采煤机摇臂惰轮断裂失效分析
Failure Analysis on Fracture of Rocker Idler Gear of a Coal Mining Machine
摘 要
利用宏观检验、磁粉探伤、化学成分分析、金相以及硬度检验等方法对某采煤机摇臂惰轮的疲劳断裂进行了失效分析，确定了疲劳源微裂纹产生的原因。结果表明：惰轮在加工完成后的返修过程中挡圈槽处产生了切削微裂纹，微裂纹在摇臂惰轮工作时的交变载荷作用下不断扩展，最终导致惰轮疲劳断裂。
疲劳断裂
返修
切削裂纹
失效分析
idler gear
fatigue fracture
repair
cutting crack
failure analysis
Abstract
Failure analysis on the fatigue fracture of the rocker idler gear of a coal mining machine was carried out by means of macro inspection, magnetic particle inspection, chemical composition analysis, metallographic test and hardness test, and the cause of fatigue source micro-cracks was determined. The results show that cutting micro-cracks produced at the ring groove of the idler gear during its rework process after machining. The micro-cracks continued to expand under the alternating load of the rocker idler gear, and eventually led to the fatigue fracture of the idler gear.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl201804013
所属栏目 质量控制与失效分析
基金项目
收稿日期 2017/4/17
修改稿日期
网络出版日期
作者单位点击查看
备注王洋(1988-),男,助理工程师,学士,主要从事无损检测及失效分析工作,694112666@qq.com
引用该论文: WANG Yang,WANG Peike,SUN Meng. Failure Analysis on Fracture of Rocker Idler Gear of a Coal Mining Machine[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2018, 54(4): 293～295
王洋,王培科,孙萌. 采煤机摇臂惰轮断裂失效分析[J]. 理化检验－物理分册, 2018, 54(4): 293～295
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】孙智,江利,应鹏展. 失效分析:基础与应用[M]. 北京:机械工业出版社,2005.
【2】夏立芳. 金属热处理工艺学[M]. 哈尔滨:哈尔滨工业大学出版社,2012.
【3】王维发,王星,王培科,等. 采煤机齿轨轮淬火开裂原因分析[J]. 理化检验(物理分册),2016,52(2):146-148.
【4】王培科,王维发,王星,等. 18Cr2Ni4W电渣钢与电炉钢组织与性能[J]. 理化检验(物理分册),2016,52(7):443-445.
【2】夏立芳. 金属热处理工艺学[M]. 哈尔滨:哈尔滨工业大学出版社,2012.
【3】王维发,王星,王培科,等. 采煤机齿轨轮淬火开裂原因分析[J]. 理化检验(物理分册),2016,52(2):146-148.
【4】王培科,王维发,王星,等. 18Cr2Ni4W电渣钢与电炉钢组织与性能[J]. 理化检验(物理分册),2016,52(7):443-445.
相关信息