摘 要
利用LINSEIS R.I.T.A L78淬火式膨胀仪,测定了高铬锻钢轧辊在1 030℃奥氏体化后以不同速率冷却时的相变膨胀曲线,采用膨胀法结合金相检验和硬度测试测定了高铬锻钢轧辊的临界点温度,用Origin软件绘制了高铬锻钢轧辊的连续冷却转变(CCT)曲线,并对其结果进行了分析。结果表明:高铬锻钢轧辊的CCT曲线上存在珠光体、贝氏体和马氏体3个相变区,且这3个相变区完全分离;当冷却速率≥ 1℃·s-1时,组织为单一马氏体相变组织,且马氏体转变开始温度Ms随着冷却速率的增大而降低。
Abstract
The phase transition expansion curve of high chromium forged steel roll after austenitizing at 1 030℃ and cooling at different rates was measured by using LINSEIS R.I.T.A L78 quenching dilatometer. The critical temperatures of the high chromium forged steel roll were determined by dilatometer method combined with metallographic test and hardness test, and the continuous cooling transformation (CCT) curves of the steel was drawn by Origin software, and then the test results were analyzed. The results show that the transformation of pearlite, bainite and martensite occurred in the continuous cooling process and the three phase transition regions were completely separated. When the cooling rate was greater than or equal to 1℃·s-1, there was only martensite phase transition and the martensite phase transition starting temperature Ms decreased with the increase of cooling rate.
中图分类号 TG142.1 DOI 10.11973/lhjy-wl201812009
所属栏目 试验技术与方法
基金项目
收稿日期 2018/1/8
修改稿日期
网络出版日期
作者单位点击查看
备注夏新蕊(1978-),女,工程师,硕士,主要从事轧辊材料检测及分析工作,xiaxinrui@163.com
引用该论文: XIA Xinrui,HUANG Binbin. Testing and Analysis on CCT Curve of High Chromium Forged Steel Roll[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2018, 54(12): 897~899
夏新蕊,黄斌斌. 高铬锻钢轧辊CCT曲线的测定及其结果分析[J]. 理化检验-物理分册, 2018, 54(12): 897~899
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】林慧国,傅代直. 钢的奥氏体转变曲线原理测试与应用[M]. 北京:机械工业出版社,1988.
【2】崔忠圻. 金属学与热处理[M]. 北京:机械工业出版社,2000.
【3】郭青苗,任吉堂. 钢的过冷奥氏体连续转变(CCT)曲线的解析化[J]. 河北理工学院学报,2006,28(2):33-36.
【4】金自力,陈刚. Gleeble 1500测定45钢CCT曲线的结果分析[J]. 包头钢铁学院学报,2004,23(4):326-328.
【5】季英萍,李炎,魏世忠,等. 高钒高速钢连续冷却转变曲线的测定与分析[J]. 机械工程材料,2007,31(7):63-65.
【6】史远,黄胜永,安治国. 冷却速率对30CrNiMo8钢的过冷奥氏体转变的影响[J]. 理化检验(物理分册),2017,53(11):782-785.
【7】徐幸. 10B21钢防滑链抗拉载荷不合格原因分析[J]. 理化检验(物理分册),2016,52(4):278-280.
【8】李壮,张平礼,王佳夫,等. 硅-锰系TRIP钢热处理工艺的研究[J]. 机械工程材料,2004,28(12):42-45.
【2】崔忠圻. 金属学与热处理[M]. 北京:机械工业出版社,2000.
【3】郭青苗,任吉堂. 钢的过冷奥氏体连续转变(CCT)曲线的解析化[J]. 河北理工学院学报,2006,28(2):33-36.
【4】金自力,陈刚. Gleeble 1500测定45钢CCT曲线的结果分析[J]. 包头钢铁学院学报,2004,23(4):326-328.
【5】季英萍,李炎,魏世忠,等. 高钒高速钢连续冷却转变曲线的测定与分析[J]. 机械工程材料,2007,31(7):63-65.
【6】史远,黄胜永,安治国. 冷却速率对30CrNiMo8钢的过冷奥氏体转变的影响[J]. 理化检验(物理分册),2017,53(11):782-785.
【7】徐幸. 10B21钢防滑链抗拉载荷不合格原因分析[J]. 理化检验(物理分册),2016,52(4):278-280.
【8】李壮,张平礼,王佳夫,等. 硅-锰系TRIP钢热处理工艺的研究[J]. 机械工程材料,2004,28(12):42-45.
相关信息