Localized Corrosion Regularities of X80 Steel Covered with Damaged GO Modified Epoxy Coating in NaCl Solution
摘 要
在环氧树脂涂层中添加2%(质量分数)的氧化石墨烯(GO)对其进行改性,利用电化学阻抗谱(EIS)和扫描开尔文探针技术(SKP),研究在5种NaCl溶液中,X80钢基体上的GO改性涂层破损后的局部腐蚀规律。结果表明:GO的独特片状结构能有效抑制水和氯离子等介质进入改性涂层内;同时,GO对腐蚀介质的阻隔作用将金属腐蚀活动限制在涂层破损处,腐蚀产物堆积并形成保护膜,对金属基体起到了一定的保护作用。
Abstract
Epoxy coating was modified by adding 2% (mass fraction) graphene oxide (GO). The localized corrosion regularities of X80 steel covered with damaged GO modified epoxy coating in five NaCl solutions were investigated using electrochemical impedance spectroscopy (EIS) and scanning Kelvin probe (SKP) technology. The results show that the unique chip structure of GO could effectively inhibit the media, like H2O and chloride ions, getting into the modified coating. At the same time, due to the blocking function of GO, the corrosive activities were restricted in the defected area, and the accumulation of corrosion products formed a protective film which had a protective effect on the metal substrate.
中图分类号 TG174 DOI 10.11973/fsyfh-201902009
所属栏目 试验研究
基金项目
收稿日期 2017/8/2
修改稿日期
网络出版日期
作者单位点击查看
联系人作者景红(605535335@qq.com)
引用该论文: JING Hong,WANG Di. Localized Corrosion Regularities of X80 Steel Covered with Damaged GO Modified Epoxy Coating in NaCl Solution[J]. Corrosion & Protection, 2019, 40(2): 126
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】BARINGHAUS J,RUAN M,EDLER F,et al. Exceptional ballistic transport in epitaxial graphene nanoribbons[J]. Nature,2014,506(7488):349-354.
【2】宁亮,王贤明,韩建军,等. 碳材料在导电涂料和隐身涂料领域的研究进展[J]. 中国涂料,2016,31(6):40-45.
【3】沈海斌,刘琼馨,瞿研. 石墨烯在涂料领域中的应用[J]. 涂料技术与文摘,2014,35(8):20-22.
【4】王耀文. 聚苯胺与石墨烯在防腐涂料中的应用[D]. 哈尔滨:哈尔滨工程大学,2012.
【5】邓尧,黄肖容,邬晓龄. 氧化石墨烯材料的研究进展[J]. 材料导报,2012,26(8):84-87.
【6】HONG J S,NAMKUNG H,AHN K H,et al. The role of organically modified layered silicate in the breakup and coalescence of droplets in PBT/PE blends[J]. Polymer,2006,47(11):3967-3975.
【7】CHANG K,HSU M,LU H,et al. Room-temperature cured hydrophobic epoxy/graphene composites as corrosion inhibitor for cold-rolled steel[J]. Carbon,2014,66:144-153.
【8】MOHAMMAD A R,JAVAD R,ZHOU W,et al. Enhanced mechanical properties of nanocomposites at low graphene content[J]. ACS Nano,2009,3(12):3884-3890.
【9】邓继勇,颜东,唐杰. 氧化石墨烯改性环氧树脂的制备及性能研究[J]. 功能材料,2016,47(8):8244-8247.
【10】RAMEZANZADEH B,HAERI Z,RAMEZANZADEH M. A facile route of making silica nanoparticles-covered graphene oxide nanohybrids (SiO2-GO); fabrication of SiO2-GO/epoxy composite coating with superior barrier and corrosion protection performance[J]. Chemical Engineering Journal,2016,303:511-528.
【11】余宗学,马瑜,何毅,等. TiO2-GO的制备及TiO2-GO/环氧树脂涂层的抗腐蚀性能[J]. 复合材料学报,2015,32(4):1017-1024.
【12】杨勇辉,孙红娟,彭同江. 石墨烯的氧化还原法制备及结构表征[J]. 无机化学学报,2010,26(11):2083-2091.
【2】宁亮,王贤明,韩建军,等. 碳材料在导电涂料和隐身涂料领域的研究进展[J]. 中国涂料,2016,31(6):40-45.
【3】沈海斌,刘琼馨,瞿研. 石墨烯在涂料领域中的应用[J]. 涂料技术与文摘,2014,35(8):20-22.
【4】王耀文. 聚苯胺与石墨烯在防腐涂料中的应用[D]. 哈尔滨:哈尔滨工程大学,2012.
【5】邓尧,黄肖容,邬晓龄. 氧化石墨烯材料的研究进展[J]. 材料导报,2012,26(8):84-87.
【6】HONG J S,NAMKUNG H,AHN K H,et al. The role of organically modified layered silicate in the breakup and coalescence of droplets in PBT/PE blends[J]. Polymer,2006,47(11):3967-3975.
【7】CHANG K,HSU M,LU H,et al. Room-temperature cured hydrophobic epoxy/graphene composites as corrosion inhibitor for cold-rolled steel[J]. Carbon,2014,66:144-153.
【8】MOHAMMAD A R,JAVAD R,ZHOU W,et al. Enhanced mechanical properties of nanocomposites at low graphene content[J]. ACS Nano,2009,3(12):3884-3890.
【9】邓继勇,颜东,唐杰. 氧化石墨烯改性环氧树脂的制备及性能研究[J]. 功能材料,2016,47(8):8244-8247.
【10】RAMEZANZADEH B,HAERI Z,RAMEZANZADEH M. A facile route of making silica nanoparticles-covered graphene oxide nanohybrids (SiO2-GO); fabrication of SiO2-GO/epoxy composite coating with superior barrier and corrosion protection performance[J]. Chemical Engineering Journal,2016,303:511-528.
【11】余宗学,马瑜,何毅,等. TiO2-GO的制备及TiO2-GO/环氧树脂涂层的抗腐蚀性能[J]. 复合材料学报,2015,32(4):1017-1024.
【12】杨勇辉,孙红娟,彭同江. 石墨烯的氧化还原法制备及结构表征[J]. 无机化学学报,2010,26(11):2083-2091.
相关信息