钢制管道熔结环氧树脂防腐蚀涂层技术标准的对比分析
Comparative Analysis on Technical Standards in Fusion Bonded Epoxy Anticorrosion Coating of Steel Pipe
摘 要
从涂层结构、原材料性能检验、涂层性能检验三个方面，对国内外熔结环氧树脂（FBE）防腐蚀涂层技术标准进行了比对分析，并在此基础上对今后国内FBE防腐蚀涂层相关技术标准修订工作提出了参考建议。
防腐蚀涂层
技术标准
比对分析
fusion bonded epoxy resin
anticorrosion coating
technical standard
comparative analysis
Abstract
Comparative analysis on worldwide technical standards of fusion bonded epoxy (FBE) anticorrosion coating is conducted from three aspects of coating structure, raw material performance testing and coating performance testing. Some advice is proposed in the revision of domestic FBE anticorrosion coating related technical standard on the basis of previous analysis.
中图分类号 TG174.4 DOI 10.11973/fsyfh-201810009
所属栏目 环氧树脂涂层
基金项目
收稿日期 2017/12/26
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: HAN Bing,LIU Jinxia,LI Aigui. Comparative Analysis on Technical Standards in Fusion Bonded Epoxy Anticorrosion Coating of Steel Pipe[J]. Corrosion & Protection, 2018, 39(10): 782
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Canadian Standards Association. Plant-applied external coatings for steel pipe:CSA Z245.20 Series-2014[S]. Mississauga,Ontario,Canada:CSA,2015.
【2】International Organization for Standardization. Petroleum and natural gas industries-external coatings for buried or submerged pipelines used in pipeline transportation systems-part 2:Single layer fusion-bonded epoxy coatings:ISO 21809-2:2014[S]. Geneva:ISO,2014.
【3】National Association of Corrosion Engineer. Application,performance,and quality control of plant-applied,fusion-bonded epoxy external pipe coating:NACE SP03942-2013[S]. Houston,Texas:NACE,2013.
【4】American Water Works Association. Fusion-bonded epoxy coatings and linings for steel water pipe and fittings:AWWA C213-2015[S]. Denver:AWWA,2015.
【5】American Petroleum Institute. External fusion bounded epoxy coating of line pipe:API 5L9-2001(R2010)[S]. Washington D.C:API,2015.
【6】张瑛,焦如义. 钢制管道熔结环氧粉末外涂层技术规范:SY/T 0315-2013[S]. 北京:石油工业出版社,2013.
【7】张其滨,刘金霞,赫连建峰,等. 钢制管道熔结环氧粉末内防腐层技术标准:SY/T 0442-2010[S]. 北京:石油工业出版社,2010.
【8】韩冰,李爱贵,那骥宇,等. 卡尔费休库仑法测定熔结环氧粉末水分含量[J]. 化学试剂,2017,39(10):1080-1082.
【9】International Organization for Standardization. Plastics-determination of water content:ISO 15512:2014[S]. Geneva:ISO,2014.
【10】IVANOVA P G,ANEVA Z V. Assessment and assurance of quality in water measurement by coulometric Karl Fischer titration of petroleum products[J]. Accreditation and Quality Assurance,2006,10(10):543-549.
【11】KRASUCKA D M,KOS K,CYBULSKI W A,et al. Karl Fisher determination of residual moisture in veterinary vaccines-practical implementation in market monitoring[J]. Acta Poloniae Pharmaceutica,2012,69(6):1364-1367.
【12】YAN M,YU M,WEI G. Determination of moisture content in thioalcohols by Karl Fischer coulometry[J]. Asian Journal Chemistry,2011,23(1):135-137.
【13】British Standards Institution. Coating powders-part6:determination of gel time of thermosetting coating powders at a given temperature:BS EN ISO8130-6:2010[S]. London:BSI Group,2010.
【14】American Society for Testing and Materials. Standard test method for apparent shear strength of single-lap-joint adhesively bonded metal specimens by tension loading(metal-to-metal):ASTM D1002-2010[S]. West Conshohocken,PA:ASTM International,2010.
【15】American Society for Testing and Materials. Standard test method for pull-off strength of coatings using portable adhesion testers:ASTM D4541-2017[S]. West Conshohocken,PA:ASTM International,2017.
【16】BRASHER D M,NURSE J T. Electrical measurements of immersed paint coatings on metal. Ⅱ. Effect of osmotic pressure and ionic concentration of solution on paint breakdown[J]. Journal of Chemical Technology & Biotechnology,2010,9(2):96-106.
【17】LEGGHE E,ARAGON E,BELEC L,et al. Correlation between water diffusion and adhesion loss:study of an epoxy primer on steel[J]. Progress in Organic Coating,2009,66(3):276-280.
【18】杨海,陆卫中,李京,等. 环氧粉末涂层在1.5 mol/L NaCl溶液中的失效行为[J]. 中国腐蚀与防护学报,2014,34(4):382-388.
【19】常永懿,王向明,许传新,等. 低温固化熔结环氧粉末涂层中水对涂层玻璃化转变温度的影响[J]. 中国高新技术企业,2010,163(28):54-55.
