相控阵和超声衍射时差法在球罐裂纹检测中的应用

The Application of Phased Array and TOFD in Crack Detection of Spherical Tanks

杨晶

赵亮

王希

摘要

在某球罐内表面环焊缝中发现裂纹，采用TOFD（超声衍射时差法）和相控阵超声检测技术对缺陷进行定量检测，为缺陷返修提供了较为准确的数据，同时验证了两种检测技术相结合的方法对缺陷定量检测是最有效的辅助手段。

标签超声衍射时差法

相控阵超声

裂纹

TOFD

phased array ultrasonic

crack

Abstract

TOFD (Time of Flight Diffraction) and phased array ultrasonic flaw detection technique were used for quantifying cracks on the interior surface of the spherical tank girth welds, and it was found that the combination of the two techniques might provide more accurate data for defect repair and was possibly the most effective aid for defect quantification.

中图分类号 TG115.28 DOI 10.11973/wsjc201901009

所属栏目试验研究

基金项目

收稿日期 2018/7/6

修改稿日期

网络出版日期

作者单位点击查看

联系人作者杨晶(yjshooop@163.com)

备注杨晶(1984-),男,本科,主要从事承压设备无损检测工作

引用该论文: YANG Jing,ZHAO Liang,WANG Xi. The Application of Phased Array and TOFD in Crack Detection of Spherical Tanks[J]. Nondestructive Testing, 2019, 41(1): 35～38
杨晶,赵亮,王希. 相控阵和超声衍射时差法在球罐裂纹检测中的应用[J]. 无损检测, 2019, 41(1): 35～38

论文评价

共有人对该论文发表了看法，其中：

人认为该论文很差

人认为该论文较差

人认为该论文一般

人认为该论文较好

人认为该论文很好

分享论文

相关信息

	标题	相关频次
	大型H型钢气割裂纹原因分析	4
	核电厂反应堆冷却剂泵电机转子铜条的开裂原因	4
	厚壁高强钢球罐埋藏裂纹的TOFD检测及其成因分析	4
	环戊烷进料线三通裂纹原因分析	4
	无缝钢管分层缺陷的相控阵超声检测	4
	相控阵超声检测技术在薄壁小径管中的应用	4
	压缩机螺栓的相控阵超声检测	4
	液氨储罐封头焊缝的相控阵超声检测	4
	苯加氢管道系统不锈钢短节开裂原因	3
	高密度聚乙烯热熔焊缝的PAUT和TOFD检测	3
	冷却器鞍座角焊缝相控阵超声检测	3
	轻烃卸车缓冲罐焊缝的超声成像检测	3
	ϕ50mm海底管道焊缝的相控阵超声检测	2
	0Cr17Ni4Cu4Nb钢电渣坯裂纹产生原因	2
	1000MW超超临界机组C12A堵板阀裂纹成因分析	2
	15Cr低合金钢和N80钢的二氧化碳腐蚀性能对比	2
	16Co14Ni10Cr2MoE钢制抽筒抓钩开裂失效分析	2
	16MnR钢板低温冲击过程的声信号特性	2
	16Mn钢长轴裂纹缺陷成因分析	2
	16Mn钢弯管的开裂原因	2
	20SiMn2MoVA钢高强度螺栓裂纹成因分析	2
	22 mm 厚Q235B钢板表面裂纹成因	2
	220 kV断路器用弹簧异常开裂失效分析	2
	27CrMoTi钢套管螺纹表面裂纹成因分析	2
	304L不锈钢薄壁小径管焊缝的相控阵超声检测工艺	2
	304L不锈钢换热管泄漏原因分析	2
	304不锈钢冷却管束加工缺陷产生原因分析	2
	316L-16MnR复合板不锈钢侧晶间腐蚀原因分析	2
	3Cr13钢耐磨盘裂纹产生原因分析	2
	4.8级十字槽螺钉断裂失效分析	2