Effect of Glass Content on Properties of Low-Temperature Sintered Borosilicate Glass-AlN Ceramic Composite
摘 要
以组成(质量分数)为15%B2O3-45%MgO-35%SiO2-5% ZrO2(BMSZ)的玻璃粉体和AlN粉体为原料,采用常压烧结工艺制备了不同玻璃含量(55%~80%,质量分数,下同)的BMSZ玻璃-AlN陶瓷复合材料,研究了玻璃含量对复合材料烧结性能、热学性能、介电性能和力学性能的影响。结果表明:在AlN粉体中添加玻璃粉体后,在775~875℃烧结即可得到致密的复合材料;玻璃含量的适量增加能够促进烧结致密化,当玻璃含量超过70%后,其促进烧结致密的作用开始减弱,并会恶化复合材料的热导率与抗弯强度,但适当降低了复合材料的介电损耗;当玻璃含量为70%时,在825℃烧结所得复合材料的结构致密,综合性能最佳,体积密度为2.84 g·cm-3,热导率为9.12 W·m-1·K-1,相对介电常数为7.65,介电损耗角正切为1.24×10-3,抗弯强度为174.88 MPa。
Abstract
With glass powder composed of 15wt%B2O3-45wt%MgO-35wt%SiO2-5wt%ZrO2 (BMSZ) and AlN powder as raw materials, BMSZ glass-AlN ceramic composites containing different glass content (55wt%-80wt%) were prepared by conventional pressureless sintering. The effects of glass content on the sintering performance, thermal properties, dielectric properties and mechanical properties were discussed. The results show that after adding the glass powder into the AlN powder and then being sintered at 775-875℃, the dense composites were obtained. Increasing the glass content properly improved the sintering densification. When the glass content exceeded 70wt%, the addition of glass weakened its role to promote the sintering densification, and deteriorated the thermal conductivity and bending strength of the composite, but appropriately reduced the dielectric loss of the composite. When the glass content was 70wt%, the composite sintered at 825℃ had a dense structure and obtained the best comprehensive performance, with the bulk density of 2.84 g·cm-3, the relative thermal conductivity of 9.12 W·m-1·K-1, the dielectric constant of 7.65, the dielectric loss angle tangent of 1.24×10-3, and the bending strength of 174.88 MPa.
中图分类号 TQ174.75 DOI 10.11973/jxgccl201810009
所属栏目 材料性能及应用
基金项目
收稿日期 2018/3/5
修改稿日期 2018/9/5
网络出版日期
作者单位点击查看
备注徐健丰(1978-),男,浙江杭州人,讲师,硕士
引用该论文: XU Jianfeng. Effect of Glass Content on Properties of Low-Temperature Sintered Borosilicate Glass-AlN Ceramic Composite[J]. Materials for mechancial engineering, 2018, 42(10): 46~50
徐健丰. 玻璃含量对低温烧结硼硅酸盐玻璃-AlN陶瓷复合材料性能的影响[J]. 机械工程材料, 2018, 42(10): 46~50
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】贾程棡, 钟朝位, 周晓华, 等. 低温共烧陶瓷用硼硅酸盐玻璃的研究进展[J]. 电子元件与材料, 2006, 25(9):8-11.
【2】EL-KHESHEN A A. Effect of alumina addition on properties of glass/ceramic composite[J]. British Ceramic Transactions, 2003, 102(5):205-209.
【3】ZAWRAH M F, HAMZAWY E M A. Effect of cristobalite formation on sinterability, microstructure and properties of glass/ceramic composites[J]. Ceramics International, 2002, 28(2):123-130.
【4】TUMMALA R R. Ceramics in microelectronic packaging[J]. American Ceramic Society Bulletin, 1988, 67(4):78-85.
【5】SHIMADE Y, UTSUMI K, SUZUKI M, et al. Low firing temperature multilayer glass ceramic (MGC) substrate[J]. NEC Research and Development, 1994, 75:8-15.
【6】陈兴宇. 硼硅铅玻璃/氧化铝的烧结特性与性能研究[D]. 长沙:国防科学技术大学, 2008:78-95.
【7】陈强, 谭敦强, 余方新, 等. 功率型LED散热基板的研究进展[J]. 材料导报, 2009, 23(12):61-64.
【8】祝大同. 散热基板市场增大对PCB产业发展的驱动[J]. 印制电路信息, 2011(2):6-11.
【9】李华平, 柴广跃, 彭文达, 等. 大功率LED的封装及其散热基板研究[J]. 半导体光电, 2007, 28(1):47-50.
【10】陈焕庭, 吕毅军, 陈忠, 等. 大功率AlGaInP红光LED散热基板热分析[J]. 光学学报, 2009, 29(3):805-810.
【11】中国硅酸盐学会. 陶瓷(硅酸盐)指南'96:中国硅酸盐学会手册[M]. 北京:中国建材工业出版社, 1996:58-62.
【12】TUMMALA R R. Ceramic and glass-ceramic packaging in the 1990s[J]. Journal of the American Ceramic Society, 1991, 74(5):895-908.
【13】SLACK G A, TANZILLI R A, POHL R O, et al. The intrinsic thermal conductivity of AIN[J]. Journal of Physics and Chemistry of Solids, 1987, 48(7):641-647.
【14】BAIK Y, DREW R A L. Aluminum nitride:Processing and applications[J]. Key Engineering Materials, 1996, 122/123/124:553-570.
