地质工程地质,2010, 37(5):128-132.
【6】肖国华.不动管柱分层酸化压裂工艺管柱研究[J].石油机械,2004,32(2):49-55.
【7】张双双.酸化液对13Cr油管柱的腐蚀[D].西安:西安石油大学,2014.
【8】解琼,史培阳,姜茂发. 铁素体不锈钢在盐酸溶液中的腐蚀过程[J]. 东北大学学报(自然科学版),2015,36(1):38-42.
【9】颜润浦,赵吉庆,杨钢,等. 工业纯钛在盐酸中的腐蚀行为[J]. 腐蚀与防护,2015,36(2):182-186.
【10】SCHUTZ R W, THODLA R, BAXTER C F, et al. Preliminary determination of hot sour brine environmental effect on fatigue crack growth rate in grade 29 titanium pipe base and weld metal[C]//Corrosion 2011. Houston, Texas:NACE International, 2011:NACE-11119.
【11】王凤平,康万利,敬和民,等. 腐蚀电化学原理,方法及应用[M].北京:化学工业出版社,2008:39-90.
【12】毕树平,杨立,韩韦英,等.电化学测量铝的方法:7502591303[P].2006-09-27.
【13】曹楚南,吴萌顺. 腐蚀电化学[M]. 北京:化学工业出版社,1994:91-115.
【14】王荣光,闵国全. 双相不锈钢在应力腐蚀开裂过程中的选择性腐蚀[J]. 中国腐蚀与防护学报, 1998, 18(1):47-51.
【15】付燕,林昌健,蔡文达.微电化学技术研究双相不锈钢优选腐蚀行为[J].金属学报, 2005,41(3):302-306.
【16】蔡文达,蔡坤铭, 林昌健, 等. 双相不锈钢的选择性腐蚀研究[J]. 电化学,2003,9(2):170-176.
相关信息