Cause Analysis on Cracking of Corrugated Plates in a Heat Exchanger
摘 要
某公司生产的换热器波纹板开裂后发生串液现象,采用化学成分分析、金相检验、扫描电镜分析等方法,对波纹板开裂原因进行了分析。结果表明:该换热器在运行过程中不规范停车,停车后未及时排空液态介质;同时波纹板材料中镍、钼元素含量低于标准要求值,热侧介质自来水中Cl-含量远超出技术要求,这些因素使得密封垫圈和波纹板交界处发生孔腐蚀,腐蚀孔连接形成裂纹,最终导致波纹板开裂失效。
Abstract
The corrugated plates of a heat exchanger produced by a company cracked which resulted in liquid-crossing phenomenon happening. Chemical composition analysis, metallographic examination and scanning electron microscopic analysis were used to analyze the causes of cracking of the corrugated plates. The results show that the heat exchanger was not stopped according to the regulation during operation and liquid medium was not emptied in time after stopping. At the same time, the content of nickel and molybdenum elements in the corrugated plate material was lower than the standard requirement, and the content of Cl- in hot side medium running water far exceeded the technical requirement. These factors caused hole corrosion happened at the interface between the junction of gasket and the corrugated plate, and cracks formed by connection of corrosion holes, which eventually led to cracking failure of the corrugated plates.
中图分类号 TG172 DOI 10.11973/lhjy-wl201905010
所属栏目 质量控制与失效分析
基金项目 甘肃省科技计划资助项目(2015GS05896)
收稿日期 2018/5/11
修改稿日期
网络出版日期
作者单位点击查看
备注李金梅(1986-),女,工程师,主要从事金属材料金相检验及压力容器失效分析工作,lijinmei.happy@163.com
引用该论文: LI Jinmei,JIANG Chunhong,QI Wenkuan,SHI Wei,YANG Li. Cause Analysis on Cracking of Corrugated Plates in a Heat Exchanger[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2019, 55(5): 326~328
李金梅,蒋春宏,齐文宽,史伟,杨莉. 某换热器波纹板开裂原因分析[J]. 理化检验-物理分册, 2019, 55(5): 326~328
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘志平,王莉,张伟. ASTM SMO254板式换热器腐蚀的原因[J]. 腐蚀与防护,2016,11(37),932-935.
【2】刘景军,林玉珍,雍兴跃,等. 不同热处理条件下双相钢的磨损腐蚀[J]. 腐蚀科学与防护技术,2002,14(3):129-131.
【3】孔文彬,马小明,江楠. 板式换热器板片失效分析[J]. 压力容器,2011,9(28):42-46.
【4】祁玉红,俞树荣,李治国. 焊接板式换热器的应力腐蚀及防护[J]. 石油化工设备,2007,2(36):91-93.
【5】龚利华,王辉煌,汤瑞瑞. 时效对节型双相不锈钢点蚀和应力腐蚀行为的影响[J]. 材料热处理学报,2015,8(36):111-114.
【6】张亚明,夏邦杰,董爱华. 板式换热器板片穿孔失效分析[J]. 腐蚀科学与防护技术,2011,6(23):525-528.
【7】雷国庆,张治川. 板式换热器缝隙腐蚀[J]. 石油化工设备,2003,4(32):66-67.
【8】隋少华,宋天革,隋鲁华. 冷变形对LC9铝合金等温转变半固态组织的影响[J]. 铸造,2006,55(7):683-685.
【2】刘景军,林玉珍,雍兴跃,等. 不同热处理条件下双相钢的磨损腐蚀[J]. 腐蚀科学与防护技术,2002,14(3):129-131.
【3】孔文彬,马小明,江楠. 板式换热器板片失效分析[J]. 压力容器,2011,9(28):42-46.
【4】祁玉红,俞树荣,李治国. 焊接板式换热器的应力腐蚀及防护[J]. 石油化工设备,2007,2(36):91-93.
【5】龚利华,王辉煌,汤瑞瑞. 时效对节型双相不锈钢点蚀和应力腐蚀行为的影响[J]. 材料热处理学报,2015,8(36):111-114.
【6】张亚明,夏邦杰,董爱华. 板式换热器板片穿孔失效分析[J]. 腐蚀科学与防护技术,2011,6(23):525-528.
【7】雷国庆,张治川. 板式换热器缝隙腐蚀[J]. 石油化工设备,2003,4(32):66-67.
【8】隋少华,宋天革,隋鲁华. 冷变形对LC9铝合金等温转变半固态组织的影响[J]. 铸造,2006,55(7):683-685.
相关信息