Evaluation and Application of High Performance Alloy Coating in Su 203 Well Area
摘 要
苏203区块于2011年开发,目前面临重大腐蚀问题,严重影响气田的正常开采和运行。寻找一种适用于苏203井区生产工况的防腐蚀措施势在必行。对苏203井区的腐蚀情况进行了调研,并对高性能合金镀层进行了室内及现场应用评价。结果表明:苏203井区腐蚀情况严重,最高腐蚀速率达2.3 mm/a,且出现穿孔的现象。高性能合金镀层具有良好的硬度、耐磨性和耐蚀性,能够明显降低试样的腐蚀速率,平均腐蚀速率为未镀层试样的3.84%~4.54%。将苏南19站站内转水管线更换为高性能合金镀层管线后,未发现壁厚明显变薄的现象,这表明高性能合金镀层具有良好的耐蚀性,可在苏203井区推广使用。
Abstract
Su 203 block was developed in 2011. At present, it faced major corrosion problems, which seriously affected the normal mining and operation of gas fields. It is imperative to find an anti-corrosion measure suitable for the production conditions of the Su 203 well area. The corrosion of the Su 203 well area was investigated, and a high-performance alloy coating was evaluated for indoor and field applications. The results show that the corrosion situation of Su 203 well was serious, the highest corrosion rate was 2.3 mm/a, and the phenomenon of perforation occurred. The high-performance alloy coating had good hardness, wear resistance and corrosion resistance, and it could significantly reduce the corrosion rate of samples. The average corrosion rate of the high-performance alloy coating was only 3.84% to 4.54% of uncoated samples. After replacing the water transfer pipeline in the 19 station of Sunan as a high-performance alloy coating pipeline, the phenomenon that the wall thickness was significantly thinned was not found, indicating that the high-performance alloy coating had good corrosion resistance and could be popularized in the Su 203 well area.
中图分类号 TG174.4 DOI 10.11973/fsyfh-201903011
所属栏目 应用技术
基金项目
收稿日期 2017/11/10
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHOU Mingming,HUANG Hangjuan,WEN Jie,ZHU Liming,CUI Xi,JIANG Kaikai,JIA Xiao,DUAN Xiaopeng. Evaluation and Application of High Performance Alloy Coating in Su 203 Well Area[J]. Corrosion & Protection, 2019, 40(3): 209
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吕瑞典,薛有祥. 油气田腐蚀防护技术综述[J]. 石油天然气学报,2008(5):367-369.
【2】杨秀清. 油气田腐蚀与防护技术[J]. 天然气工业,1994(5):59-62.
【3】李鹤林,路民旭. 油气田腐蚀类型、特点及几个重要研究领域[C]//中国腐蚀与防护学会成立20周年学术年会,北京:[出版者不详],1999.
【4】李国敏,李爱魁,郭兴蓬,等. 油气田开发中的CO2腐蚀及防护技术[J]. 材料保护,2003,36(6):1-5.
【5】郭学辉,周生杰,杜素珍,等. 油气田中几种常见的腐蚀机理[J]. 辽宁化工,2014(1):52-56.
【6】杨光,王亚刚,曹成章,等. 含硫油气田钻井腐蚀与防护对策[J]. 全面腐蚀控制,2008,22(5):16-18.
【7】曹建春,郭忠诚,周晓龙. 镁合金表面耐蚀涂层研究进展[J]. 云南冶金,2003,32(6):28-32.
【8】李岩,谢发勤,吴向清. 四种涂层在模拟油田环境下的腐蚀性能评价[J]. 电镀与精饰,2005,27(4):29-32.
【2】杨秀清. 油气田腐蚀与防护技术[J]. 天然气工业,1994(5):59-62.
【3】李鹤林,路民旭. 油气田腐蚀类型、特点及几个重要研究领域[C]//中国腐蚀与防护学会成立20周年学术年会,北京:[出版者不详],1999.
【4】李国敏,李爱魁,郭兴蓬,等. 油气田开发中的CO2腐蚀及防护技术[J]. 材料保护,2003,36(6):1-5.
【5】郭学辉,周生杰,杜素珍,等. 油气田中几种常见的腐蚀机理[J]. 辽宁化工,2014(1):52-56.
【6】杨光,王亚刚,曹成章,等. 含硫油气田钻井腐蚀与防护对策[J]. 全面腐蚀控制,2008,22(5):16-18.
【7】曹建春,郭忠诚,周晓龙. 镁合金表面耐蚀涂层研究进展[J]. 云南冶金,2003,32(6):28-32.
【8】李岩,谢发勤,吴向清. 四种涂层在模拟油田环境下的腐蚀性能评价[J]. 电镀与精饰,2005,27(4):29-32.
相关信息