Analysis on Cracking Failure of Support Plate of Drum Filter Net of a Rotary Vacuum Filter
摘 要
某旋转真空过滤机滤网支撑板,在使用5 a(年)后开始出现零星开裂失效,局部更换后又使用了约2 a出现大面积开裂失效。采用宏观观察、化学成分分析、金相检验、扫描电镜分析、能谱分析等方法,对该支撑板开裂失效原因进行了分析。结果表明:支撑板材料中钼、镍元素含量低,使得滤网支撑板的耐腐蚀性能较低,在冷加工过程中产生的形变马氏体进一步影响了材料的耐腐蚀性能;过滤物中含有Br-造成了滤网支撑板的点蚀,在点蚀坑位置处产生应力集中,最终导致滤网支撑板发生了应力腐蚀开裂。
Abstract
Fragmentary cracking occurred on a rotary vacuum filter support plate after 5 a (annum) service. The plate was used about 2 a by replacing some parts, after that large area cracking failure appearing. The failure reasons were analyzed by means of macroscopic observation, chemical composition analysis, metallographic examination, scanning electron microscope analysis and energy spectrum analysis. The results show that the low content of Mo and Ni in the support plate, which makes the poor corrosion resistance of the filter support plate. The strain-induced martensite produced during cold processing further affects the corrosion resistance. The filters contains Br-, which results in pitting on the filter support plate. Stress concentration was produced at the pitting position, which eventually leads to the stress corrosion cracking of the filter support plate.
中图分类号 TG172.9 TG115.2 DOI 10.11973/lhjy-wl201803014
所属栏目 质量控制与失效分析
基金项目
收稿日期 2017/5/26
修改稿日期
网络出版日期
作者单位点击查看
备注梁涛(1992-),男,硕士,主要从事金属及其合金的金相分析和失效分析工作,1435926665@qq.com
引用该论文: LIANG Tao,JIANG Yong. Analysis on Cracking Failure of Support Plate of Drum Filter Net of a Rotary Vacuum Filter[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2018, 54(3): 222~225
梁涛,姜勇. 旋转真空过滤机转鼓滤网支撑板开裂失效分析[J]. 理化检验-物理分册, 2018, 54(3): 222~225
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘伦, 鲁光沅,刘福润. 钛、钼离子注入对工业纯铁腐蚀性能的影响[J]. 天津师范大学学报(自然科学版),2004,24(3):49-51.
【2】NISHIMURA T,KATAYAMA H,NODA K,et al. Effect of Co and Ni on the corrosion behavior of low alloy steels in wet/dry environments[J]. Corrosion Science,2000,42(9):1611-1621.
【3】段汉桥,魏伯康,林汉同. 我国铸造不锈钢应用现状及发展趋势[J]. 铸造,2002,51(5):268-272.
【4】RYAN M P,WILLIAMS D E,CHATER R J,et al. Why stainless steel corrodes[J]. Nature,2002,415(6873):770.
【5】王勤生. 奥氏体不锈钢波纹管的应力腐蚀研究[D]. 南京:南京工业大学,2004.
【6】陈彩霞,郑杨艳. 316L不锈钢波纹管膨胀节开裂原因分析与预防[J]. 理化检验(物理分册),2015,51(1):55-58.
【2】NISHIMURA T,KATAYAMA H,NODA K,et al. Effect of Co and Ni on the corrosion behavior of low alloy steels in wet/dry environments[J]. Corrosion Science,2000,42(9):1611-1621.
【3】段汉桥,魏伯康,林汉同. 我国铸造不锈钢应用现状及发展趋势[J]. 铸造,2002,51(5):268-272.
【4】RYAN M P,WILLIAMS D E,CHATER R J,et al. Why stainless steel corrodes[J]. Nature,2002,415(6873):770.
【5】王勤生. 奥氏体不锈钢波纹管的应力腐蚀研究[D]. 南京:南京工业大学,2004.
【6】陈彩霞,郑杨艳. 316L不锈钢波纹管膨胀节开裂原因分析与预防[J]. 理化检验(物理分册),2015,51(1):55-58.
相关信息