钢轨轨头浅表面缺陷的空气耦合超声导波检测
Air Coupled Ultrasonic Guided Wave Detection of Shallow Surface Defects of Rail Head
摘 要
针对常规检测方法如压电超声、涡流、漏磁及机器视觉等表面检测方法均无法对钢轨轨头浅表面缺陷进行检测的问题，采用空气耦合超声类瑞利波检测方法，利用回波信号在不同频率、不同缺陷深度下幅值的变化来评估钢轨轨头的浅表面缺陷。通过对空气耦合超声导波检测过程的仿真和试验，证明了该检测方法的可行性和可靠性。
类瑞利波
浅表面缺陷检测
钢轨轨头
air coupled ultrasonic guided wave
Rayleigh like wave
shallow surface defect detection
rail head
Abstract
Due to some shortcomings, the usual piezoelectric ultrasonic, eddy current, magnetic flux leakage, machine vision and other surface inspection methods cannot meet the rail head shallow surface defects detection requirements.In this paper, the air-coupled ultrasonic Rayleigh like wave detection method is used to evaluate the shallow surface defects of the rail head by using the change of the amplitude of the echo signal at different frequencies and different defect depths. Through the simulation and experimental research on the air coupled ultrasonic guided wave detection process, the feasibility and reliability of the detection are proved.
中图分类号 TG115.28 DOI 10.11973/wsjc201803004
所属栏目 试验研究
基金项目 国家自然科学基金资助项目（11464030）；山西省青年科学基金资助项目（2015021086）
收稿日期 2017/11/12
修改稿日期
网络出版日期
作者单位点击查看
备注常俊杰(1964-),女,博士,主要从事超声无损检测的应用技术研究及检测设备的研发等工作
引用该论文: CHANG Junjie,LI Yuanyuan,LI Guangya. Air Coupled Ultrasonic Guided Wave Detection of Shallow Surface Defects of Rail Head[J]. Nondestructive Testing, 2018, 40(3): 14～18
常俊杰,李媛媛,李光亚. 钢轨轨头浅表面缺陷的空气耦合超声导波检测[J]. 无损检测, 2018, 40(3): 14～18
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】米武军. 基于电磁超声表面波的钢轨轨头缺陷检测方法的研究[D].哈尔滨:哈尔滨工业大学,2011.
【2】周一平,严学模,战东平,等. 我国钢轨钢的质量现状及发展趋势[J]. 材料与冶金学报,2004,3(3):161-167.
【3】鲁国堂.超声波探伤技术在钢轨检测中的研究[D].沈阳:沈阳理工大学,2015.
【4】常俊杰,李娟娟.合成孔径算法在混凝土检测中的应用[J]. 无损检测, 2017, 39(4):22-25.
【5】CHANG Junjie, TAKAHIRO, HAYASHI. Development of inspection equipment for bottom edges of rails with guided waves[C]//The 29th Symposium on Ultrasonic Electronics.[S.l.]:[s.n.],2008.
【6】欧阳凯.基于瑞利波的材料表面缺陷深度检测数值研究[D].哈尔滨:哈尔滨工业大学,2014.
【7】赵振宁,吴迪,张博南,等. 薄板中超声类瑞利波传播模态信号分析方法[J]. 无损检测,2017,39(1):10-15.
【8】张博南,霍宇森,吴迪,等. 钛合金薄板Lamb波检测的有限元分析[J]. 无损检测,2015,37(10):64-68.
【9】单振刚,朱继洲,翟兴耀. 无损检验新技术——超声频散曲线分析法研究[J]. 西安交通大学学报,1989(6):113-122.
【10】CHANG Junjie, KATSUMI O. Development of inspection equipment for bottom edges of rails with guided waves[J]. Proceedings of Symposium on Ultrasonic Electronics, 2009, 30(11):18-20.
【11】常俊杰,魏强. 非接触空气耦合超声波钢板探伤的应用研究[J]. 浙江理工大学学报,2015,33(6):102-107.
【12】常俊杰,卢超, 川嶋紘一郎. 非接触空气耦合超声波的材料无损评价与检测[J]. 浙江理工大学学报, 2015, 33(4):532-536.
【2】周一平,严学模,战东平,等. 我国钢轨钢的质量现状及发展趋势[J]. 材料与冶金学报,2004,3(3):161-167.
【3】鲁国堂.超声波探伤技术在钢轨检测中的研究[D].沈阳:沈阳理工大学,2015.
【4】常俊杰,李娟娟.合成孔径算法在混凝土检测中的应用[J]. 无损检测, 2017, 39(4):22-25.
【5】CHANG Junjie, TAKAHIRO, HAYASHI. Development of inspection equipment for bottom edges of rails with guided waves[C]//The 29th Symposium on Ultrasonic Electronics.[S.l.]:[s.n.],2008.
【6】欧阳凯.基于瑞利波的材料表面缺陷深度检测数值研究[D].哈尔滨:哈尔滨工业大学,2014.
【7】赵振宁,吴迪,张博南,等. 薄板中超声类瑞利波传播模态信号分析方法[J]. 无损检测,2017,39(1):10-15.
【8】张博南,霍宇森,吴迪,等. 钛合金薄板Lamb波检测的有限元分析[J]. 无损检测,2015,37(10):64-68.
【9】单振刚,朱继洲,翟兴耀. 无损检验新技术——超声频散曲线分析法研究[J]. 西安交通大学学报,1989(6):113-122.
【10】CHANG Junjie, KATSUMI O. Development of inspection equipment for bottom edges of rails with guided waves[J]. Proceedings of Symposium on Ultrasonic Electronics, 2009, 30(11):18-20.
【11】常俊杰,魏强. 非接触空气耦合超声波钢板探伤的应用研究[J]. 浙江理工大学学报,2015,33(6):102-107.
【12】常俊杰,卢超, 川嶋紘一郎. 非接触空气耦合超声波的材料无损评价与检测[J]. 浙江理工大学学报, 2015, 33(4):532-536.
相关信息