304不锈钢防盗罩锈蚀原因分析
Reason Analysis on Tarnishing of 304 Stainless Steel Anti-Theft Cover
摘 要
某304不锈钢防盗罩安装一周后，部分管材表面出现严重锈蚀，采用宏观观察、金相检验、扫描电镜分析、能谱分析、化学成分分析、电化学腐蚀试验、模拟对比试验等方法，对锈蚀原因及机理进行了分析。结果表明：管材表面受到含氯酸性腐蚀物质侵蚀，材料的钝化层遭到破坏，发生了点腐蚀，并逐步发展为严重锈蚀。
防盗罩
锈蚀
钝化层
点腐蚀
304 stainless steel
anti-theft cover
tarnishing
passivation layer
pitting corrosion
Abstract
After one week of installation, the surface of 304 stainless steel pipes of a anti-theft cover suffered serious tarnishing. In order to find out the tarnishing causes and mechanism, the pipe were analyzed by methods of macroscopic observation, metallographic examination, scanning electron microscope analysis, energy spectrum analysis, chemical composition analysis, electrochemical corrosion test and simulated contrast test. The results show that the surface of the pipe was corroded by chlorinated acid, which caused the passivation layer of material to be damaged and pitting corrosion, and it gradually developed to serious tarnishing.
中图分类号 TG115.2 TG172 DOI 10.11973/lhjy-wl201805017
所属栏目 质量控制与失效分析
基金项目
收稿日期 2017/6/17
修改稿日期
网络出版日期
作者单位点击查看
备注魏亮新(1984-),男,工程师,主要从事金属材料及制品质量检验及失效分析工作,weilx-ike@163.com
引用该论文: WEI Liangxin,HUANG Zidong,HONG Zehao,CHEN Liling,XIE Chunyu,LI Jielong. Reason Analysis on Tarnishing of 304 Stainless Steel Anti-Theft Cover[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2018, 54(5): 378～381
魏亮新,黄子东,洪泽浩,陈丽玲,谢春玉,李杰龙. 304不锈钢防盗罩锈蚀原因分析[J]. 理化检验－物理分册, 2018, 54(5): 378～381
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王明政, 邓鑑清,刘胜英,等. 不锈钢护栏锈蚀原因分析[J]. 物理测试,2008,26(3):54-56.
【2】任颂赞,张静江,陈质如,等. 钢铁金相图谱[M]. 上海:上海科学技术文献出版社,2003.
【3】YB/T 5363-2016装饰用焊接不锈钢管[S].
【4】JG/T 3030-1995建筑装饰用用不锈钢焊接管材[S].
【5】孙秋霞,白玉光,贺春林,等. 材料腐蚀与防护[M]. 北京:冶金工业出版社,2001.
【6】姜银方,朱元右,戈晓岚,等. 现代表面工程技术[M]. 北京:化学工业出版社,2005.
【7】张旭,赵景峰,李轶文,等. 输电线用钢芯铝绞线的腐蚀原因分析[J]. 理化检验(物理分册),2016,52(7):484-488.
【8】张培俊,孙全胜. 常减压塔顶部回流泵叶轮腐蚀原因分析[J]. 理化检验(物理分册),2016,52(5):345-349.
【2】任颂赞,张静江,陈质如,等. 钢铁金相图谱[M]. 上海:上海科学技术文献出版社,2003.
【3】YB/T 5363-2016装饰用焊接不锈钢管[S].
【4】JG/T 3030-1995建筑装饰用用不锈钢焊接管材[S].
【5】孙秋霞,白玉光,贺春林,等. 材料腐蚀与防护[M]. 北京:冶金工业出版社,2001.
【6】姜银方,朱元右,戈晓岚,等. 现代表面工程技术[M]. 北京:化学工业出版社,2005.
【7】张旭,赵景峰,李轶文,等. 输电线用钢芯铝绞线的腐蚀原因分析[J]. 理化检验(物理分册),2016,52(7):484-488.
【8】张培俊,孙全胜. 常减压塔顶部回流泵叶轮腐蚀原因分析[J]. 理化检验(物理分册),2016,52(5):345-349.
相关信息