摘 要
对油田常用玻璃钢管道进行了辐照加速时效试验和自然放置试验,分析了玻璃钢管道的环向拉伸性能和剪切性能;利用声发射仪以及采用断铅的方式测得不同试验周期下管道的声学参数,得出自然环境下和辐照加速时效下玻璃钢管道的力学性能和声学性能规律,运用灰色关联法计算了声学-力学关联度。结果表明,环向拉伸力学性能和断铅信号波速的关联度达到0.7以上。
Abstract
By choosing oilfield as the experimental site,both the irradiation accelerated aging test and the natural aging test of commonly used FRP pipes were carried out. The circumferential tensile properties and shear mechanical properties of FRP pipes were tested. The acoustic parameters of pipes in different test circles were measured by means of lead breaking method combined with acoustic emission equipment, then the mechanical properties and acoustic properties of FRP pipes under natural environment and irradiation accelerated aging are obtained, and the acoustic-mechanical correlation degree was calculated by using grey relational analysis. The results show that the correlation degree between circumferential tensile mechanical properties and the broken lead signal velocity was more than 0.7.
中图分类号 TG115.28 DOI 10.11973/wsjc201805011
所属栏目 试验研究
基金项目
收稿日期 2017/11/22
修改稿日期
网络出版日期
作者单位点击查看
备注盛华(1983-),硕士,主要从事油田特种设备检测与无损检测研究工作
引用该论文: SHENG Hua,CHEN Jianfei,CONG Xueming,QIU Dongquan,WANG Anquan,XIE Keming,ZHOU Xianjun. The Correlation between Acoustic and Mechanical Properties of GFRP Pipes Exposed to Irradiation and Natural Aging[J]. Nondestructive Testing, 2018, 40(5): 46~49
盛华,陈健飞,丛雪明,仇东泉,王安泉,谢珂铭,周先军. 自然时效及受到辐照时玻璃钢管道声学与力学性能的关联性[J]. 无损检测, 2018, 40(5): 46~49
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】SALIBI Z. Performance of reinforced thermosetting resin pipe system in desalination applications:a long-term solution to corrosion-the arabian gulf example[J].Desalination, 2001, 138(1/3):380.
【2】张立国,吕琴.我国玻璃钢复合材料行业发展对玻璃纤维的市场需求[J].玻璃纤维,2010(5):51-56.
【3】刘洋,董事尔,刘倩,等.玻璃钢管的应用现状及展望[J].油气田地面工程,2011,30(4):98-99.
【4】李立民,王丽. 玻璃钢老化问题的试验研究[J].中国建材,2003(3):64-65.
【5】薛志勇.国外玻璃钢老化问题的试验研究[J].上海建材,2002(6):34-35.
【6】孙岩,王登霞,刘亚平,等. 玻璃纤维/溴化环氧乙烯基酯加速老化与自然老化的相关性[J]. 复合材料学报,2014,31(4):916-917.
【7】冯青,李敏,顾轶卓,等.不同湿热条件下碳纤维/环氧复合材料湿热性能实验研究[J]. 复合材料学报,2010,27(6):16-20.
【8】LAN M. Discussion about common problems in artificial accelerated aging test[J].Plastic Technology,2006,34(4):76-80.
【9】冯琰妮,禄芳菊,庞虎平,等. 声发射波在不同复合材料容器表面的衰减特性[J].无损检测,2014,36(12):69-72.
【10】杨瑞峰,马铁华.声发射技术研究及应用进展[J]. 中北大学学报(自然科学版),2006(5):456-461.
【11】邓聚龙.灰色预测与决策[M].武汉:华中科技大学出版社,2002:56-146.
【12】傅立.灰色系统理论及其应用[M].北京:科学技术文献出版杜,1992:26-78.
【13】杨云龙,崔建国. 灰色关联分析在地下水污染评价中的应用[J].压电与声光,2013, 18(2):57-60.
【2】张立国,吕琴.我国玻璃钢复合材料行业发展对玻璃纤维的市场需求[J].玻璃纤维,2010(5):51-56.
【3】刘洋,董事尔,刘倩,等.玻璃钢管的应用现状及展望[J].油气田地面工程,2011,30(4):98-99.
【4】李立民,王丽. 玻璃钢老化问题的试验研究[J].中国建材,2003(3):64-65.
【5】薛志勇.国外玻璃钢老化问题的试验研究[J].上海建材,2002(6):34-35.
【6】孙岩,王登霞,刘亚平,等. 玻璃纤维/溴化环氧乙烯基酯加速老化与自然老化的相关性[J]. 复合材料学报,2014,31(4):916-917.
【7】冯青,李敏,顾轶卓,等.不同湿热条件下碳纤维/环氧复合材料湿热性能实验研究[J]. 复合材料学报,2010,27(6):16-20.
【8】LAN M. Discussion about common problems in artificial accelerated aging test[J].Plastic Technology,2006,34(4):76-80.
【9】冯琰妮,禄芳菊,庞虎平,等. 声发射波在不同复合材料容器表面的衰减特性[J].无损检测,2014,36(12):69-72.
【10】杨瑞峰,马铁华.声发射技术研究及应用进展[J]. 中北大学学报(自然科学版),2006(5):456-461.
【11】邓聚龙.灰色预测与决策[M].武汉:华中科技大学出版社,2002:56-146.
【12】傅立.灰色系统理论及其应用[M].北京:科学技术文献出版杜,1992:26-78.
【13】杨云龙,崔建国. 灰色关联分析在地下水污染评价中的应用[J].压电与声光,2013, 18(2):57-60.
相关信息