两种典型聚合物基固体自润滑材料的摩擦磨损性能
Friction and Wear Properties of Two Kinds of Typical Polymer Based Solid Self-Lubrication Materials
摘 要
对两种典型的聚合物基固体自润滑材料聚四氟乙烯（PTFE）和聚酰亚胺（PI）的热稳定性和摩擦磨损性能进行了测试，并用扫描电子显微镜（SEM）观察了试验后的摩擦表面形貌，用X射线能量分散谱仪（EDS）分析了试验后摩擦表面的特征元素。结果表明：两种聚合物基固体自润滑材料均具有良好的热稳定性，聚四氟乙烯基固体自润滑材料的润滑性能和耐摩擦磨损性能要优于聚酰亚胺基固体自润滑材料的。
固体自润滑材料
摩擦磨损性能
热稳定性
润滑机理
polymer
solid self-lubrication material
friction and wear property
thermal stability
lubrication mechanism
Abstract
The thermal stability and friction and wear properties of two typical polymer based solid self-lubricating materials, polytetrafluoroethylene (PTFE) and polyimide (PI), were tested. The friction surface morphology after test was observed by scanning electron microscopy (SEM), and the characteristic elements on the friction surface after test were analyzed by X-ray energy dispersive spectroscopy (EDS). The results show that the two polymer based solid self-lubricating materials both have good thermal stability, and the lubricating properties and friction and wear resistance of the PTFE-based solid self-lubricating material are better than those of the PI-based solid self-lubricating material.
中图分类号 O631.2 DOI 10.11973/lhjy-wl201812005
所属栏目 试验与研究
基金项目
收稿日期 2017/11/1
修改稿日期
网络出版日期
作者单位点击查看
备注刘泊天(1986-),女,工程师,硕士,主要从事航天材料研发与评价工作
引用该论文: LIU Botian,GAO Hong,ZHENG Jun,ZHANG Yanshuai,XING Yan. Friction and Wear Properties of Two Kinds of Typical Polymer Based Solid Self-Lubrication Materials[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2018, 54(12): 882～886
刘泊天,高鸿,郑军,张延帅,邢焰. 两种典型聚合物基固体自润滑材料的摩擦磨损性能[J]. 理化检验－物理分册, 2018, 54(12): 882～886
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘维民, 翁立军,孙嘉奕. 空间润滑材料与技术手册[M]. 北京:科学出版社,2009:7-9.
【2】王彦宗,刘振营,郭亚军. 高分子-无机纳米复合润滑材料研究进展[J]. 材料导报,2006,20(增刊2):215-218.
【3】乔红斌,田雪梅,吴芳. 高分子自润滑材料研究进展[J]. 材料导报,2007,21(10):24-26.
【4】王成彪,刘家浚,韦淡平,等. 摩擦学材料及表面工程[M]. 北京:国防工业出版社,2012:27-28,236-239.
【5】黄挺. 聚酰亚胺的摩擦学改性研究[D]. 上海:复旦大学,2014:20-26.
【6】姜旭峰,季峰,孙世安. 聚四氟乙烯润滑材料的摩擦学特性及其改性研究[C]//第八届国际摩擦密封材料技术交流暨产品展示会. 北京:中国摩擦密封材料协会,2006:169-173.
【7】于坤,罗新民. 纳米聚四氟乙烯合成工艺进展[J]. 润滑油,2002,17(5):18-20.
【8】王振廷,孟君晟. 摩擦磨损与耐磨材料[M]. 哈尔滨:哈尔滨工业大学出版社,2013:35-38,129-149.
【9】王文东,张超,杜鸣杰,等. 水/油润滑条件下PTFE复合材料的摩擦学性能[J]. 理化检验(物理分册),2016,52(10):717-721.
【10】刘海彬,郭强,米雪,等. 氧化程度对氧化石墨改性环氧树脂涂层摩擦学性能的影响[J]. 理化检验(物理分册),2013,49(11):727-730.
【11】乔玉林,池俊成,徐滨士,等. X光电子能谱分析边界润滑膜特性的研究[J]. 理化检验(物理分册),2001,37(8):323-327.
【12】张菊,包春江,杨志伊. 润滑滑动摩擦磨损试验及其铁谱监测技术研究[J]. 农机化研究,2006,28(4):161-163.
【13】张延帅,周晖,万志华,等. 靶功率对射频磁控溅射制备MoS2-Sb2O3复合薄膜结构和性能的影响[J]. 润滑与密封,2011,36(7):70-74.
【14】郑军,周晖,杨拉毛草,等. 不同金属基体上W-C:H溅射薄膜的摩擦学性能[J]. 宇航材料工艺,2015,45(1):57-61.
【15】MAREK K,WLADYSLAW S. The finite element method in tribological studies of polymer materials in tribo-pair with the oxide layer[J]. Tribology Letters,2013,52(3):381-393.
【16】EMERSON E N,ANDREAS A P. The effect of surface roughness on the transfer of polymer films under unlubricated testing conditions[J]. Wear,2015,326-327:74-83.
【2】王彦宗,刘振营,郭亚军. 高分子-无机纳米复合润滑材料研究进展[J]. 材料导报,2006,20(增刊2):215-218.
【3】乔红斌,田雪梅,吴芳. 高分子自润滑材料研究进展[J]. 材料导报,2007,21(10):24-26.
【4】王成彪,刘家浚,韦淡平,等. 摩擦学材料及表面工程[M]. 北京:国防工业出版社,2012:27-28,236-239.
【5】黄挺. 聚酰亚胺的摩擦学改性研究[D]. 上海:复旦大学,2014:20-26.
【6】姜旭峰,季峰,孙世安. 聚四氟乙烯润滑材料的摩擦学特性及其改性研究[C]//第八届国际摩擦密封材料技术交流暨产品展示会. 北京:中国摩擦密封材料协会,2006:169-173.
【7】于坤,罗新民. 纳米聚四氟乙烯合成工艺进展[J]. 润滑油,2002,17(5):18-20.
【8】王振廷,孟君晟. 摩擦磨损与耐磨材料[M]. 哈尔滨:哈尔滨工业大学出版社,2013:35-38,129-149.
【9】王文东,张超,杜鸣杰,等. 水/油润滑条件下PTFE复合材料的摩擦学性能[J]. 理化检验(物理分册),2016,52(10):717-721.
【10】刘海彬,郭强,米雪,等. 氧化程度对氧化石墨改性环氧树脂涂层摩擦学性能的影响[J]. 理化检验(物理分册),2013,49(11):727-730.
【11】乔玉林,池俊成,徐滨士,等. X光电子能谱分析边界润滑膜特性的研究[J]. 理化检验(物理分册),2001,37(8):323-327.
【12】张菊,包春江,杨志伊. 润滑滑动摩擦磨损试验及其铁谱监测技术研究[J]. 农机化研究,2006,28(4):161-163.
【13】张延帅,周晖,万志华,等. 靶功率对射频磁控溅射制备MoS2-Sb2O3复合薄膜结构和性能的影响[J]. 润滑与密封,2011,36(7):70-74.
【14】郑军,周晖,杨拉毛草,等. 不同金属基体上W-C:H溅射薄膜的摩擦学性能[J]. 宇航材料工艺,2015,45(1):57-61.
【15】MAREK K,WLADYSLAW S. The finite element method in tribological studies of polymer materials in tribo-pair with the oxide layer[J]. Tribology Letters,2013,52(3):381-393.
【16】EMERSON E N,ANDREAS A P. The effect of surface roughness on the transfer of polymer films under unlubricated testing conditions[J]. Wear,2015,326-327:74-83.
相关信息