Effect of Direct Stray Current on Degradation of Epoxy Resin Coating in Immersion
摘 要
利用浸泡试验、电化学测试等技术研究了直流杂散电流对环氧树脂涂层在不同pH和氯离子环境中浸泡失效的影响。结果表明:施加直流干扰会加速环氧树脂涂层失效,在1~5 V直流干扰情况下,随着直流干扰电压的增大,该涂层的吸水量增加,失效更加严重;在直流干扰电压为3 V的中性环境中,该涂层的吸水量最大,但在酸性环境中环氧树脂涂层更容易失效;随着氯离子含量的增大,涂层失效情况加剧,而吸水量呈现先增大后减小的趋势。
Abstract
The effect of direct stray current on the degradation of epoxy resin coating in the environment with different pH values and chloride ion concentrations was studied by immersion test and electrochemical testing. The results show that the degradation of epoxy resin coating in the presence of direct current was accelerated. As the direct current (DC) interference voltage increased in the range of 1-5 V, the water absorption of the coating increased and the degradation was more serious. At DC interference voltage of 3 V the coating got the largest water absorption in neutral environment, but the degradation of the coating failed more easily in acidic environment. With the increase of chloride ion concentration the degradation of the coating became more serious and the water absorption increased first and then decreased.
中图分类号 TG172 DOI 10.11973/fsyfh-201810007
所属栏目 环氧树脂涂层
基金项目
收稿日期 2017/7/15
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: CUI Yanyu,WANG Yujun,DING Qingmiao. Effect of Direct Stray Current on Degradation of Epoxy Resin Coating in Immersion[J]. Corrosion & Protection, 2018, 39(10): 770
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】曹楚南,张鉴清. 电化学阻抗谱导论[M]. 北京:科学出版社,2002:154-166.
【2】BIERWAGEN G P,HE L,LI J. Study of a new accelerated evaluation method for coating corrosion resistance-thermal cycling test[J]. Progress in Organic Coatings,2000,39(1):67-78.
【3】WEI Y H,ZHANG L X,KE W. Comparison of the degradation behavior of fusion-bonded epoxy powder coating systems under flowing and static immersion[J]. Corrosion Science,2006,48(6):1449-1461.
【4】刘旭文,熊金平,曹京宜,等. EIS法研究3种配套涂层体系的电化学腐蚀[J]. 化工学报,2008,59(3):659-664.
【5】LEGGHE E,ARAGON E,BELEC L,et al. Correlation between water diffusion and adhesion loss:study of an epoxy primer on steel[J]. Progress in Organic Coatings,2009,66(3):276-280.
【6】方华,彭立涛,华大力. 金属涂层与有机涂层在5% NaCl溶液中的腐蚀特征[J]. 材料保护,2010,43(7):55-57.
【7】杨海,陆卫中,李京,等. Na+在环氧粉末涂层/Q235钢界面的传输行为[J]. 中国腐蚀与防护学报,2013,33(4):266-270.
【8】肖述辉. 杂散电流对长输管道腐蚀影响的研究[D]. 西安:西安石油大学,2014:9-11.
【9】张明,余建飞,张予,等. 低强度直流杂散电流对Q235钢在SO2大气中腐蚀行为的影响[J]. 材料保护,2015,48(9):18-21.
【10】闫爱军,陈沂,冯拉俊,等. 几种接地网材料在土壤中的腐蚀特性研究[J]. 腐蚀科学与防护技术,2010,22(3):197-199.
【11】谭铮辉,朱志平,裴锋,等. 直流杂散电流对不同含水率土壤中接地网材料腐蚀特性的影响[J]. 腐蚀科学与防护技术,2013,25(3):207-212.
【12】张玉星,杜艳霞,路民旭. 动态直流杂散电流干扰下埋地管道的腐蚀行为[J]. 腐蚀与防护,2013,34(9):771-774.
【13】杨超,崔淦,李自力,等. 直流杂散电流对X65钢表面形态及电化学行为的影响[J]. 材料保护,2016,29(10):18-22.
【14】杨超,张成斌,李自力,等. 直流杂散电流对X65钢腐蚀行为的影响[J]. 腐蚀与防护,2016,37(11):873-875.
【2】BIERWAGEN G P,HE L,LI J. Study of a new accelerated evaluation method for coating corrosion resistance-thermal cycling test[J]. Progress in Organic Coatings,2000,39(1):67-78.
【3】WEI Y H,ZHANG L X,KE W. Comparison of the degradation behavior of fusion-bonded epoxy powder coating systems under flowing and static immersion[J]. Corrosion Science,2006,48(6):1449-1461.
【4】刘旭文,熊金平,曹京宜,等. EIS法研究3种配套涂层体系的电化学腐蚀[J]. 化工学报,2008,59(3):659-664.
【5】LEGGHE E,ARAGON E,BELEC L,et al. Correlation between water diffusion and adhesion loss:study of an epoxy primer on steel[J]. Progress in Organic Coatings,2009,66(3):276-280.
【6】方华,彭立涛,华大力. 金属涂层与有机涂层在5% NaCl溶液中的腐蚀特征[J]. 材料保护,2010,43(7):55-57.
【7】杨海,陆卫中,李京,等. Na+在环氧粉末涂层/Q235钢界面的传输行为[J]. 中国腐蚀与防护学报,2013,33(4):266-270.
【8】肖述辉. 杂散电流对长输管道腐蚀影响的研究[D]. 西安:西安石油大学,2014:9-11.
【9】张明,余建飞,张予,等. 低强度直流杂散电流对Q235钢在SO2大气中腐蚀行为的影响[J]. 材料保护,2015,48(9):18-21.
【10】闫爱军,陈沂,冯拉俊,等. 几种接地网材料在土壤中的腐蚀特性研究[J]. 腐蚀科学与防护技术,2010,22(3):197-199.
【11】谭铮辉,朱志平,裴锋,等. 直流杂散电流对不同含水率土壤中接地网材料腐蚀特性的影响[J]. 腐蚀科学与防护技术,2013,25(3):207-212.
【12】张玉星,杜艳霞,路民旭. 动态直流杂散电流干扰下埋地管道的腐蚀行为[J]. 腐蚀与防护,2013,34(9):771-774.
【13】杨超,崔淦,李自力,等. 直流杂散电流对X65钢表面形态及电化学行为的影响[J]. 材料保护,2016,29(10):18-22.
【14】杨超,张成斌,李自力,等. 直流杂散电流对X65钢腐蚀行为的影响[J]. 腐蚀与防护,2016,37(11):873-875.
相关信息