【15】SHEPPARD L M. Aluminum nitride:A versatile but challenging material[J]. American Ceramic Society Bulletin, 1990, 69(11):70-82.
【16】张擎雪, 雒晓军, 李文兰, 等. 一种低温烧结氮化铝基复相材料及其制备方法:02110651.7[P]. 2002-08-14.
【17】赵宏生, 高廿子. 氮化铝/硼硅酸盐玻璃低温共烧陶瓷基板材料及其制备方法:101100367A[P]. 2008-01-09.
【18】杨德安, 袁利娜, 申娜娜. 多元硼硅酸盐玻璃+氮化铝低温共烧陶瓷材料及其制备方法:103553558A[P]. 2014-02-05.
【19】王焕平, 徐时清, 杨清华, 等. 一种氮化铝基玻璃陶瓷及其制备方法:103395993A[P]. 2013-11-20.
【20】张文娟, 杨清华, 方一航, 等. CBZS/AlN玻璃-陶瓷的低温烧结及性能研究[J]. 陶瓷学报, 2013, 34(1):11-16.
【21】张文娟. 氮化铝基复合基板材料的低温烧结及其性能研究[D]. 杭州:中国计量学院, 2013:45-67.
【22】胡一晨, 徐庭, 王雯, 等. CaO-ZnO-B2O3-SiO2玻璃/Al2O3低温共烧复合陶瓷基板研究[J]. 玻璃与搪瓷, 2010, 18(6):1-5.
【23】张擎雪. 高密度封装用低温烧结AlN玻璃复合材料的制备与性能研究[D]. 上海:中国科学院上海硅酸盐研究所, 2002:45-67.
【2】EL-KHESHEN A A. Effect of alumina addition on properties of glass/ceramic composite[J]. British Ceramic Transactions, 2003, 102(5):205-209.
【3】ZAWRAH M F, HAMZAWY E M A. Effect of cristobalite formation on sinterability, microstructure and properties of glass/ceramic composites[J]. Ceramics International, 2002, 28(2):123-130.
【4】TUMMALA R R. Ceramics in microelectronic packaging[J]. American Ceramic Society Bulletin, 1988, 67(4):78-85.
【5】SHIMADE Y, UTSUMI K, SUZUKI M, et al. Low firing temperature multilayer glass ceramic (MGC) substrate[J]. NEC Research and Development, 1994, 75:8-15.
【6】陈兴宇. 硼硅铅玻璃/氧化铝的烧结特性与性能研究[D]. 长沙:国防科学技术大学, 2008:78-95.
【7】陈强, 谭敦强, 余方新, 等. 功率型LED散热基板的研究进展[J]. 材料导报, 2009, 23(12):61-64.
【8】祝大同. 散热基板市场增大对PCB产业发展的驱动[J]. 印制电路信息, 2011(2):6-11.
【9】李华平, 柴广跃, 彭文达, 等. 大功率LED的封装及其散热基板研究[J]. 半导体光电, 2007, 28(1):47-50.
【10】陈焕庭, 吕毅军, 陈忠, 等. 大功率AlGaInP红光LED散热基板热分析[J]. 光学学报, 2009, 29(3):805-810.
【11】中国硅酸盐学会. 陶瓷(硅酸盐)指南'96:中国硅酸盐学会手册[M]. 北京:中国建材工业出版社, 1996:58-62.
【12】TUMMALA R R. Ceramic and glass-ceramic packaging in the 1990s[J]. Journal of the American Ceramic Society, 1991, 74(5):895-908.
【13】SLACK G A, TANZILLI R A, POHL R O, et al. The intrinsic thermal conductivity of AIN[J]. Journal of Physics and Chemistry of Solids, 1987, 48(7):641-647.
【14】BAIK Y, DREW R A L. Aluminum nitride:Processing and applications[J]. Key Engineering Materials, 1996, 122/123/124:553-570.
【15】SHEPPARD L M. Aluminum nitride:A versatile but challenging material[J]. American Ceramic Society Bulletin, 1990, 69(11):70-82.
【16】张擎雪, 雒晓军, 李文兰, 等. 一种低温烧结氮化铝基复相材料及其制备方法:02110651.7[P]. 2002-08-14.
【17】赵宏生, 高廿子. 氮化铝/硼硅酸盐玻璃低温共烧陶瓷基板材料及其制备方法:101100367A[P]. 2008-01-09.
【18】杨德安, 袁利娜, 申娜娜. 多元硼硅酸盐玻璃+氮化铝低温共烧陶瓷材料及其制备方法:103553558A[P]. 2014-02-05.
【19】王焕平, 徐时清, 杨清华, 等. 一种氮化铝基玻璃陶瓷及其制备方法:103395993A[P]. 2013-11-20.
【20】张文娟, 杨清华, 方一航, 等. CBZS/AlN玻璃-陶瓷的低温烧结及性能研究[J]. 陶瓷学报, 2013, 34(1):11-16.
【21】张文娟. 氮化铝基复合基板材料的低温烧结及其性能研究[D]. 杭州:中国计量学院, 2013:45-67.
【22】胡一晨, 徐庭, 王雯, 等. CaO-ZnO-B2O3-SiO2玻璃/Al2O3低温共烧复合陶瓷基板研究[J]. 玻璃与搪瓷, 2010, 18(6):1-5.
【23】张擎雪. 高密度封装用低温烧结AlN玻璃复合材料的制备与性能研究[D]. 上海:中国科学院上海硅酸盐研究所, 2002:45-67.
相关信息