UNS31803双相不锈钢手工电弧焊接接头的组织与性能
Structure and Properties of Welded Joint for UNS31803 Duplex Stainless Steel by Shielded Metal Arc Welding
摘 要
采用手工电弧焊（SMAW）对UNS31803双相不锈钢进行焊接，通过金相检验、力学性能试验、硬度测试、耐蚀性能试验等方法对UNS31803双相不锈钢手工电弧焊接接头的显微组织和性能进行了分析。结果表明：采用适当的焊接工艺参数进行焊接，所得到的焊缝显微组织为铁素体+奥氏体，无σ相析出；焊接接头具有优良的力学性能；焊缝和热影响区的铁素体含量均在35%~65%（体积分数）的合理范围内；在22℃的6%（质量分数） FeCl3溶液中，焊接接头的不同区域均具有良好的耐蚀性能。
手工电弧焊
显微组织
力学性能
耐蚀性能
duplex stainless steel
shielded metal arc welding (SMAW)
microstructure
mechanical property
corrosion resistance
Abstract
Duplex stainless steel UNS31803 was welded by shielded metal arc welding (SMAW). Microstructure and properties of the welded joint for UNS31803 duplex stainless steel by SMAW were analyzed by means of metallographic examination, mechanical property test, hardness test and corrosion resistance test. The results show that the microstructure of the weld seam were ferrite+austenite, and without σ phase precipitation when proper welding parameters were adopted. The welded joint had excellent mechanical properties, and the ferrite content of the weld seam and the heat affected zone was within the reasonable range of 35%-65% (volume fraction). In 6% (mass fraction) FeCl3 solution at 22℃, the different regions of the welded joint had good corrosion resistance.
中图分类号 TG444.1 DOI 10.11973/lhjy-wl201907004
所属栏目 试验与研究
基金项目
收稿日期 2018/5/11
修改稿日期
网络出版日期
作者单位点击查看
备注代绪成(1985-),男,工程师,主要从事金属材料焊接工艺评定工作,daixc@cooec.com.cn
引用该论文: DAI Xucheng,CHEN Qiang,TONG Minglei,ZHANG Xiuhe. Structure and Properties of Welded Joint for UNS31803 Duplex Stainless Steel by Shielded Metal Arc Welding[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2019, 55(7): 445～450
代绪成,陈强,仝明磊,张秀荷. UNS31803双相不锈钢手工电弧焊接接头的组织与性能[J]. 理化检验－物理分册, 2019, 55(7): 445～450
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吴玫. 双相不锈钢[M]. 北京:冶金工业出版社,2000.
【2】KESHMIRI H, MOMENI A, DEHGHANI K, et al. Effect of aging time and temperature on mechanical properties and microstructural evolution of 2205 ferritic-austenitic atainless steel[J]. Journal of Materials Science & Technology,2009,25(5):597-602.
【3】刘建波,付俊,黄巍. 双相不锈钢焊接工艺试验研究[J]. 焊接,2009(6):54-58.
【4】贾法勇,霍立兴,吴冰,等. 双相不锈钢焊接接头疲劳强度[J]. 焊接学报,2004,25(2):31-34.
【5】李志军,陈湘茹,孙卿卿,等. 双相不锈钢的研究与发展[J]. 铸造技术,2011,32(9):1320-1323.
【6】王建军,温艳慧,吴海天,等. 热输入对2205双相不锈钢MIG焊接接头组织及力学性能的影响[J]. 材料与冶金学报,2016,15(2):139-142.
【7】金晓军,霍立兴,张玉凤,等. 热输入对双相不锈钢管接头力学和腐蚀性能的影响[J]. 焊接学报,2004,25(3):109-112.
【8】尹士科,李凤辉. 双相不锈钢的焊接特性和焊接材料[J]. 机械制造文摘(焊接分册),2012(3):20-23.
【9】李为卫,曾君,马开阳,等. 2205双相不锈钢管焊接工艺评定[J]. 现代制造工程,2006(1):86-87,96.
【10】刘宏伟. 焊接工艺对S32205双相不锈钢组织和性能的影响[J]. 理化检验(物理分册),2013,49(5):282-285.
【2】KESHMIRI H, MOMENI A, DEHGHANI K, et al. Effect of aging time and temperature on mechanical properties and microstructural evolution of 2205 ferritic-austenitic atainless steel[J]. Journal of Materials Science & Technology,2009,25(5):597-602.
【3】刘建波,付俊,黄巍. 双相不锈钢焊接工艺试验研究[J]. 焊接,2009(6):54-58.
【4】贾法勇,霍立兴,吴冰,等. 双相不锈钢焊接接头疲劳强度[J]. 焊接学报,2004,25(2):31-34.
【5】李志军,陈湘茹,孙卿卿,等. 双相不锈钢的研究与发展[J]. 铸造技术,2011,32(9):1320-1323.
【6】王建军,温艳慧,吴海天,等. 热输入对2205双相不锈钢MIG焊接接头组织及力学性能的影响[J]. 材料与冶金学报,2016,15(2):139-142.
【7】金晓军,霍立兴,张玉凤,等. 热输入对双相不锈钢管接头力学和腐蚀性能的影响[J]. 焊接学报,2004,25(3):109-112.
【8】尹士科,李凤辉. 双相不锈钢的焊接特性和焊接材料[J]. 机械制造文摘(焊接分册),2012(3):20-23.
【9】李为卫,曾君,马开阳,等. 2205双相不锈钢管焊接工艺评定[J]. 现代制造工程,2006(1):86-87,96.
【10】刘宏伟. 焊接工艺对S32205双相不锈钢组织和性能的影响[J]. 理化检验(物理分册),2013,49(5):282-285.
相关信息