【20】曾纬丽,王浩江,李思钰,等. 塑料吸水性的测定:GB/T 1034-2008[S]. 北京:中国标准出版社,2008.
【21】American Society for Testing and Materials. Standard test methods for abrasion resistance of organic coatings by falling abrasive:ASTM D968-2010[S]. West Conshohocken,PA:ASTM International,2010.
【22】American Society for Testing and Materials. Standard test method for abrasion resistance of organic coatings by the taber abraser:ASTM D4060-2014[S]. West Conshohocken,PA:ASTM International,2014.
【23】International Organization for Standardization. Paints and varnishes-Buchholz indentation test:ISO 2815:2003[S]. Geneva:ISO,2003.
【2】International Organization for Standardization. Petroleum and natural gas industries-external coatings for buried or submerged pipelines used in pipeline transportation systems-part 2:Single layer fusion-bonded epoxy coatings:ISO 21809-2:2014[S]. Geneva:ISO,2014.
【3】National Association of Corrosion Engineer. Application,performance,and quality control of plant-applied,fusion-bonded epoxy external pipe coating:NACE SP03942-2013[S]. Houston,Texas:NACE,2013.
【4】American Water Works Association. Fusion-bonded epoxy coatings and linings for steel water pipe and fittings:AWWA C213-2015[S]. Denver:AWWA,2015.
【5】American Petroleum Institute. External fusion bounded epoxy coating of line pipe:API 5L9-2001(R2010)[S]. Washington D.C:API,2015.
【6】张瑛,焦如义. 钢制管道熔结环氧粉末外涂层技术规范:SY/T 0315-2013[S]. 北京:石油工业出版社,2013.
【7】张其滨,刘金霞,赫连建峰,等. 钢制管道熔结环氧粉末内防腐层技术标准:SY/T 0442-2010[S]. 北京:石油工业出版社,2010.
【8】韩冰,李爱贵,那骥宇,等. 卡尔费休库仑法测定熔结环氧粉末水分含量[J]. 化学试剂,2017,39(10):1080-1082.
【9】International Organization for Standardization. Plastics-determination of water content:ISO 15512:2014[S]. Geneva:ISO,2014.
【10】IVANOVA P G,ANEVA Z V. Assessment and assurance of quality in water measurement by coulometric Karl Fischer titration of petroleum products[J]. Accreditation and Quality Assurance,2006,10(10):543-549.
【11】KRASUCKA D M,KOS K,CYBULSKI W A,et al. Karl Fisher determination of residual moisture in veterinary vaccines-practical implementation in market monitoring[J]. Acta Poloniae Pharmaceutica,2012,69(6):1364-1367.
【12】YAN M,YU M,WEI G. Determination of moisture content in thioalcohols by Karl Fischer coulometry[J]. Asian Journal Chemistry,2011,23(1):135-137.
【13】British Standards Institution. Coating powders-part6:determination of gel time of thermosetting coating powders at a given temperature:BS EN ISO8130-6:2010[S]. London:BSI Group,2010.
【14】American Society for Testing and Materials. Standard test method for apparent shear strength of single-lap-joint adhesively bonded metal specimens by tension loading(metal-to-metal):ASTM D1002-2010[S]. West Conshohocken,PA:ASTM International,2010.
【15】American Society for Testing and Materials. Standard test method for pull-off strength of coatings using portable adhesion testers:ASTM D4541-2017[S]. West Conshohocken,PA:ASTM International,2017.
【16】BRASHER D M,NURSE J T. Electrical measurements of immersed paint coatings on metal. Ⅱ. Effect of osmotic pressure and ionic concentration of solution on paint breakdown[J]. Journal of Chemical Technology & Biotechnology,2010,9(2):96-106.
【17】LEGGHE E,ARAGON E,BELEC L,et al. Correlation between water diffusion and adhesion loss:study of an epoxy primer on steel[J]. Progress in Organic Coating,2009,66(3):276-280.
【18】杨海,陆卫中,李京,等. 环氧粉末涂层在1.5 mol/L NaCl溶液中的失效行为[J]. 中国腐蚀与防护学报,2014,34(4):382-388.
【19】常永懿,王向明,许传新,等. 低温固化熔结环氧粉末涂层中水对涂层玻璃化转变温度的影响[J]. 中国高新技术企业,2010,163(28):54-55.
【20】曾纬丽,王浩江,李思钰,等. 塑料吸水性的测定:GB/T 1034-2008[S]. 北京:中国标准出版社,2008.
【21】American Society for Testing and Materials. Standard test methods for abrasion resistance of organic coatings by falling abrasive:ASTM D968-2010[S]. West Conshohocken,PA:ASTM International,2010.
【22】American Society for Testing and Materials. Standard test method for abrasion resistance of organic coatings by the taber abraser:ASTM D4060-2014[S]. West Conshohocken,PA:ASTM International,2014.
【23】International Organization for Standardization. Paints and varnishes-Buchholz indentation test:ISO 2815:2003[S]. Geneva:ISO,2003.
相关信息