Effect of Magnetic Field on Corrosion of X60 Pipeline Steel in Soil of Changsha Area
摘 要
采用失重法,电化学方法,腐蚀形貌分析等研究了磁场对X60管线钢在长沙磁浮快线与西气东输管道潜湘支线交叉点处土壤中的腐蚀行为影响规律。结果表明:磁场的存在加速了X60钢在长沙土壤中的腐蚀;埋设相同时间,试样在无磁场条件下的腐蚀失重最小,在强磁场条件下的腐蚀最严重,其埋设28 d的腐蚀速率达到0.068 mm/a。
Abstract
The effects of magnetic field on the corrosion behavior of X60 pipeline steel in the soil at the intersection of Changsha maglev express line and West-East gas pipeline Qianxiang branch were studied by weight loss method, electrochemical method and corrosion morphology analysis. The results show that the presence of magnetic field accelerated the corrosion of X60 steel in Changsha soil. When the samples were buried for the same time, the corrosion weight loss under the condition without magnetic field was the smallest, and the corrosion weight loss under the condition with strong magnetic field was the most serious. Under strong magnetic field conditions, the corrosion rate of the samples embedded for 28 d reached 0.068 mm/a.
中图分类号 TG174 DOI 10.11973/fsyfh-201907002
所属栏目 试验研究
基金项目
收稿日期 2018/1/5
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: HUI Haijun,DAI Qiansheng,CHEN Kai,JIANG Zitao,CUI Wei,LI Yongfa. Effect of Magnetic Field on Corrosion of X60 Pipeline Steel in Soil of Changsha Area[J]. Corrosion & Protection, 2019, 40(7): 474
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张文艳,唐德智,熊娟. 地铁杂散电流对埋地管道腐蚀电位和管中电流分布的影响规律. 腐蚀与防护, 2017, 38(1):144-151.
【2】杨霜, 唐囡, 闫茂成, 等. 温度对X80管线钢酸性红壤腐蚀行为的影响. 中国腐蚀与防护学报, 2015, 35(3):227-232.
【3】曹勇, 杨志成. 磁场对航空拖缆碳钢材料腐蚀行为影响研究. 装备环境工程, 2016, 13(4):42-47.
【4】EL-SHAMY A M, SHEHATA M F, ISMAIL A I M. Effect of moisture contents of bentonitic clay on the corrosion behavior of steel pipelines. Applied Clay Science, 2015, 114:461-466.
【5】滕彧, 陈旭, 何川,等. 显微组织对X70钢在含有硫酸盐还原菌的3.5%NaCl溶液中腐蚀行为的影响. 中国腐蚀与防护学报, 2017, 37(2):168-174.
【6】GHABASHY M E, SEDAHMED G H, MANSOUR I A S. Effect of a magnetic field on the rate of diffusion-controlled corrosion of metals. British Corrosion Journal, 1982, 17(1):36-37.
【7】GHABASHY M A. Effect of magnetic field on the rate of steel corrosion in aqueous solutions. Anti-Corrosion Methods and Materials, 1988, 35(1):12-13.
【8】田光, 魏爱军, 霍富永,等. 磁场对金属腐蚀的实验研究. 管道技术与设备, 2010(1):50-52.
【9】LU Z P, SHOJI T, YANG W. Anomalous surface morphology of iron generated after anodic dissolution under magnetic fields. Corrosion Science, 2010, 52(8):2680-2686.
【10】SUEPTITZ R, TSCHULIK K, UHLEMANN M, et al. Effect of high gradient magnetic fields on the anodic behaviour and localized corrosion of iron in sulphuricacid solutions. Corrosion Science, 2011, 53(10):3222-3230.
【11】郭昊, 杜翠薇, 李晓刚, 等. 在NaHCO3溶液中X70钢的模拟缝隙腐蚀机理研究. 腐蚀科学与防护技术, 2008, 20(5):336-339.
【12】何业东, 齐慧滨. 材料腐蚀与防护概论. 北京:机械工业出版社, 2005.
【13】雍兴跃. 磁场对金属腐蚀的影响. 全面腐蚀控制, 1992, 6(3):15-17.
【2】杨霜, 唐囡, 闫茂成, 等. 温度对X80管线钢酸性红壤腐蚀行为的影响. 中国腐蚀与防护学报, 2015, 35(3):227-232.
【3】曹勇, 杨志成. 磁场对航空拖缆碳钢材料腐蚀行为影响研究. 装备环境工程, 2016, 13(4):42-47.
【4】EL-SHAMY A M, SHEHATA M F, ISMAIL A I M. Effect of moisture contents of bentonitic clay on the corrosion behavior of steel pipelines. Applied Clay Science, 2015, 114:461-466.
【5】滕彧, 陈旭, 何川,等. 显微组织对X70钢在含有硫酸盐还原菌的3.5%NaCl溶液中腐蚀行为的影响. 中国腐蚀与防护学报, 2017, 37(2):168-174.
【6】GHABASHY M E, SEDAHMED G H, MANSOUR I A S. Effect of a magnetic field on the rate of diffusion-controlled corrosion of metals. British Corrosion Journal, 1982, 17(1):36-37.
【7】GHABASHY M A. Effect of magnetic field on the rate of steel corrosion in aqueous solutions. Anti-Corrosion Methods and Materials, 1988, 35(1):12-13.
【8】田光, 魏爱军, 霍富永,等. 磁场对金属腐蚀的实验研究. 管道技术与设备, 2010(1):50-52.
【9】LU Z P, SHOJI T, YANG W. Anomalous surface morphology of iron generated after anodic dissolution under magnetic fields. Corrosion Science, 2010, 52(8):2680-2686.
【10】SUEPTITZ R, TSCHULIK K, UHLEMANN M, et al. Effect of high gradient magnetic fields on the anodic behaviour and localized corrosion of iron in sulphuricacid solutions. Corrosion Science, 2011, 53(10):3222-3230.
【11】郭昊, 杜翠薇, 李晓刚, 等. 在NaHCO3溶液中X70钢的模拟缝隙腐蚀机理研究. 腐蚀科学与防护技术, 2008, 20(5):336-339.
【12】何业东, 齐慧滨. 材料腐蚀与防护概论. 北京:机械工业出版社, 2005.
【13】雍兴跃. 磁场对金属腐蚀的影响. 全面腐蚀控制, 1992, 6(3):15-17.
相关信息