高矿化度油田污水处理系统的腐蚀因素分析及治理措施
Corrosion Factor Analysis and Treatment Measures of High Mineralization Oilfield Sewage Treatment System
摘 要
西部某高矿化度油田污水处理装置的设备和管线发生多次腐蚀，综合分析了污水水质、腐蚀监测数据、腐蚀产物成分，结合现场缓蚀剂使用情况研究了腐蚀原因。结果表明：系统不密闭，导致环境中的氧进入系统，并且污水腐蚀性较强，加速了管道和设备的腐蚀；此外，系统中缓蚀剂加注点设计不合理且加入量不足，导致缓蚀剂不能有效减缓系统的腐蚀。针对这些原因提出了治理措施。
污水处理装置
腐蚀
溶解氧
缓蚀剂
high mineralization degree
sewage treatment system
corrosion
dissolved oxygen
corrosion inhibitor
Abstract
The equipment and pipelines of a high salinity oilfield sewage treatment plant in the west corroded repeatedly. The causes of corrosion were studied by comprehensive analysis of sewage water quality, corrosion monitoring data, corrosion product composition, and the use of on-site corrosion inhibitors. The results showed that the system was not closed, causing oxygen in the environment to enter the system, and the sewage was highly corrosive, which accelerated the corrosion of pipes and equipment. In addition, the design of the corrosion inhibitor filling point in the system was unreasonable and the addition amount was insufficient, so that the corrosion inhibitor could not effectively alleviate the corrosion of the system. Governance measures were proposed for these reasons.
中图分类号 TG17 DOI 10.11973/fsyfh-201811016
所属栏目 失效分析
基金项目
收稿日期 2017/7/3
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: LOU Liangjie,XU Zhongping,LI Aigui,KONG Xiangang. Corrosion Factor Analysis and Treatment Measures of High Mineralization Oilfield Sewage Treatment System[J]. Corrosion & Protection, 2018, 39(11): 892
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张统. 污水处理工艺及工程方案设计[M]. 北京:中国建筑工业出版社,2011,11:77-81.
【2】高俊发. 污水处理厂工艺设计手册[M]. 北京:化学工业出版社,2003,10:51-52.
【3】严春者. 悬浮污泥过滤法处理油田采出水技术研究及应用[D]. 山东:中国海洋大学,2016:26-29.
【4】陈新民. 滨二污水站处理系统腐蚀成因分析及对策研究[J]. 油田化学,2009,26(1):46-50.
【5】张新丽,赵朝成. 广利联合站污水处理系统的腐蚀与防护[J]. 油气田环境保护,2004,11(1):45-47.
【6】曹怀山,姜红. 纯化油田回注污水腐蚀原因分析及治理措施[J]. 石油化工腐蚀与防护,2005,22(6):33-40.
【7】汪刚跃,张守献,徐鹏,等. 攀家站污水腐蚀超标原因分析及控制措施研究[J]. 石油天然气学报,2013,35(2):146-148.
【8】苏焕荣,刘鸿升. 玻璃钢管道在胜利油田采油工程中的应用[J]. 石油工程建设,1997,23(2):30-33.
【9】万泰力,刘可金,门秀华. 大庆油田采油污水腐蚀因素分析[J]. 油田底面工程,2008,27(2):29-30.
【10】YOON-SEOK C,SRDJAN N. Determining the corrosive potential of CO2 transport pipline in high pCO2-water environments[J]. International Journal of Greenhouse Gas Control,2011,18(5):788-797.
【11】朱西柱,蒋天昊,李立标,等. 溶解性气体对油井腐蚀速度影响分析[J]. 石油化工应用,2011,30(40):77-80.
【12】曲虎,刘静,马梓涵,等. 油田污水腐蚀影响因素研究[J]. 应用化学,2011,40(6):1062-1065.
【13】龙媛媛,张春茂,王遂平,等. 郑408火烧驱油注气井油套管腐蚀安全评估与防护[J]. 腐蚀科学与防护技术,2008,20(5):386-387.
【14】SARIN P,SNOEYINK V L,LYTLE D A,et al. Iron corrosion scales:model for scale growth, iron release,and colored water formation[J]. J Environ Engin,2004,130:364-373.
【15】陈德胜,龙媛媛,刘璐,等. 胜利油田孤六联合站污水腐蚀与防护措施[J]. 腐蚀与防护,2010,31(10):800-802.
【16】白心德. 材料腐蚀与控制[M]. 北京:清华大学出版社,2005.
【17】张丽平,李家宇,杨鹏. 大路沟一区污水腐蚀结垢机理及防治技术[J]. 油气田地面工程,2012,31(7):29.
【2】高俊发. 污水处理厂工艺设计手册[M]. 北京:化学工业出版社,2003,10:51-52.
【3】严春者. 悬浮污泥过滤法处理油田采出水技术研究及应用[D]. 山东:中国海洋大学,2016:26-29.
【4】陈新民. 滨二污水站处理系统腐蚀成因分析及对策研究[J]. 油田化学,2009,26(1):46-50.
【5】张新丽,赵朝成. 广利联合站污水处理系统的腐蚀与防护[J]. 油气田环境保护,2004,11(1):45-47.
【6】曹怀山,姜红. 纯化油田回注污水腐蚀原因分析及治理措施[J]. 石油化工腐蚀与防护,2005,22(6):33-40.
【7】汪刚跃,张守献,徐鹏,等. 攀家站污水腐蚀超标原因分析及控制措施研究[J]. 石油天然气学报,2013,35(2):146-148.
【8】苏焕荣,刘鸿升. 玻璃钢管道在胜利油田采油工程中的应用[J]. 石油工程建设,1997,23(2):30-33.
【9】万泰力,刘可金,门秀华. 大庆油田采油污水腐蚀因素分析[J]. 油田底面工程,2008,27(2):29-30.
【10】YOON-SEOK C,SRDJAN N. Determining the corrosive potential of CO2 transport pipline in high pCO2-water environments[J]. International Journal of Greenhouse Gas Control,2011,18(5):788-797.
【11】朱西柱,蒋天昊,李立标,等. 溶解性气体对油井腐蚀速度影响分析[J]. 石油化工应用,2011,30(40):77-80.
【12】曲虎,刘静,马梓涵,等. 油田污水腐蚀影响因素研究[J]. 应用化学,2011,40(6):1062-1065.
【13】龙媛媛,张春茂,王遂平,等. 郑408火烧驱油注气井油套管腐蚀安全评估与防护[J]. 腐蚀科学与防护技术,2008,20(5):386-387.
【14】SARIN P,SNOEYINK V L,LYTLE D A,et al. Iron corrosion scales:model for scale growth, iron release,and colored water formation[J]. J Environ Engin,2004,130:364-373.
【15】陈德胜,龙媛媛,刘璐,等. 胜利油田孤六联合站污水腐蚀与防护措施[J]. 腐蚀与防护,2010,31(10):800-802.
【16】白心德. 材料腐蚀与控制[M]. 北京:清华大学出版社,2005.
【17】张丽平,李家宇,杨鹏. 大路沟一区污水腐蚀结垢机理及防治技术[J]. 油气田地面工程,2012,31(7):29.
相关信息