N80钢在含沙和含Cl-溶液中的冲刷腐蚀行为
Erosion-Corrosion Behavior of N80 Steel in the Solution Containing Cl- and Sand
摘 要
采用旋转圆柱电极冲刷腐蚀装置并辅以电化学工作站，结合失重法和电化学测试方法研究了NaCl含量和沙粒粒径对N80钢在含沙、含Cl-液固两相流溶液中的冲刷腐蚀影响规律。结果表明：Cl-在N80钢的冲刷腐蚀过程中发挥了至关重要的作用，在不含NaCl的情况下，试样的腐蚀失重极小；当NaCl质量分数为3.5%时，试样的腐蚀速率最大。N80钢的冲刷腐蚀临界粒径为0.125~0.21 mm。
冲刷腐蚀
NaCl含量
沙粒粒径
电化学试验
N80 steel
erosion-corrosion
NaCl concentration
sand particle size
electrochemical experiment
Abstract
The effect laws of NaCl content and sand particle size on the erosion corrosion of N80 steel in sandy and liquid-solid two-phase flow solutions were studied by a rotating cylindrical electrode scouring apparatus and an electrochemical workstation combined with weight loss method and electrochemical test method. The results showed that Cl- played a crucial role in the erosion corrosion process of N80 steel, in the absence of NaCl, the corrosion loss of the sample was very small; when the NaCl mass fraction was 3.5%, the corrosion rate of the sample was the largest. The critical particle size of N80 steel for scouring corrosion was 0.125-0.21 mm.
中图分类号 TG172.8 DOI 10.11973/fsyfh-201809004
所属栏目 试验研究
基金项目 江苏省油气储运重点实验室开放课题（SCZ1311700006/004）；常州市科技计划项目（CE20160069）
收稿日期 2018/7/3
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: CHEN Hu,ZHOU Hao,WANG Shuli,WANG Minhui,ZHAO Shuhua,CAI Zheng. Erosion-Corrosion Behavior of N80 Steel in the Solution Containing Cl- and Sand[J]. Corrosion & Protection, 2018, 39(9): 668
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】PARSI M,NAJMI K,NAYAFIFARD F,et al. A comprehensive review of solid particle erosion modeling for oil and gas wells and pipelines applications[J]. Journal of Natural Gas Science and Engineering,2014,21:850-873.
【2】张安峰,王跃豫,邢建东. 不锈钢与碳钢在液固两相流中冲刷腐蚀特性的研究[J]. 兵器材料科学与工程,2002,26(2):36-39.
【3】MCLAURY B S,SHIRAZI S A,SHADLY J R,et al. How operating and environmental conditions affect erosion[J]. Corrosion,1999,34:1-11.
【4】李成斌. N80钢在几种压井液中的腐蚀规律的研究[J]. 化学工程与装备,2017(2):160-163.
【5】李桂芝,孙冬柏,俞宏英. 采油管材N80钢在流动介质中的腐蚀行为研究[J]. 腐蚀与防护,2001,22(12):544-545.
【6】李涌泉,余斌高,刘建强,等. N80钢抗液固两相冲刷腐蚀行为的研究[J]. 表面技术,2013,42(6):29-31.
【7】李涌泉,田进. pH值对N80钢固液两相冲刷腐蚀的影响[J]. 表面技术,2013,42(5):37-39.
【8】郑玉贵,姚治铭,龙康,等. 液/固双相流冲刷腐蚀实验装置的研制及动态电化学测试[J]. 腐蚀科学与防护技术,1993,5(4):286-290.
【9】曹楚南. 腐蚀电化学原理[M]. 北京:化学工业出版社,2008:125-129.
【10】赫献超,苏鹏,肖葵,等. 不同NaCl浓度对耐候钢腐蚀产物的影响[J]. 腐蚀与防护,2009,30(5):298-299.
【11】陈长风,路民旭,赵国先,等. 温度、Cl-浓度、Cr元素对N80钢CO2腐蚀电极过程的影响[J]. 金属学报,2003,39(8):849-851.
【12】王树立,龙凤仪,汪敏慧,等. 电化学测量技术在不锈钢点蚀研究中的应用与进展[J]. 腐蚀与防护,2016,37(7):586-591.
【13】NESIE S,PSTLETHWAITS J. Relationship between the structure of disturbed flow and erosion-corrosion[J]. Corrosion,1990,46(11):847-880.
【14】姜胜利,郑玉贵,姚治铭. 不同沙粒粒径多相流中CrMnB堆焊层的损伤行为[J]. 材料保护,2004,37(10):12-14.
【2】张安峰,王跃豫,邢建东. 不锈钢与碳钢在液固两相流中冲刷腐蚀特性的研究[J]. 兵器材料科学与工程,2002,26(2):36-39.
【3】MCLAURY B S,SHIRAZI S A,SHADLY J R,et al. How operating and environmental conditions affect erosion[J]. Corrosion,1999,34:1-11.
【4】李成斌. N80钢在几种压井液中的腐蚀规律的研究[J]. 化学工程与装备,2017(2):160-163.
【5】李桂芝,孙冬柏,俞宏英. 采油管材N80钢在流动介质中的腐蚀行为研究[J]. 腐蚀与防护,2001,22(12):544-545.
【6】李涌泉,余斌高,刘建强,等. N80钢抗液固两相冲刷腐蚀行为的研究[J]. 表面技术,2013,42(6):29-31.
【7】李涌泉,田进. pH值对N80钢固液两相冲刷腐蚀的影响[J]. 表面技术,2013,42(5):37-39.
【8】郑玉贵,姚治铭,龙康,等. 液/固双相流冲刷腐蚀实验装置的研制及动态电化学测试[J]. 腐蚀科学与防护技术,1993,5(4):286-290.
【9】曹楚南. 腐蚀电化学原理[M]. 北京:化学工业出版社,2008:125-129.
【10】赫献超,苏鹏,肖葵,等. 不同NaCl浓度对耐候钢腐蚀产物的影响[J]. 腐蚀与防护,2009,30(5):298-299.
【11】陈长风,路民旭,赵国先,等. 温度、Cl-浓度、Cr元素对N80钢CO2腐蚀电极过程的影响[J]. 金属学报,2003,39(8):849-851.
【12】王树立,龙凤仪,汪敏慧,等. 电化学测量技术在不锈钢点蚀研究中的应用与进展[J]. 腐蚀与防护,2016,37(7):586-591.
【13】NESIE S,PSTLETHWAITS J. Relationship between the structure of disturbed flow and erosion-corrosion[J]. Corrosion,1990,46(11):847-880.
【14】姜胜利,郑玉贵,姚治铭. 不同沙粒粒径多相流中CrMnB堆焊层的损伤行为[J]. 材料保护,2004,37(10):12-14.
相关信息